One-pot fabrication of robust hydrophobia and superoleophilic cotton fabrics for effective oil-water separation

  • 369 Accesses

  • 3 Citations

Abstract

A one-pot sonochemical irradiation method was developed for the fabrication of superhydrophobic and superoleophilic cotton fabric from a solution consisting of branched silica nanoparticles and tetraethoxysilane-dodecyltrimethoxysilane sol. The silica/sol-coated cotton fabric could be wetted by liquids of low surface tension, but was water repellent with a water contact angle of 159 ± 1.2° and water shedding angle of 6 ± 0.8°. The as-prepared cotton fabric could be used as effective materials for the separation of oil from water with separation efficiency as high as 98.2% and maintained separation efficiency above 94% after 30 separation cycles for the kerosene-water mixture. Moreover, the superhydrophobic and superoleophilic cotton fabric could maintain stable superhydrophobicity after treatment with strong acidic and alkali solutions, and harsh mechanical damage. Therefore, this reported robust superhydrophobic cotton fabric exhibits encouraging practical application for oil-water separation.

This is a preview of subscription content, log in to check access.

Access options

Buy single article

Instant unlimited access to the full article PDF.

US$ 39.95

Price includes VAT for USA

Subscribe to journal

Immediate online access to all issues from 2019. Subscription will auto renew annually.

US$ 99

This is the net price. Taxes to be calculated in checkout.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

References

  1. 1.

    Wang, B, Liang, W, Guo, Z, Liu, W, “Biomimetic Super-Lyophobic and Super-Lyophilic Materials Applied for Oil/Water Separation: A New Strategy Beyond Nature.” Chem. Soc. Rev., 44 336–361 (2015)

  2. 2.

    Xue, Z, Wang, S, Lin, L, Chen, L, Liu, M, Feng, L, Jiang, L, “A Novel Superhydrophilic and Underwater Superoleophobic Hydrogel-Coated Mesh for Oil/Water Separation.” Adv. Mater., 23 4270–4273 (2011)

  3. 3.

    Al-Majed, AA, Adebayo, AR, Hossain, ME, “A Sustainable Approach to Controlling Oil Spills.” J. Environ. Manag., 113 213–227 (2012)

  4. 4.

    Lessard, RR, DeMarco, G, “The Significance of Oil Spill Dispersants.” Spill. Sci. Technol. Bull., 6 59–68 (2000)

  5. 5.

    Jadhav, SR, Vemula, PK, Kumar, R, Raghavan, SR, John, G, “Sugar-Derived Phase-Selective Molecular Gelators as Model Solidifiers for Oil Spills.” Angew. Chem., 49 7695–7698 (2010)

  6. 6.

    Wang, FJ, Lei, S, Li, CQ, Qu, JF, Xue, MS, Li, W, “Superhydrophobic Cu Mesh Combined with a Superoleophilic Polyurethane Sponge for Oil Spill Adsorption and Collection.” Ind. Eng. Chem. Res., 53 7141–7148 (2014)

  7. 7.

    Feng, L, Zhang, Z, Mai, Z, Ma, Y, Liu, B, Jiang, L, Zhu, D, “A Super-Hydrophobic and Super-Oleophilic Coating Mesh Film for the Separation of Oil and Water.” Angew. Chem. Int. Ed., 43 2012–2014 (2004)

  8. 8.

    Jing, B, Wang, H, Lin, KY, McGinn, PJ, Na, C, Zhu, Y, “A Facile Method to Functionalize Engineering Solid Membrane Supports for Rapid and Efficient Oil–Water Separation.” Polymer, 54 5771–5778 (2013)

  9. 9.

    Cao, Y, Liu, N, Fu, C, Li, K, Tao, L, Feng, L, Wei, Y, “Thermo and pH Dual-Responsive Materials for Controllable Oil/Water Separation.” ACS Appl. Mater. Interfaces, 6 2026–2030 (2014)

  10. 10.

    Ouyang, SS, Wang, T, Jia, XY, Chen, Y, Yao, JM, Wang, S, “Self-Indicating and Recyclable Superhydrophobic Membranes for Effective Oil/Water Separation in Harsh Conditions.” Mater. Des., 96 357–363 (2016)

  11. 11.

    Zheng, X, Guo, ZY, Tian, DL, Zhang, XF, Li, WX, Jiang, L, “Underwater Self-Cleaning Scaly Fabric Membrane for Oily Water Separation.” ACS Appl. Mater. Interfaces, 7 (7) 4336–4343 (2015)

  12. 12.

    Tian, DL, Zhang, XF, Wang, X, Zhai, J, Jiang, L, “Micro/nanoscale Hierarchical Structured ZnO Mesh Film for Separation of Water and Oil.” Phys. Chem. Chem. Phys., 13 14606–14610 (2011)

  13. 13.

    Wu, L, Zhang, JP, Li, BC, Wang, AQ, “Mechanical- and Oil-Durable Superhydrophobic Polyester Materials for Selective Oil Absorption and Oil/Water Separation.” J. Colloid. Interface Sci, 413 112–117 (2014)

  14. 14.

