Application of EIS and SECM Studies for Investigation of Anticorrosion Properties of Epoxy Coatings containing ZrO2 Nanoparticles on Mild Steel in 3.5% NaCl Solution

Technical Article---Peer-Reviewed
  • 157 Downloads

Abstract

The effect of corrosion protection performance of epoxy coatings containing zirconium oxide (ZrO2) nanoparticles on carbon steel was analyzed using scanning electrochemical microscopy (SECM) and electrochemical impedance spectroscopy (EIS). Localized measurements such as oxygen consumption and iron dissolution were observed using SECM in 3.5% NaCl in the epoxy coated sample. Line profile and topographic image analysis were measured by applying −0.70 and +0.60 V as the tip potential for the cathodic and anodic reactions, respectively. The tip current at −0.70 V for the epoxy coated sample with ZrO2 nanoparticles decreased rapidly, which is due to cathodic reduction of dissolved oxygen. The EIS measurements were conducted in 3.5% NaCl after wet and dry cyclic corrosion test. The film resistance (R f) and charge transfer resistance (R ct) values were increased by the addition of ZrO2 nanoparticles in the epoxy coating. SEM/EDX analysis showed that oxides of Zr were enriched in corrosion products at a scratched area of the coated steel after corrosion testing. Focused ion beam-transmission electron microscope analysis confirmed the presence of the nanoscale oxide layers of Zr in the rust of the steel, which had a beneficial effect on the corrosion resistance of coated steel by forming protective corrosion products in the wet/dry cyclic test.

