On the Role of Chromium in Dynamic Transformation of Austenite

  • K. Chadha
  • Davood Shahriari
  • C. Jr. Aranas
  • Louis-Philippe Lapierre-Boire
  • Mohammad Jahazi
Article
  • 34 Downloads

Abstract

The effect of Chromium (Cr) on the dynamic transformation (DT) of austenite to ferrite at temperatures up to 430 °C above Ae3 was studied in a medium-carbon low-alloy steel. Hot compression tests were performed using Gleeble 3800® thermomechanical simulator followed by microstructural examinations using electron microscopy (FESEM-EBSD). Driving force calculation using austenite flow stress and ferrite yield stress on an inverse absolute temperature graph indicated that Cr increases the driving force for the transformation of austenite to ferrite; however, when the influence of stress and thermodynamic analysis are taken into account, it was observed that Cr increases the barrier energy and therefore, emerges as a barrier to the transformation. An analysis, based on lattice and pipe diffusion theories is presented that quantifies the role of stress on the diffusivity of Cr and is compared with other the main alloying elements such as C, Si and Mn and its impact, positive or negative, on the DT barrier energy. Finally, a comparison is made on the differential effects of temperature and stress on the initiation of DT in medium-carbon low-alloy steels.

Keywords

Dynamic transformation Medium-carbon low-alloy steel Phase transformation Stress induced diffusion As-cast structure 

Notes

Acknowledgements

The authors are very much grateful to Finkl Steel for providing the specimens for the present research. The authors would also like to thank National Science Engineering Research Council (NSERC) Canada for their support in the framework of a Collaborative Research and Development project (CRD). One of the authors (Kanwal Chadha) would like to acknowledge the support of ÉTS, Canada for financial support for visiting Indian Institute of Technology, Hyderabad, India for carrying out the EBSD characterization. We would also like to thank Dr. Pinaki Prasad Bhattacharjee for his valuable input to the analysis of EBSD images and Mr. Rajasekhar Reddy Salem for assisting in the post processing of EBSD data.