    Li, BC, Wu, L, Li, LX, Seeger, S, Zhang, JP, Wang, AQ, “Superwetting Double-Layer Polyester Materials for Effective Removal of Both Insoluble Oils and Soluble Dyes in Water.” ACS Appl. Mater. Interfaces, 6 (14) 11581–11588 (2014)

  15. 15.

    Pham, VH, Dickerson, JH, “Superhydrophobic Silanized Melamine Sponges as High Efficiency Oil Absorbent Materials.” ACS Appl. Mater. Interfaces, 6 14181–14188 (2014)

  16. 16.

    Chen, N, Pan, QM, “Versatile Fabrication of Ultralight Magnetic Foams and Application for Oil–Water Separation.” ACS Nano., 7 6875–6883 (2013)

  17. 17.

    Calcagnile, P, Fragouli, D, Bayer, IS, Anyfantis, GC, Martiradonna, L, Cozzoli, PD, Cingolani, R, Athanassiou, A, “Magnetically Driven Floating Foams for the Removal of Oil Contaminants from Water.” ACS Nano., 6 5413–5419 (2012)

  18. 18.

    Sun, HY, Xu, Z, Gao, C, “Multifunctional, Ultra-Flyweight, Synergistically Assembled Carbon Aerogels.” Adv. Mater., 25 2554–2560 (2013)

  19. 19.

    Liang, HW, Guan, QF, Chen, LF, Zhu, Z, Zhang, WJ, Yu, SH, “Macroscopic-Scale Template Synthesis of Robust Carbonaceous Nanofiber Hydrogels and Aerogels and Their Applications.” Angew. Chem. Int. Ed., 51 5101–5105 (2012)

  20. 20.

    Wang, J, Shang, LR, Cheng, Y, Ding, HB, Zhao, YJ, Gu, ZZ, “Microfluidic Generation of Porous Particles Encapsulating Spongy Graphene for Oil Absorption.” Small, 11 3890–3895 (2015)

  21. 21.

    Kwon, G, Post, E, Tuteja, A, “Membranes with Selective Wettability for the Separation of Oil–Water Mixtures.” MRS Commun., 5 475–494 (2015)

  22. 22.

    Liu, MM, Li, J, Shi, L, Guo, ZG, “Stable Underwater Superoleophobic Conductive Polymer Coated Meshes for High-Efficiency Oil–Water Separation.” RSC Adv., 5 (42) 33077–33082 (2015)

  23. 23.

    Tian, DL, Guo, ZY, Wang, YL, Li, WX, Zhang, X, Zhai, J, Jiang, L, “Photo-Tunable Underwater Oil-Adhesion of the Micro/Nanoscale Hierarchical Structured ZnO Mesh Films with Switchable Contact Mode.” Adv. Funct. Mater., 24 536–542 (2014)

  24. 24.

    Tian, DL, Zhang, XF, Tian, Y, Wu, Y, Wang, X, Zhai, J, Song, YL, Jiang, L, “Photo-Induced Water-Oil Separation Based on Switchable Superhydrophobicity-Superhydrophilicity and Underwater Superoleophobicity of the Aligned ZnO Nanorod Array-Coated Mesh Films.” J. Mater. Chem., 22 19652–19657 (2012)

  25. 25.

    Feng, XJ, Shi, YL, Liu, J, Yang, W, “Fabrication of Filter Paper with Tunable Wettability and Its Application in Oil–Water Separation.” J. Sol–Gel Sci. Technol., 76 129–137 (2015)

  26. 26.

    Zhang, M, Wang, CY, Wang, SL, Li, J, “Fabrication of Superhydrophobic Cotton Textiles for Water–Oil Separation Based on Drop-Coating Route.” Carbohydr. Polym., 97 59–64 (2013)

  27. 27.

    Wu, L, Zhang, JP, Li, BC, Wang, AQ, “Mimic Nature, Beyond Nature: Facile Synthesis of Durable Superhydrophobic Textiles Using Organosilanes.” J. Mater. Chem. B, 1 4756–4763 (2013)

  28. 28.

    Li, SH, Huang, JY, Ge, MZ, Li, SW, Xing, TL, Chen, GQ, Liu, YQ, Zhang, KQ, Al-Deyab, SS, Lai, YK, “Controlled Grafting Superhydrophobic Cellulose Surface with Environmentally–friendly Short Fluoroalkyl Chains by ATRP.” Mater. Des., 85 815–822 (2015)

  29. 29.

    Li, SH, Huang, JY, Ge, MZ, Cao, CY, Deng, S, Zhang, SN, Chen, GQ, Zhang, KQ, Al-Deyab, SS, Lai, YK, “Robust Flower-Like TiO2@cotton Fabrics with Special Wettability for Effective Self-Cleaning and Versatile Oil/Water Separation.” Adv. Mater. Interfaces, 2 1500220 (2015)

  30. 30.

    Guo, P, Zhai, SR, Xiao, ZY, An, QD, “One-Step Fabrication of Highly Stable, Superhydrophobic Composites from Controllable and Low-cost PMHS/TEOS Sols for Efficient Oil Cleanup.” J. Colloid. Interface Sci., 446 155–162 (2015)

  31. 31.

