, Volume 19, Issue 4, pp 986–991 | Cite as

Failure Analysis of a MW-Class Wind Turbine Blade Root Bolt

  • Zhunbei Zheng
  • Xiaochen WangEmail author
  • Wenbin Guo
  • Zhanjun Yang
  • Xingxin Sun
  • Xiuguang Li
Technical Article---Peer-Reviewed
  • 42 Downloads

Abstract

Failure analysis of a fractured high strength bolt used in a MW Class wind turbine blade connection system was conducted to clarify the failure cause and to determine the prevention method. Applying detailed mechanical characteristics and metallurgical investigations, the bolts failure cause can be attributed to bending fatigue. Evidenced by the nut polished markings, insufficient tightening was considered as the important reason for the bolt failure. The thread microstructure indicated that the fractured bolt thread was rolled rather than machined. However, rolling induced cracks locating on the thread crest and non-uniformly distributed decarburized layer on the bolt thread root existed. Thus, it can be concluded that the bolt failure was caused by the insufficient tightening and improper manufacturing procedure.

Keywords

Wind turbine blade High strength bolt Insufficient tightening Decarburized layer Cyclic bending fatigue 

Notes

Acknowledgment

This study was supported by the Datang Power Company Fundamental Research Funds under Grant No. JT2016-01.

References

  1. 1.
    A.R. Ghasemi, M. Mohandes, Composite blades of wind turbine: design, stress analysis, aeroelasticity, and fatigue, in Wind TurbinesDesign, Control and Applications (2016)Google Scholar
  2. 2.
    D. Liu, X. Shang, Failure investigation of the wind turbine blade root bolt. J. Fail. Anal. Prev. 13(3), 333–339 (2013)CrossRefGoogle Scholar
  3. 3.
    J. Zhang, A. Li, C. Zhang et al., Failure and fracture analysis of bolt assembled on the fan used in the internal combustion engine. J. Fail. Anal. Prev. 16(2), 302–309 (2016)CrossRefGoogle Scholar
  4. 4.
    J. Zhang, B.F. Wen, J.T. Zhao, W. Shi, Failure analysis on fracture of high-strength bolts for fastening wind turbine. Phys. Test. Chem. Anal. Part A: Phys. Test. 50(12), 933–935 (2014)Google Scholar
  5. 5.
    F.R. Hutchings, P.M. Unterweiser, Failure analysis: the British Engine Technical Reports. IEEE Trans. Reliab. 35(4), 374 (1986)CrossRefGoogle Scholar
  6. 6.
    Q. Zhao, F. Liu, L. Wang et al., Effects of Thread Rolling on 1240 MPa Titanium Hi-Bolt (Aeronautical Manufacturing Technology, Beijing, 2016)Google Scholar
  7. 7.
    J.A. Escobar, A.F. Romero, J. Lobo-Guerrero, Failure analysis of submersible pump system collapse caused by assembly bolt crack propagation by stress corrosion cracking. Eng. Fail. Anal. 60, 1–8 (2016)CrossRefGoogle Scholar

Copyright information

© ASM International 2019

Authors and Affiliations

  • Zhunbei Zheng
    • 1
  • Xiaochen Wang
    • 1
    • 2
    Email author
  • Wenbin Guo
    • 1
  • Zhanjun Yang
    • 1
  • Xingxin Sun
    • 1
  • Xiuguang Li
    • 1
  1. 1.China Datang Northwest Electric Power Test and Research InstituteXi’anChina
  2. 2.School of AutomationXi’an University of Post and TelecommunicationXi’anChina

Personalised recommendations