On the Critical Assessment into Damage Behavior of a WC–Co Hard Metal Alloy Used in the Form of Rock Drill Bits

  • Saurabh DewanganEmail author
Technical Article---Peer-Reviewed
  • 29 Downloads

Abstract

Cemented carbide possesses a good combination of wear resistance, strength and toughness. Therefore, it is mainly used as a tool material. During rock drilling and coal cutting operations, the cemented carbide undergoes a complex condition which limits the service life. It has been an interesting area of research to characterize different wear mechanisms in various working environments. The durability of the cemented carbide has been tested after using it for rock drilling, coal cutting and laboratory wear testing. The present work deals with rock drilling experiments. Granite samples were drilled by using three different grades of cemented carbides (possessing 5, 10 and 15% cobalt) based twist drill bits. All the experimental parameters were kept the same for each sample. After drilling, suitable samples of worn-out cemented carbides were prepared for examining under field emission scanning electron microscope and energy-dispersive spectroscopy. A critical characterization of wear mechanisms was performed. An attempt was made to identify wear behavior among the three grades of cemented carbide.

Keywords

WC–Co Drill bits Rock drilling Wear behavior Characterization 

Notes

References

  1. 1.
    Prodrill, www.rock-drill-bits.com/t38/Threaded-Button-Bit-02.html. Date of access 24 Oct 2017
  2. 2.
    Prodrill, www.rock-drill-bits.com/tricone-drill-bits/. Date of access 24 Oct 2017
  3. 3.
    Third edition 2012, www.atlascopco.com/blastholedrills. Date of access 24 Oct 2017
  4. 4.
    J. Dvoracek, R. Sousedikova, T. Vratny, Z. Jurekova, Global tungsten demand and supply forecast. Arch. Min. Sci. 62, 3–12 (2017)Google Scholar
  5. 5.
    R.S. Montgomery, The mechanism of percussive wear of tungsten carbide composites. Wear 12, 309–329 (1968)CrossRefGoogle Scholar
  6. 6.
    U. Beste, T. Hartzell, H. Engqvist, N. Axén, Surface damage on cemented carbide rock-drill buttons. Wear 249, 324–329 (2001)CrossRefGoogle Scholar
  7. 7.
    U. Beste, E. Coronel, S. Jacobson, Wear induced material modification of cemented carbide rock drills. Int. J. Refract. Met. Hard Mater. 24, 168–176 (2006)CrossRefGoogle Scholar
  8. 8.
    U. Beste, S. Jacobson, S. Hogmark, Rock penetration into cemented carbide drill buttons during rock drilling. Wear 264, 1142–1151 (2008)CrossRefGoogle Scholar
  9. 9.
    U. Beste, S. Jacobson, A new view of the deterioration and wear of WC/Co cemented carbide rock drill buttons. Wear 264, 1129–1141 (2008)CrossRefGoogle Scholar
  10. 10.
    S. Olovsjo, R. Johanson, F. Falsafi, U. Bexell, M. Olsson, Surface failure and wear of cemented carbide rock drill buttons—the importance of sample preparation and optimized microscopy settings. Wear 302, 1546–1554 (2013)CrossRefGoogle Scholar
  11. 11.
    J. Gurland, New scientific approaches to development of tool materials. Int. Mater. Rev. 33, 151–166 (1988)CrossRefGoogle Scholar
  12. 12.
    H.E. Exner, Physical and chemical nature of cemented carbides. Int. Mater. Rev. 4, 149–173 (1979)CrossRefGoogle Scholar
  13. 13.
    S. Dewangan, S. Chattopadhyaya, Critical analysis of wear mechanisms in cemented carbide. J. Mater. Eng. Perform. 24, 2628–2636 (2015)CrossRefGoogle Scholar
  14. 14.
    S. Dewangan, S. Chattopadhyaya, Characterization of wear mechanisms in distorted conical picks after coal cutting. Rock Mech. Rock Eng. 49, 225–242 (2016)CrossRefGoogle Scholar
  15. 15.
    S. Dewangan, S. Chattopadhyaya, S. Hloch, Critical damage analysis of WC–Co tip of conical pick due to coal excavation in mines. Adv. Mater. Sci. Eng. 2015, 7 (2015).  https://doi.org/10.1155/2015/292046 CrossRefGoogle Scholar
  16. 16.
    S. Dewangan, S. Chattopadhyaya, S. Hloch, Wear assessment of conical pick used in coal cutting operation. Rock Mech. Rock Eng. 48, 2129–2139 (2015)CrossRefGoogle Scholar
