Journal of Failure Analysis and Prevention

, Volume 13, Issue 3, pp 320–327 | Cite as

Fracture Analysis of Blade of an Integrated Compressor Impeller

Technical Article---Peer-Reviewed

Abstract

During a trial test of a ZL104 al-alloy impeller, one of its blades experienced sudden catastrophic failure. Fractographic investigation indicates that the fracture mode of the blade is of instantaneous fracture. Metallurgical observation indicates that the fractured blade had been repair-welded on the sides of the lower and upper surfaces of blade before fracture. Multiple crack origins were found at the interface between the substrate and the repair welding layer at the side of the lower surface of the fractured blade. The defective casting process caused at least four shrinkage cavities in the substrate region at the side of the lower surface of blade, from which crack origins were initiated. The crack propagated from the lower surface toward the upper surface of blade. The presence of original casting defect of shrinkage cavities in the substrate at the side of the lower surface of blade which act as “stress raiser” is mainly responsible for the instantaneous fracture of the blade. Imperfect removal of original casting defects before repair-welding and the occurrence of numerous blowholes on the repair-welding layer can aggravate the problem, aiding in the crack propagation.

Keywords

Blade Repair-welding Shrinkage Blowhole Instantaneous fracture 

Reference

  1. 1.
    Kim, T.-G., Lee, H.-C.: Failure analysis of MVR (machinery vapor recompressor) impeller blade. Eng. Fail. Anal. 10, 307–315 (2003)CrossRefGoogle Scholar
  2. 2.
    Park, M., Hwang, Y.-H., Choi, Y.-S., Kim, T.-G.: Analysis of a J69-T-25 engine turbine blade fracture. Eng. Fail. Anal. 9, 539–601 (2002)Google Scholar
  3. 3.
    Yu, Z., Xu, X.: Failure investigation on inducer blades of locomotive turbocharger. J Fail. Anal. Prev. 10, 56–59 (2010)CrossRefGoogle Scholar
  4. 4.
    Mazur, Z., García-lllescas, R., Porcayo-Calderón, J.: Last stage blade failure analysis of a 28 MW geothermal turbine. Eng. Fail. Anal. 16, 1020–1032 (2009)CrossRefGoogle Scholar
  5. 5.
    Witek, L., Wierzbińska, M., Poznańka, A.: Fracture analysis of compressor blade of a helicopter engine. Eng. Fail. Anal. 16, 1616–1622 (2009)CrossRefGoogle Scholar
  6. 6.
    Gallardo, J.M., Soria, L., Herrera, E.J.: Investigation of service failures in automobile shock absorbers. Eng. Fail. Anal. 14, 355–363 (2007)CrossRefGoogle Scholar
  7. 7.
    Jha, A.K., Sreekumar, K.: Effect of pore and arcular eutetic silicon particles on the performance of Al-Si-Mg (AS7G03) casting. Eng. Fail. Anal. 16, 2433–2439 (2009)CrossRefGoogle Scholar
  8. 8.
    Mansoor, M., Ejaz, N., Tauqir, A.: Second phase structure effect to the failure of an Al–Si casting. Eng. Fail. Anal. 16, 1533–1549 (2009)CrossRefGoogle Scholar
  9. 9.
    Bagnoli, F., Bernabei, M., Ciliberto, A.: Failure analysis of an aircraft auxiliary power unit air intake door. Eng. Fail. Anal. 18, 284–294 (2011)CrossRefGoogle Scholar
  10. 10.
    Sujata, M., Bhuvana, R., Madan, M., Venkataswamy, M.A., Bhaumik, S.K.: Hydrogen-assisted cracking in boiler steam drums. J. Fail. Anal. Prev. 9, 213–221 (2009)CrossRefGoogle Scholar
  11. 11.
    Márquez, A., De Bona, J., Alija, A.: Failure analysis of a blower fan at a petrochemical plant. Eng. Fail. Anal. 16, 2417–2426 (2009)CrossRefGoogle Scholar
  12. 12.
    Pantazopoulos, G.A.: Failure analysis of a fractured hook-shaped steel rod from a lifting weight bridge beam. J Fail. Anal. Prev. 10, 18–22 (2010)CrossRefGoogle Scholar

Copyright information

© ASM International 2013

Authors and Affiliations

  1. 1.Electromechanics and Material Engineering CollegeDalian Maritime UniversityDalianPeople’s Republic of China
  2. 2.College of ScienceNortheast UniversityShenyangPeople’s Republic of China

Personalised recommendations