Self-emulsifiable soybean oil phosphate ester polyols for low-VOC corrosion resistant coatings
- 272 Downloads
A series of soybean oil phosphate ester polyols (SOPEP) was prepared by reaction of fully epoxidized soybean oil with phosphoric acid and simultanoeous hydrolysis in the presence of a polar solvent. The polyols were characterized by determination of acid value, oxirane number, hydroxyl value, molecular weight (GPC), and FTIR spectra. These polyols with varying amounts of acid phosphate groups could be self-emulsified to form aqueous dispersions after neutralization with organic base. These aqueous dispersion showed varying degrees of stability and their appearance ranged from opaque dispersions to translucent to clear solutions. Waterborne coating compositions were prepared using these aqueous dispersions as principal components and their thermally cured film properties were studied. it was found that by careful selection and formulation, SOPEPs can be successfully used for low-VOC waterborne coating formulations. SOPEPs with 3.5% phosphate ester content showed visibly superior corrosion resistance properties.
KeywordsSoybean oil phosphate ester polyols self-emulsified aqueous dispersion corrosion resistance VOC corrosion testing hardness scratch resistance solvent resistance alkyds oils (castor) linseed styrenated sunflower waterborne adhesion corrosion weath erability container enamel high-solids water-based VOC control epoxy esters oxygenated VOC aluminum iron cast iron steel
Unable to display preview. Download preview PDF.
- (4).Sato, S.H., Peloggia, T., Hunt, J., Schwarzer, R., Bueno, C., and Lovald, R.A., “Process for the Preparation of Polyamides”, U.S. Patent 6,011, 131, 2000.Google Scholar
- (8).Raghavachar, R., Sarnecki, G., Baghdachi, J., and Massingill, J., Jr., “Cationic UV Cured Coatings Using Epoxidized Soybean Oil”, RadTech Report, 12, 36–40 (1998).Google Scholar
- (10).Lin, G., Baghdachi, J., and Massingill, J. Jr., “Alkyd Coatings from Hyperbranched Polyols”, Proc. 79th Annual Meeting of the Federation of Societies for Coatings Technology, Atlanta, GA, November 4–7, 2001.Google Scholar
- (11).Guo, Y., Hardesty, J., Mannari, V., and Massingill, J. Jr., “Hydrolysis of Epoxidized Soybean Oil”, under review at J. Am. Oil Chem. Soc. Google Scholar
- (13).Massingill, J. Jr., “Organic Solvent Solutions of Phosphate Esters of Epoxy Resins”, U.S. Patent 5,086,094, 1992.Google Scholar
- (15).Massingill, J. Jr., “Adhesion and Flexibility Contributions to the Performance of Epoxy Phosphate Ester Coastings”, J. Coat. Technol., 63, No. 797, 47 (1991).Google Scholar