  17. 17.
    S. Nahak, S. Dewangan, S. Chattopadhyaya, Discussion on wear phenomena in cemented carbide. Proc. Earth Planet. Sci. 11, 284–294 (2015)CrossRefGoogle Scholar
  18. 18.
    S. Nahak, S. Dewangan, S. Chattopadhyaya, Wearing mechanisms of picks used in continuous miner machine for coal cutting. J. Mines Met. Fuels 64, 128–135 (2016)Google Scholar
  19. 19.
    S. Nahak, S. Dewangan, S. Chattopadhyaya, S. Hloch, Characterization of failure behaviour in distorted WC–Co tip of coal mining picks. J. Fail. Anal. Prev. 17, 136–143 (2017)CrossRefGoogle Scholar
  20. 20.
    S. Nahak, S. Dewangan, S. Chattopadhyaya, S. Hloch, G. Krolczyk, S. Legutko, Microstructural study of failure phenomena in WC 94%–Co 6% hard metal alloy tips of radial picks. Adv. Sci. Technol. Res. J. 11, 36–47 (2017)CrossRefGoogle Scholar
  21. 21.
    G. Dixon, R.N. Wright, M. Lee, Processes involved in the wear of cemented carbide tools. Proc. Int. Conf. Wear Mater. 1983, 218–226 (1983)Google Scholar
  22. 22.
    J. Larsen-Basse, Binder extrusion of sliding wear of WC–Co alloys. Proc. Int. Conf. Wear Mater. 5, 39–44 (1985)Google Scholar
  23. 23.
    Z. Tong, C. Ding, D. Yan, Size and shape characteristics of wear debris of WC + Co coating sliding against 45 steel. Chin. J. Met. Sci. Technol. 7, 282–287 (1991)Google Scholar
  24. 24.
    K. Jia, T.E. Fischer, Abrasion resistance of nanostructured and conventional cemented carbides. Wear 200, 206–214 (1996)CrossRefGoogle Scholar
  25. 25.
    J. Pirso, S. Letunovits, M. Viljus, Friction and wear behaviour of cemented carbides. Wear 257, 257–265 (2004)CrossRefGoogle Scholar
  26. 26.
    D.G.F. O’quigley, S. Luyckx, M.N. James, An empirical ranking of a wide range of WC–Co grades in terms of their abrasion resistance measured by the ASTM standard B 611-85 test. Int. J. Refract. Met. Hard Mater. 15, 73–79 (1997)CrossRefGoogle Scholar
  27. 27.
    J.Y. Sheikh-Ahamad, J.A. Bailey, The wear characteristics of some cemented tungsten carbides in machining particleboard. Wear 225–229, 256–266 (1999)CrossRefGoogle Scholar
  28. 28.
    S.I. Cha, S.H. Hong, G.H. Ha, B.K. Kim, Mechanical properties of WC–10Co cemented carbides sintered from nanocrystalline spray conversion processed powders. Int. J. Refract Metal Hard Mater. 19, 397–403 (2001)CrossRefGoogle Scholar
  29. 29.
    B. Casas, X. Ramis, M. Anglada, J.M. Salla, L. Llanes, Oxidation induced strength degradation of WC–Co hard metals. Int. J. Refract. Metal Hard Mater. 19, 303–309 (2001)CrossRefGoogle Scholar
  30. 30.
    S. Okamoto, Y. Nakazono, K. Otsuka, Y. Shimoitani, J. Takada, Mechanical properties of WC/Co cemented carbide with larger WC grain size. Mater. Charact. 55, 281–287 (2005)CrossRefGoogle Scholar
  31. 31.
    H. Saito, A. Iwabuchi, T. Shimizu, Effects of Co content and WC grain size on wear of WC cemented carbide. Wear 261, 126–132 (2006)CrossRefGoogle Scholar
  32. 32.
    J.A.M. Ferreira, M.A. Pina Amaral, F.V. Antunes, J.D.M. Costa, A study on the mechanical behaviour of WC/Co hardmetals. Int. J. Refract. Met. Hard Mater. 27, 1–8 (2009)CrossRefGoogle Scholar
  33. 33.
    P. Kindermann, P. Schlund, H.G. Sockel, M. Herr, W. Heinrich, K. Gorting, U. Schleinkofer, High-temperature fatigue of cemented carbides under cyclic loads. Int. J. Refract. Met. Hard Mater. 17, 55–68 (1999)CrossRefGoogle Scholar
  34. 34.
    J. Angseryd, V. From, J. Wallin, S. Jacobson, S. Norgren, On a wear test for rock drill inserts. Wear 301, 109–115 (2013)CrossRefGoogle Scholar
  35. 35.
    M.G. Gee, V. Gant, B. Roebuck, Wear mechanisms in abrasion and erosion of WC/Co and related hardmetals. Wear 263, 137–148 (2007)CrossRefGoogle Scholar

Copyright information

© ASM International 2019

Authors and Affiliations

  1. 1.Department of Mechanical EngineeringManipal University JaipurDehmi Kalan, JaipurIndia

Personalised recommendations