References

  1. 1.
    Y. Matsumura, H. Yada, Evolution of ultrafine-grained ferrite in hot successive deformation. Trans. Iron Steel Inst. Jpn. 27(6), 492–498 (1987)CrossRefGoogle Scholar
  2. 2.
    H. Yada, C.M. Li, H. Yamagata, Dynamic γ → α transformation during hot deformation in iron–nickel–carbon alloys. ISIJ Int. 40(2), 200–206 (2000)CrossRefGoogle Scholar
  3. 3.
    C. Ghosh, C. Aranas Jr., J.J. Jonas, Dynamic transformation of deformed austenite at temperatures above the Ae3. Prog. Mater Sci. 82, 151–233 (2016)CrossRefGoogle Scholar
  4. 4.
    N. Park et al., Flow stress analysis for determining the critical condition of dynamic ferrite transformation in 6Ni–0.1C steel. Acta Mater. 61(1), 163–173 (2013)CrossRefGoogle Scholar
  5. 5.
    L. Sun et al., Effect of strain path on dynamic strain-induced transformation in a microalloyed steel. Acta Mater. 66, 132–149 (2014)CrossRefGoogle Scholar
  6. 6.
    B. Guo, et al., Dynamic transformation of Ti–6Al–4 V during torsion in the two-phase region. J. Mater. Sci. 53(12), 9305–9315 (2018)CrossRefGoogle Scholar
  7. 7.
    B. Guo et al., Reverse transformation behavior of Ti-6Al-4 V after deformation in the two-phase region. Metal. Mater. Trans. A 49(1), 22–27 (2018)CrossRefGoogle Scholar
  8. 8.
    D.N. Hanlon, J. Sietsma, S. van der Zwaag, The effect of plastic deformation of austenite on the kinetics of subsequent ferrite formation. ISIJ Int. 41(9), 1028–1036 (2001)CrossRefGoogle Scholar
  9. 9.
    C. Ghosh et al., The dynamic transformation of deformed austenite at temperatures above the Ae3. Acta Mater. 61(7), 2348–2362 (2013)CrossRefGoogle Scholar
  10. 10.
    C. Aranas Jr., J.J. Jonas, Effect of Mn and Si on the dynamic transformation of austenite above the Ae3 temperature. Acta Mater. 82, 1–10 (2015)CrossRefGoogle Scholar
  11. 11.
    K. Chadha et al., Influence of strain rate on dynamic transformation of austenite in an as-cast medium-carbon low-alloy steel. Materialia 1, 155–167 (2018)CrossRefGoogle Scholar
  12. 12.
    N. Saunders et al., Using JMatPro to model materials properties and behavior. JOM 55(12), 60–65 (2003)CrossRefGoogle Scholar
  13. 13.
    K. Chadha et al., Deformation and recrystallization behavior of the cast structure in large size, high strength steel ingots: experimentation and modeling. Metal. Mater. Trans. A 48(9), 4297–4313 (2017)CrossRefGoogle Scholar
  14. 14.
    K. Chadha, Z.A., C. Jr. Aranas, D. Shahriari, M. Jahazi, Influence of strain rate in dynamic transformation of austenite in an As-cast medium carbon low alloy steel. Materialia (2018)Google Scholar
  15. 15.
    H. Song et al., Effect of austenite stability on microstructural evolution and tensile properties in intercritically annealed medium-mn lightweight steels. Metal. Mater. Trans. A 47(6), 2674–2685 (2016)CrossRefGoogle Scholar
  16. 16.
    Koskenniska, J., Austenitic Stainless Steel. 2014, Google PatentsGoogle Scholar
  17. 17.
    P.J. Wray, High temperature plastic-flow behavior of mixtures of austenite, cementite, ferrite, and pearlite in plain-carbon steels. Metal. Trans. A, Phys. Metal. Mater. Sci. 15A(11), 2041–2058 (1984)CrossRefGoogle Scholar
  18. 18.
    J.J. Jonas, C. Ghosh, Role of mechanical activation in the dynamic transformation of austenite. Acta Mater. 61(16), 6125–6131 (2013)CrossRefGoogle Scholar
  19. 19.
    H. Bhadeshia, Material factors. ASM International, Member/Customer Service Center, Materials Park, OH 44073-0002, USA, pp. 3–10 (2002)Google Scholar
  20. 20.
    C. Aranas Jr. et al., Flow softening-based formation of widmanstätten ferrite in a 0.06%C steel deformed above the Ae3. ISIJ Int. 55(1), 300–307 (2015)CrossRefGoogle Scholar
  21. 21.
    R. Grewal et al., Formation of Widmanstätten ferrite at very high temperatures in the austenite phase field. Acta Mater. 109, 23–31 (2016)CrossRefGoogle Scholar
  22. 22.
    C. Aranas Jr., et al. Formation of Widmanstätten ferrite in a C-Mn steel at temperatures high in the austenite phase field. in Proceedings of the International Conference on Solid-Solid Phase Transformations in Inorganic Materials (PTM 2015). Whistler, BC (2015)Google Scholar
  23. 23.
    F. Masoumi et al., On the occurrence of liquation during linear friction welding of Ni-based superalloys. Metal. Mater. Trans. A 48(6), 2886–2899 (2017)CrossRefGoogle Scholar
  24. 24.
    G.B. Viswanathan et al., Segregation at stacking faults within the γ′ phase of two Ni-base superalloys following intermediate temperature creep. Scripta Mater. 94(Supplement C), 5–8 (2015)CrossRefGoogle Scholar
  25. 25.
    S.L. Robinson, O.D. Sherby, Mechanical behavior of polycrystalline tungsten at elevated temperature. Acta Metall. 17(2), 109–125 (1969)CrossRefGoogle Scholar
  26. 26.
    D. Samantaray et al., Strain dependent rate equation to predict elevated temperature flow behavior of modified 9Cr-1Mo (P91) steel. Mater. Sci. Eng., A 528(3), 1071–1077 (2011)CrossRefGoogle Scholar
  27. 27.
    H.J. Frost, M.F. Ashby, Deformation Mechanism Maps: The Plasticity and Creep of Metals and Ceramics (Pergamon Press, Oxford, 1982)Google Scholar
  28. 28.
    M.F. Ashby et al., Micromechanisms of flow and fracture, and their relevance to the rheology of the upper mantle. Philos. Trans. R. Soc. Lond. Ser. A, Math. Phys. Sci. 288, 59–95 (1978)CrossRefGoogle Scholar
  29. 29.
    J.-O. Andersson et al., Thermo-Calc & DICTRA, computational tools for materials science. Calphad 26(2), 273–312 (2002)CrossRefGoogle Scholar
  30. 30.
    Y. Taniguchi, K. Hara, M. Senoo, High Pressure Liquids and Solutions (Elsevier, Amsterdam, 2013)Google Scholar
  31. 31.
    A.F. Smitll, R. Hales, Diffusion of manganese in type 316 austenitic stainless steel. Metal Sci. 9(1), 181–184 (1975)CrossRefGoogle Scholar
  32. 32.
    Posner, E.S., Experiments and applications of chromium diffusion in spinel. 2012, University of ArizonaGoogle Scholar
  33. 33.
    C.L. Beswick, R.D. Shalders, T.W. Swaddle, Volume profile for substitution in labile chromium (III) complexes: reactions of aqueous [Cr (Hedta) OH2] and [Cr (edta)]-with thiocyanate ion. Inorg. Chem. 35(4), 991–994 (1996)CrossRefGoogle Scholar
  34. 34.
    F. Béjina et al., Activation volume of silicon diffusion in San Carlos olivine. Geophys. Res. Lett. 24(21), 2597–2600 (1997)CrossRefGoogle Scholar
  35. 35.
    X. Tingdong, Creating and destroying vacancies in solids and non-equilibrium grain-boundary segregation. Phil. Mag. 83(7), 889–899 (2003)CrossRefGoogle Scholar
  36. 36.
    E.I. Poliak, J.J. Jonas, A one-parameter approach to determining the critical conditions for the initiation of dynamic recrystallization. Acta Mater. 44(1), 127–136 (1996)CrossRefGoogle Scholar
  37. 37.
    C. Aranas et al., Determination of the critical stress for the initiation of dynamic transformation in commercially pure titanium. Scr. Mater. 133, 83–85 (2017)CrossRefGoogle Scholar
  38. 38.
    C. Ghosh et al., Dynamic transformation behavior of a deformed high carbon steel at temperatures above the Ae3. ISIJ Int. 53(5), 900–908 (2013)CrossRefGoogle Scholar

Copyright information

© The Korean Institute of Metals and Materials 2018

Authors and Affiliations

  1. 1.Department of Mechanical EngineeringÉcole de technologie supérieureMontrealCanada
  2. 2.Department of Mechanical EngineeringUniversity of New BrunswickFrederictonCanada
  3. 3.OperationsFinkl Steel - SorelSaint-Joseph-de-SorelCanada

Personalised recommendations