Journal of Mechanical Science and Technology

, Volume 33, Issue 8, pp 3749–3754 | Cite as

Bonding properties on diffusion bonding layer for micro PCD-WC tool fabrication

  • Uk-Su Kim
  • Seung-Sik Shin
  • Ki-Gwon Kim
  • Ba-Wi Jeong
  • Jeong-Woo ParkEmail author
Article
  • 7 Downloads

Abstract

This paper demonstrates the fabrication process of precision machining tools from polycrystalline diamond (PCD) attached on tungsten carbide (WC) tips and WC shanks via diffusion bonding with a nickel alloy filler metal. The join was investigated using micro X-ray computed tomography (micro-CT), and the strength of the bond was measured via tensile strength tests. Diffusion bonding was carried out with various pressures and various time durations. The micro-CT results showed that the nickel alloy filler metal between the PCDWC composite tip and WC shank disappeared at higher pressures. Voids were observed if the pressure was too low or the time duration for bonding was not enough. The presence of these voids can result in insufficient bonding force of the join, and hence leads to unpredictable failure of the tool. The pressure was found to affect the properties of the bond more significantly than the bonding time. Diffusion bonding with high quality joins between PCD-WC and WC can be achieved at relatively low temperature under 1000 °C through high pressure around 24 MPa and relatively long bonding time durations.

Keywords

PCD tool Diffusion bonding Bonding layer Micro X-ray computed tomography Tensile strength test Tungsten carbide 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Notes

Acknowledgments

This research was partially supported by research fund from Chosun University 2018 and Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Education (NRF-2017R1D1A1 B03031463).

References

  1. [1]
    R. Venter, S. Critchley and M. C. de Malherbe, The evaluation of tungsten carbide properties as applied to high pressure equipment, Materials Science and Engineering, 19 (2) (1975) 201–210.CrossRefGoogle Scholar
  2. [2]
    Z. Yao, J. J. Stiglich and T. S. Sudarshan, Nano-grained tungsten carbide-cobalt (WC/Co), Materials Modification (1999) 1–27.Google Scholar
  3. [3]
    P.-L. Tso and Y.-G. Liu, Study on PCD machining, International Journal of Machine Tools & Manufacture, 42 (3) (2002) 331–336.CrossRefGoogle Scholar
  4. [4]
    B. Ravisanker, J. Krisnamoorthi, S. S. Ramakrishnan and P. C. Angelo, Diffusion bonding of SU 263, Journal of Materials Processing Technology, 209 (4) (2009) 2135–2144.CrossRefGoogle Scholar
  5. [5]
    Rusnaldy, Diffusion bonding: An advanced of material process, ROTASI, 3 (1) (2001) 23–27.Google Scholar
  6. [6]
    B. W. Jeong and J. W. Park, Transient liquid phase diffusion bonding for micro PCD tool fabrication, Journal of Mechanical Science and Technology, 27 (10) (2013) 3005–3010.CrossRefGoogle Scholar
  7. [7]
    B. W. Jeong and J. W. Park, Temperature dependency of diffusion bonding for micro WC-PCD tool fabrication, Journal of the Korean Society of Manufacturing Technology Engineers, 22 (5) (2013) 812–817.CrossRefGoogle Scholar
  8. [8]
    I. K. Byun and H. S. Jung, The study on diffusion bonding of hard metal to high speed steel, The Korean Welding and Joining Society (2000) 317–319.Google Scholar
  9. [9]
    I. Tiseanu, L. Zani, T. Craciunescu, F. Cotorobai, C. Dobrea and A. Sima, Characterization of superonducting wires and cables by X-ray micro-tomography, Fusion Engineering and Design, 88 (9-10) (2013) 1613–1619.CrossRefGoogle Scholar
  10. [10]
    T. Klunsner, S. Wurster, P. Supancic, R. Ebner, M. Jenko, J. Glatzle, A. Puschel and R. Pippan, Effect of specimen size on the tensile strength of WC-Co hard metal, Acta Materialia, 59 (10) (2011) 4244–4252.CrossRefGoogle Scholar
  11. [11]
    D. Parkes, D. Westerbaan, S. S. Nayak, Y. Zhou, F. Goodwin, S. Bhole and D. L. Chen, Tensile properties of fiber laser welded joints of high strength low alloy and dual-phase steels at warm and low temperatures, Materials & Design, 56 (2014) 193–199.CrossRefGoogle Scholar

Copyright information

© KSME & Springer 2019

Authors and Affiliations

  • Uk-Su Kim
    • 1
  • Seung-Sik Shin
    • 1
  • Ki-Gwon Kim
    • 1
  • Ba-Wi Jeong
    • 1
  • Jeong-Woo Park
    • 2
    Email author
  1. 1.Department of Mechanical System & Automotive Engineering, College of EngineeringChosun UniversityGwangjuKorea
  2. 2.School of Mechanical System & Automotive Engineering, College of EngineeringChosun UniversityGwangjuKorea

Personalised recommendations