    Wu, XH, Fu, QT, Kumar, D, Ho, JWC, Kanhere, P, Zhou, HF, Chen, Z, “Mechanically Robust Superhydrophobic and Superoleophobic Coatings Derived by Sol–Gel Method.” Mater. Des., 89 1302–1309 (2016)

  32. 32.

    Cortese, B, Caschera, D, Federici, F, Ingo, GM, Gigli, G, “Superhydrophobic Fabrics for Oil–Water Separation Through a Diamond like Carbon (DLC) Coating.” J. Mater. Chem. A, 2 6781–6789 (2014)

  33. 33.

    Huang, JY, Li, SH, Ge, MZ, Wang, LN, Xing, TL, Chen, GQ, Liu, XF, Al-Deyab, SS, Zhang, KQ, Chen, T, Lai, YK, “Robust Superhydrophobic TiO2@fabrics for UV Shielding, Self-Cleaning and Oil–Water Separation.” J. Mater Chem. A, 3 2825–2832 (2015)

  34. 34.

    Wang, JF, Tsuzuki, T, Tang, B, Sun, L, Dai, XJ, Rajmohan, GD, Li, JL, Wang, XG, “Recyclable Textiles Functionalized with Reduced Graphene Oxide@ZnO for Removal of oil Spills and Dye Pollutants.” Aust. J Chem., 67 71–77 (2013)

  35. 35.

    Zhou, XY, Zhang, ZZ, Xu, XH, Guo, F, Zhu, XT, Men, XH, Ge, B, “Robust and Durable Superhydrophobic Cotton Fabrics for Oil/Water Separation.” ACS Appl. Mater. Interfaces, 5 7208–7214 (2013)

  36. 36.

    Zeng, C, Wang, HX, Zhou, H, Lin, T, “Self-Cleaning, Superhydrophobic Cotton Fabrics with Excellent Washing Durability, Solvent Resistance and Chemical Stability Prepared from an SU-8 Derived Surface Coating.” RSC Adv., 5 61044–61050 (2015)

  37. 37.

    Zhou, H, Wang, HX, Niu, HT, Gestos, A, Lin, T, “Robust, Self-Healing Superamphiphobic Fabrics Prepared by Two-step Coating of Fluoro-containing Polymer, Fluoroalkyl Silane, and Modified Silica Nanoparticles.” Adv. Funct. Mater., 23 1664–1670 (2013)

  38. 38.

    Perelshtein, I, Applerot, G, Perkas, N, Wehrschetz-Sigl, E, Hasmann, A, Guebitz, GM, Gedanken, A, “Antibacterial Properties of an In Situ Generated and Simultaneously Deposited Nanocrystalline ZnO on Fabrics.” ACS Appl. Mater. Interfaces, 1 (2) 363–366 (2009)

  39. 39.

    Enis, KH, Birer, Ö, Karakus, K, Yıldırım, C, “Shadow-Casted Ultrathin Surface Coatings of Titanium and Titanium/Silicon Oxide Sol Particles via Ultrasound-Assisted Deposition.” Ultrason. Sonochem., 31 481–489 (2016)

  40. 40.

    Lu, Y, Sathasivam, S, Song, JL, Crick, CR, Carmalt, CJ, Parkin, IP, “Robust Self-Cleaning Surfaces that Function when Exposed to Either Air or Oil.” Science, 347 1132–1136 (2015)

  41. 41.

    Zhang, JP, Seeger, S, “Polyester Materials with Superwetting Silicone Nanofilaments for Oil/Water Separation and Selective Oil Absorption.” Adv. Funct. Mater., 21 4699–4704 (2011)

  42. 42.

    Okano, T, Sarko, A, “Mercerization of Cellulose. I. X-ray Diffraction Evidence for Intermediate Structures.” J. Appl. Polym. Sci., 29 4175–4182 (1984)

  43. 43.

    Perelshtein, I, Applerot, G, Perkas, N, Wehrschetz-Sigl, E, Hasmann, A, Guebitz, G, Gedanken, A, “Antibacterial Properties of an In Situ Generated and Simultaneously Deposited Nanocrystalline ZnO on Fabrics.” ACS Appl. Mater. Interfaces, 1 361–366 (2008)

Download references

Acknowledgments

The authors are thankful for the financial support of Natural Science Foundation of Jiangsu Province of China (Grants BK20150072).

Author information

Correspondence to Chengguo Liu or Yonghong Zhou.

Electronic supplementary material

Below is the link to the electronic supplementary material.

Supplementary material 2 (MP4 18586 kb)

Supplementary material 1 (DOCX 4031 kb)

Supplementary material 2 (MP4 18586 kb)

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Shang, Q., Liu, C. & Zhou, Y. One-pot fabrication of robust hydrophobia and superoleophilic cotton fabrics for effective oil-water separation. J Coat Technol Res 15, 65–75 (2018). https://doi.org/10.1007/s11998-017-9947-0

Download citation

Keywords

  • Superhydrophobic
  • Superoleophilic
  • Cotton fabric
  • Sol-gel
  • Oil-water separation