Effect of Microstructural Constituents on Fusion Zone Corrosion Properties of GMA Welded AA 5083 with Novel Al–Mg Welding Wires of High Mg Contents
- 19 Downloads
The corrosion behavior of fusion zones (FZ-1: 5.39 Mg–0.66Mn, FZ-2: 5.49 Mg–0.35Mn, and FZ-3: 5.72 Mg–0.32Mn) of AA5083 alloy welded with high Mg-containing Al–Mg filler wires has been systematically investigated. An extensive microstructural characterization was performed to evaluate the localized corrosion properties of the fusion zones. The potentiodynamic polarization test and salt spray test showed that the corrosion resistance decreases with increasing Mg content, therefore, the corrosion resistance of FZ-3 is lower than that of the FZ-1 and FZ-2. The electron microscopic analysis after intermittent corrosion test revealed that the eutectic β-phase (Al3Mg2) was responsible for the initiation of corrosion. The corrosion behavior of each microstructural constituents was related to the dissolution potentials of the corresponding microstructures; hence, it forms galvanic couple with the Al matrix. Moreover, high Mg content in the filler wire lead to the formation of additional β-phase in the fusion zone. However, intermetallics such as Al6(Fe,Mn) and Mg2Si were significant only during the later stages of corrosion.
KeywordsAA 5083 alloy Fusion zones β-phase Intermetallics Corrosion Dissolution potentials
This work was supported by the Korea Basic Science Institute (KBSI) National Research Facilities and Equipment Center (NFEC) grant funded by the Korea government (Ministry of Education) (No. 2019R1A6C1010045).
- 2.D.S. D'Antuono, β Phase Growth and Precipitation in the 5xxx Series Aluminum Alloy System (2017)Google Scholar
- 15.ASM Handbook, Volume 2: Properties and Selection: Nonferrous Alloys and Special Purpose Materials (1987)Google Scholar
- 16.Occupational Safety and Health Administration (OSHA), Proposed rule occupational exposure to beryllium and beryllium compounds in construction and shipyard sectors, n.d. https://www.osha.gov/beryllium/nprm_sectors/index.html. Accessed 12 Sept 2018
- 18.S.G. Kim, Y.Y. Ok, S.J. Ho (2011), Oxidation-resistant aluminum alloy and manufacturing method thereof. https://patents.google.com/patent/KR101273582B1/en. Accessed 16 Feb 2019
- 20.ASTM International, ASTM B117-standard practice for operating salt spray test fog apparatus, 2011. https://doi.org/10.1520/B0117-11.2
- 21.International Organization for Standardization (ISO), ISO 9227:2012-corrosion tests in artificial atmospheres (Salt spray tests), 2012. https://doi.org/10.1007/s11367-011-0297-3
- 22.ASTM International, Standard practice for preparing, cleaning and evaluating corrosion test, 1999. https://doi.org/10.1520/G0001-03R11.2
- 23.ASTM International, Standard reference test method for making potentiodynamic anodic polarization measurements, 2015. https://doi.org/10.1520/G0005-14.2
- 26.ASTM International, G102-Standard practice for calculation of corrosion rates and related information from electrochemical measurements 1 rosion test specimens ASTM International. G102–89 (2008) 1–7. https://doi.org/10.1520/G0102-89R10.2
- 36.C. Luo, Role of Microstructure on Corrosion Control of AA2024-T3 Aluminium Alloy (2011)Google Scholar