Analytic model of non-uniform corrosion induced cracking of reinforced concrete structure

  • Xiao-gang Zhang (张小刚)Email author
  • Xue-zhi Wang (王学志)
  • Zhao-hui Lu (卢朝辉)
  • Feng Xing (邢锋)
Article
First Online:

Abstract

In order to perfectly reflect the dynamic corrosion of reinforced concrete (RC) cover in practical engineering, an analytic model of non-uniform corrosion induced cracking was presented based on the elastic-plastic fracture mechanics theory. Comparisons with the published experimental data show that the predictions given by the present model are in good agreement with the results both for natural exposed experiments and short-time indoor tests (the best difference is about 2.7%). Also it obviously provides much better precision than those models under the assumption of uniform corrosion (the maximal improved precision is about 48%). Therefore, it is pointed out that the so-called uniform corrosion models to describe the cover cracking of RC should be adopted cautiously. Finally, the influences of thickness of local rusty layer around the reinforcing steel bar on the critical corrosion-induced crack indexes were investigated. It is found that the thickness of local rusty layer has great effect on the critical mass loss of reinforcing steel, threshold expansion pressure, and time to cover cracking. For local rusty layer thickness with a size of a = 0.5 mm, the time to cover cracking will increase by about one times when a/b (a, semi-minor axis; b, semi-major axis) changes from 0.1 to 1 mm.

Key words

reinforced concrete non-uniform corrosion induced cracking dynamic cracking local rusty layer stress intensity factor 
This is a preview of subscription content, log in to check access.

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    PANTAZOPOLOU S J, PAPOULIA K D. Modeling cover-cracking due to reinforcement corrosion in RC structures [J]. Journal of Engineering Mechanics, 2001, 127(4): 342–351.CrossRefGoogle Scholar
  2. [2]
    TAMER E L, MAADDAW Y, KHALED S. A model for prediction of time from corrosion initiation to corrosion cracking [J]. Cement & Concrete Composites, 2007, 29: 168–175.CrossRefGoogle Scholar
  3. [3]
    WANG Xiao-hui, LIU Xi-la. Bond strength modeling for corroded reinforcements [J]. Construction and Building Materials, 2006, 20: 177–186.CrossRefGoogle Scholar
  4. [4]
    KAPILESH B, GHOSH A K, YASUHIRO M, RAMANUJAM S. Analytical model for time to cover cracking in RC structures due to rebar corrosion [J]. Nuclear Engineering and Design, 2006, 236: 1123–1139.CrossRefGoogle Scholar
  5. [5]
    KAPILESH B, GHOSH A K, YASUHIRO M, RAMANUJAM S. Model for cover cracking due to rebar corrosion in RC structures [J]. Engineering Structures, 2006, 28: 1093–1109.CrossRefGoogle Scholar
  6. [6]
    LI Shu-cai, WANG Ming-bin, LI Shu-chen. Model for cover cracking due to corrosion expansion and uniform stresses at infinity [J]. Applied Mathematical Modelling, 2008, 32(7): 1436–1444.CrossRefGoogle Scholar
  7. [7]
    XU Gang, WEI Jun, ZHANG Ke-qiang, ZHOU Xi-wu. A calculation model for corrosion cracking in RC structures [J]. Journal of China University of Geosciences, 2007, 1(18): 85–89.CrossRefGoogle Scholar
  8. [8]
    YUAN Li-qun. The investigation and analysis of corroded and cracked reinforced concrete [D]. Xi’an: Xi’an University of Architecture & Technology, 2007. (in Chinese)Google Scholar
  9. [9]
    MURAKAMI Y. Stress intensity factors handbook [M]. Japan: The Society of Materials Science, Japan & Elsevier Science Ltd, 2001: 349–351.Google Scholar
  10. [10]
    XU Shi-lang, REINHARDT H W. Determination of double-K criterion for crack propagation in quasi-brittle fracture, Part III: Compact tension specimens and wedge splitting specimens [J]. International Journal of Fracture, 1999, 98(2): 179–193.CrossRefGoogle Scholar
  11. [11]
    XU Shi-lang, REINHARDT H W. Crack extension resistance and fracture properties of quasi-brittle softening materials like concrete based on the complete process of fracture [J]. International Journal of Fracture, 1998, 92(1): 71–99.CrossRefGoogle Scholar
  12. [12]
    REINHARDT H W, XU Shi-lang. Crack extension resistance based on the cohesive force in concrete [J]. Engineering Fracture Mechanics, 1999, 64(5): 563–587.CrossRefGoogle Scholar
  13. [13]
    LIU You-ping, RICHARD E W. Modeling the time-to-corrosion cracking in chloride contaminated reinforced concrete structures [J]. ACI Materials Journal, 1998, 95(6): 675–681.Google Scholar
  14. [14]
    TORRES-ACOSTA A A. Cracking induced by localized corrosion of reinforcement in chloride contaminated concrete [D]. Florida, USA: Department of Civil and Environmental Engineering, University of South Florida, 2005.Google Scholar
  15. [15]
    WU Zhi-min, XU Shi-lang, DING Yi-ning. The double-K fracture parameter of concrete for non-standard three point bending beam specimens [J]. China Engineering Science, 2001, 3(4): 76–81. (in Chinese)Google Scholar
  16. [16]
    MARK G S, ROSOWSKY D V. Time-dependent reliability of deteriorating reinforced concrete bridge decks [J]. Structural Safety, 1998, 20: 91–109.CrossRefGoogle Scholar

Copyright information

© Central South University Press and Springer-Verlag Berlin Heidelberg 2011

Authors and Affiliations

  • Xiao-gang Zhang (张小刚)
    • 1
    Email author
  • Xue-zhi Wang (王学志)
    • 2
  • Zhao-hui Lu (卢朝辉)
    • 3
  • Feng Xing (邢锋)
    • 1
  1. 1.Shenzhen Municipal Key Laboratory for Durability of Civil Engineering Structure, College of Civil EngineeringShenzhen UniversityShenzhenChina
  2. 2.College of Civil EngineeringLiaoning University of TechnologyJinzhouChina
  3. 3.School of Civil Engineering and ArchitectureCentral South UniversityChangshaChina

Personalised recommendations

Cite article

Buy options