Keywords

Corrosion Epoxy coating ZrO2 Nanoparticle EIS SECM 

References

  1. 1.
    E. Bardel, Corrosion and Protection (Springer, London, 2003)Google Scholar
  2. 2.
    P.R. Roberge, Handbook of Corrosion Engineering (McGraw-Hill, New York, 1999)Google Scholar
  3. 3.
    E.S. Ferreira, C. Giacomelli, F.C. Giacomelli, A. Spinelli, Evaluation of the inhibitor effect of l-ascorbic acid on the corrosion of mild steel. Mater. Chem. Phys. 83, 129–134 (2004)CrossRefGoogle Scholar
  4. 4.
    M.M. Popovic, B.N. Grgur, V.B. Miskovic-Stankovic, Corrosion studies on electrochemically deposited PANI and PANI/epoxy coatings on mild steel in acid sulfate solution. Prog. Org. Coat. 52, 359–365 (2005)CrossRefGoogle Scholar
  5. 5.
    H. Leidheiser Jr., Corrosion of painted metals—a review. Corrosion 38, 374–383 (1982)CrossRefGoogle Scholar
  6. 6.
    Y. González-García, S. González, R.M. Souto, Electrochemical and structural properties of a polyurethane coating on steel substrates for corrosion protection. Corros. Sci. 49, 3514–3526 (2007)CrossRefGoogle Scholar
  7. 7.
    G.W. Walter, A critical review of the protection of metals by paints. Corros. Sci. 26, 27–38 (1986)CrossRefGoogle Scholar
  8. 8.
    E.P.M. van Westing, G.M. Ferrari, J.H.W. De Wit, The determination of coating performance with impedance measurements: I. Coating polymer properties. Corros. Sci. 34, 1511–1530 (1993)CrossRefGoogle Scholar
  9. 9.
    X. Zhang, F. Wang, Y. Du, Effect of nano-sized titanium powder addition on corrosion performance of epoxy coatings. Surf. Coat. Technol. 201, 7241–7245 (2007)CrossRefGoogle Scholar
  10. 10.
    K. Dhoke Shailesh, A.S. Khanna, T.J.M. Sinha, Effect of nano-ZrO2 particles on the corrosion behavior of alkyd-based waterborne coatings. Prog. Org. Coat. 64, 371–382 (2009)CrossRefGoogle Scholar
  11. 11.
    Xu Jiang, Jie Tao, Shuyun Jiang, Xu Zhong, Investigation on corrosion and wear behaviors of nanoparticles reinforced Ni-based composite alloying layer. Appl. Surf. Sci. 254, 4036–4043 (2008)CrossRefGoogle Scholar
  12. 12.
    T.A. Truc, T.T.X. Hang, V.K. Oanh, E. Dantras, C. Lacabanne, D. Oquab, N. Pébère, Incorporation of an indole-3 butyric acid modified clay in epoxy resin for corrosion protection of carbon steel. Surf. Coat. Technol. 202, 4945–4951 (2008)CrossRefGoogle Scholar
  13. 13.
    S. Kozhukharov, G. Tsaneva, V. Kozhukharov, J. Gerwann, M. Schem, T. Schmidt, M. Veith, Corrosion protection properties of composite hybrid coatings with involved nanoparticles of zirconia and ceria. J. Univ. Chem. Technol. 43, 73–80 (2008)Google Scholar
  14. 14.
    G. Gusmano, G. Montesperelli, M. Rapone, G. Padeletti, A. Cusmà, S. Kaciulis, A. Mezzi, R. Di Maggio, Zirconia primers for corrosion resistant coatings. Surf. Coat. Technol. 201, 5822–5828 (2007)CrossRefGoogle Scholar
  15. 15.
    J.F. Quinson, C. Chino, A.M. De Becdelievre, C. Guizard, M. Brunel, Deformation capability and protective role of zirconia coatings on stainless steel. J. Mater. Sci. 31, 5179–5184 (1996)CrossRefGoogle Scholar
  16. 16.
    J.C. Seegmiller, D.A. Buttry, A SECM study of heterogeneous redox activity at AA2024 surfaces. J. Electrochem. Soc. 150, B413–B418 (2003)CrossRefGoogle Scholar
  17. 17.
    J. Izquierdo, J.J. Santana, S. González, R.M. Souto, Uses of scanning electrochemical microscopy for the characterization of thin inhibitor films on reactive metals: the protection of copper surfaces by benzotriazole. Electrochim. Acta 55, 8791–8800 (2010)CrossRefGoogle Scholar
  18. 18.
    F.J. Martin, G.T. Cheek, W.E. O’Grady, P.M. Natishan, Impedance studies of the passive film on aluminium. Corros. Sci. 47, 3187–3201 (2005)CrossRefGoogle Scholar
  19. 19.
    R.M. Souto, Y. Gonzalez-Garcıa, S. Gonzalez, G.T. Burstein, Damage to paint coatings caused by electrolyte immersion as observed in situ by scanning electrochemical microscopy. Corros. Sci. 46, 2621–2628 (2004)CrossRefGoogle Scholar
  20. 20.
    R.M. Souto, Y. González-García, J. Izquierdo, S. González, Examination of organic coatings on metallic substrates by scanning electrochemical microscopy in feedback mode: revealing the early stages of coating breakdown in corrosive environments. Corros. Sci. 52, 748–753 (2010)CrossRefGoogle Scholar
  21. 21.
    R. Akid, D.J. Mills, A comparison between conventional macroscopic and novel microscopic scanning electrochemical methods to evaluate galvanic corrosion. Corros. Sci. 43, 1203–1216 (2001)CrossRefGoogle Scholar
  22. 22.
    X.J. Raj, T. Nishimura, Galvanic corrosion behaviour of iron coupled to aluminium in nacl solution by scanning eectrochemical microscopy. Prot. Met. Phys. Chem. Appl. Surf. 52, 543–554 (2016)CrossRefGoogle Scholar
  23. 23.
    X.J. Raj, T. Nishimura, Scanning electrochemical microscopy for the investigation of galvanic corrosion of iron with Zinc in 0.1 M NaCl solution. J. Mater. Eng. Perform. 25, 474–486 (2016)CrossRefGoogle Scholar

Copyright information

© ASM International 2016

Authors and Affiliations

  1. 1.Department of ChemistryVel Tech Dr.RR & Dr.SR Technical UniversityChennaiIndia
  2. 2.Department of ChemistryAnna UniversityChennaiIndia

Personalised recommendations