Failure Analysis of Steady Clamps Used in Electrified Railway

Case History---Peer-Reviewed
  • 135 Downloads

Abstract

In this study, cracks were detected in two steady clamps made of CuNi2Si alloy after approximately 6 months of service in an electrified railway system. Efforts were made to analyze the failure of the steady clamps using both experimental and finite-element (FE) methods. Microfractography revealed the brittle nature of the fracture. No microstructural degradation was found in the failed material. Extensive flake oxides were observed in the fracture. The investigation results suggest that the root cause of the failure was overlap defect which occurred in the forging process. The association of precracks induced by overlap defect with bolt preload resulted in premature failure.

Keywords

CuNi2Si alloy Failure analysis Steady clamp Overlap 

Notes

Acknowledgments

This work is funded by the National Science Foundation of China grant no. 51274162, National High Technology Research and Development Program of China (863 Program).

References

  1. 1.
    R.E. Kusner, J.C. Kuli Jr et al. A copper–nickel–silicon–chromium alloy for mold tooling. Mold Making Technol. (2007)Google Scholar
  2. 2.
    R. Monzen, C. Watanabe, Microstructure and mechanical properties of Cu–Ni–Si alloys. Mater. Sci. Eng. A 483–484, 117–119 (2008)CrossRefGoogle Scholar
  3. 3.
    S.A. Locker, M. Yun, J.D. Hunt et al., Micro- and macrodefects in thin sheet twin-roll cast aluminum alloys. Mater. Charact. 37, 301–310 (1996)CrossRefGoogle Scholar
  4. 4.
    Q. Chu, M. Zhang, J. Li, Failure analysis of impeller made of FV520B martensitic precipitated hardening stainless steel. Eng. Fail. Anal. 34, 501–510 (2013)CrossRefGoogle Scholar
  5. 5.
    M. Zhang, Q. Chu, J. Li et al., Failure analysis of a welded impeller in coke oven gas environment. Eng. Fail. Anal. 38, 16–24 (2014)CrossRefGoogle Scholar
  6. 6.
    E.A. Patterson, R.B. Johns, Theoretical analysis of the fatigue life of fixture screws in osseointegrated dental implants. Int. J. Oral Maxillofac. Implants 7, 26–33 (1992)Google Scholar
  7. 7.
    L.A. Lang, B. Kang, R.F. Wang, B.R. Lang, Finite element analysis to determine implant preload. J. Prosthet. Dent. 900(6), 539–546 (2003)CrossRefGoogle Scholar
  8. 8.
    D.G. Karalis, N.E. Melanitis, D.I. Pantelis, Failure analysis of a rock anchor made of stainless steel in marine environment. Eng. Fail. Anal. 19, 123–130 (2012)CrossRefGoogle Scholar

Copyright information

© ASM International 2014

Authors and Affiliations

  1. 1.College of Material Science and EngineeringXi’an University of TechnologyXi’anChina

Personalised recommendations