Preparation and microwave absorption properties of Ni(Co/Zn/Cu)Fe2O4/SiC@SiO2 composites

  • Peng Wang
  • Ping-An LiuEmail author
  • Sheng Ye
Article
  • 118 Downloads

Abstract

Ni(Co/Zn/Cu)Fe2O4/SiC@SiO2, a microwave absorber, was prepared by the sol–gel method. The phase structure and the morphology of the microwave absorbers were characterized by X-Ray Diffraction (XRD) and scanning electron microscopy (SEM), respectively. Laser sizer (LS) and X-ray photoelectron spectroscopy (XPS) analysis show the core–shell structure of SiC@SiO2. Coaxial method was used to measure the microwave absorption properties of the prepared composites in the frequency range of 2–18 GHz. When 70 wt% SiC is wrapped by 30 wt% SiO2, and 50 wt% NiFe2O4 is added into 50 wt% SiC@SiO2, the as-prepared powders are found to have advanced microwave absorption properties with a minimum reflection loss (RL) of −32.26 dB at about 6.08 GHz, and the available bandwidth is approximately 2.1 GHz when the RL is below −10 dB.

Keywords

Ni(Co/Zn/Cu)Fe2O4/SiC@SiO2 Microwave absorption property Sol–gel method Core–shell structure 

Notes

Acknowledgments

This study was financially supported by the Military Project of the Ministry of National Defense of China (No. JPPT-125-2-168).

References

  1. [1]
    Ma RT, Shang HY, Wang X, Jiang D. Dielectric, magnetic and microwave absorbing properties of polyaniline Co0.7Cr0.1Zn0.2Fe2O4 composites. Rare Met. 2015;29(8):622.Google Scholar
  2. [2]
    Luo F, Zhu DM, Zhou WC. A two-layer dielectric absorber covering a wide frequency range. Ceram Int. 2007;33(2):197.CrossRefGoogle Scholar
  3. [3]
    Liu HT, Tian H. Mechanical and microwave dielectric properties of SiCf/SiC composites with BN interphase prepared by dip-coating process. J Eur Ceram Soc. 2012;32(10):2505.CrossRefGoogle Scholar
  4. [4]
    Zheng GP, Yin XW, Liu SH, Li XM, Deng JL, Li Q. Improved electromagnetic absorbing properties of Si3N4–SiC/SiO2 composite ceramics with multi-shell microstructure. J Eur Ceram Soc. 2013;33(11):2173.CrossRefGoogle Scholar
  5. [5]
    Tian H, Liu HT, Cheng HF. Effects of SiC contents on the dielectric properties of SiO2f/SiO2 composites fabricated through a sol–gel process. Powder Technol. 2013;239(17):374.CrossRefGoogle Scholar
  6. [6]
    Zhao DL, Luo F, Zhou WC. Microwave absorbing property and complex permittivity of nano SiC particles doped with nitrogen. J Alloys Compd. 2010;490(1–2):190.CrossRefGoogle Scholar
  7. [7]
    Agathopoulos S. Influence of synthesis process on the dielectric properties of B-doped SiC powders. Ceram Int. 2012;38(4):3309.CrossRefGoogle Scholar
  8. [8]
    Zou GZ, Cao MS, Zhang L, Li JG, Xu H, Chen YJ. A nanoscale core-shell of β-SiC P–Ni prepared by electroless plating at lower temperature. Surf Coat Technol. 2006;201(1–2):108.CrossRefGoogle Scholar
  9. [9]
    Tian H, Liu HT, Cheng HF. Mechanical and microwave dielectric properties of KD-I SiCf/SiC composites fabricated through precursor infiltration and pyrolysis. Ceram Int. 2014;40(7):9009.CrossRefGoogle Scholar
  10. [10]
    Zhang HT, Zhang JS, Zhang HY. Electromagnetic properties of silicon carbide foams and their composites with silicon dioxide as matrix in X-band. Compos A. 2007;38(2):602.CrossRefGoogle Scholar
  11. [11]
    Li XM, Zhang LT, Yin XW, Feng L, Li Q. Effect of chemical vapor infiltration of SiC on the mechanical and electromagnetic properties of Si3N4–SiC ceramic. Scr Mater. 2010;63(6):657.CrossRefGoogle Scholar
  12. [12]
    Giannakopoulou T, Kompotiatis L, Kontogeorgakos A, Kordas G. Microwave behavior of ferrites prepared via sol-gel method. J Magn Magn Mater. 2002;246(3):360.CrossRefGoogle Scholar
  13. [13]
    Hosseini SH, Mohseni SH, Asadnia A, Kerdari H. Synthesis and microwave absorbing properties of polyaniline/MnFe2O4 nanocomposite. J Alloys Compd. 2011;509(14):4682.CrossRefGoogle Scholar
  14. [14]
    Pan S, Lin PH, Wang L, Liu X, Hu SQ, Zhou HY. Microwave properties of RE(Nd, Tb)FeCoB alloy system. Rare Met Mater Eng. 2014;43(4):803.CrossRefGoogle Scholar
  15. [15]
    Fu M, Jiao QZ, Zhao Y. In situ fabrication and characterization of cobalt ferrite nanorods/graphene composites. Mater Schara Cterization. 2013;86(8):303.Google Scholar
  16. [16]
    Xiao HM, Liu XM, Fu SY. Synthesis, magnetic and microwave absorbing properties of core–shell structured MnFe2O4/TiO2 nanocomposites. Compos Sci Technol. 2006;66(13):2003.CrossRefGoogle Scholar
  17. [17]
    Oh JH, Oh KS, Kim CG, Hong CS. Design of radar absorbing structures using glass/epoxy composite containing carbon black in X-band frequency ranges. Compos B Eng. 2004;35(1):49.CrossRefGoogle Scholar
  18. [18]
    Chin WS, Lee DG. Development of the composite RAS (radar absorbing structure) for the X-band frequency range. Compos Struct. 2007;77(4):457.CrossRefGoogle Scholar
  19. [19]
    Singh P, Babbar VK, Razdan A, Puri RK, Goel TC. Complex permittivity, permeability, and X-band microwave absorption of CaCoTi ferrite composites. J Appl Phys. 2000;87(9):4362.CrossRefGoogle Scholar
  20. [20]
    Liao ZQ, Gong RZ, Nie Y, Wang T, Wang X. Absorption enhancement of fractal frequency selective surface absorbers by using microwave absorbing material based substrates. Photonics Nanostruct Fundam Appl. 2011;9(3):287.CrossRefGoogle Scholar
  21. [21]
    Singh C, Narang SB, Hudiara IS, Sudheendran K, Raju KCJ. Complex permittivity and complex permeability of Sr ions substituted Ba ferrite at X-band. J Magn Magn Mater. 2008;320(10):1657.CrossRefGoogle Scholar
  22. [22]
    Li LC, Chen KY, Liu H, Tong GX, Qian HS, Hao B. Attractive microwave-absorbing properties of M-BaFe12O19 ferrite. J Alloys Compd. 2013;557(16):11.CrossRefGoogle Scholar

Copyright information

© The Nonferrous Metals Society of China and Springer-Verlag Berlin Heidelberg 2016

Authors and Affiliations

  1. 1.School of Materials Science and EngineeringSouth China University of TechnologyGuangzhouChina

Personalised recommendations