Journal of Failure Analysis and Prevention

, Volume 9, Issue 5, pp 420–428 | Cite as

Hydrogen-Induced Cracking (HIC) of Hardened and Tempered Steel Fastener Used in Space Application

Case History---Peer-Reviewed

Abstract

Cadmium-plated 0.35C–3.5Ni–1.5Cr–0.5Mo steel threaded fasteners of 1230 MPa properties class are used for aerospace applications. These fasteners were torqued to 13 N·m. Few fasteners parted into two pieces while in use under sustained assembly load for a period of 50 days. The fracture surface of the failed fasteners had two distinct regions when viewed under microscope at higher magnification. Fractography revealed that the larger region consisted of predominantly intergranular features, whereas the smaller region had features of microvoid coalescence. From the metallography evidences it was concluded that the fastener failure was due to hydrogen embrittlement. Electro-deposit of cadmium was identified to be the main source for hydrogen entrapment, which could not be compelled completely by post-plating baking treatment.

Keywords

0.35C–3.5Ni-1.5Cr–0.5Mo steel Hydrogen embrittlement 

Notes

Acknowledgments

The authors thank Dr. P.P. Sinha, Deputy Director, VSSC (MME), for his technical support during the investigation. They are indebted to Dr. K. Radakrishnanan, Director, VSSC, for permission to publish this work.

References

  1. 1.
    Carter, T.J., Cornish, L.A.: Hydrogen in metals. Eng. Fail. Anal. 8, 113–121 (2001)CrossRefGoogle Scholar
  2. 2.
    ASTM International, B 850-90 (reapproved 2004) standard guide for post-coating treatment of steel for reducing risk of hydrogen embrittlementGoogle Scholar
  3. 3.
    Eliaz, N., Shachar, A., Tal, B., Eliezer, D.: Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels. Eng. Fail. Anal. 9, 167–184 (2002)CrossRefGoogle Scholar
  4. 4.
    Troiano, A.R.: The role of hydrogen and other interstitials in the mechanical behaviors of metals, 1959 Edward De Mille Campbell Memorial Lecture, Trans ASM, vol. 52, pp. 54–80 (1960)Google Scholar
  5. 5.
    Oriani, R.A.: The diffusion and trapping of hydrogen in steel. Acta Metall. 18, 147–157 (1970)CrossRefGoogle Scholar
  6. 6.
    Gerberich, W.W., Marsh, P.G., Hoehn, J.W.: Hydrogen induced cracking mechanism—Are there critical experiments? Hydrogen Effects Mater. Miner. Met. Mater. Soc. 539–551 (1996)Google Scholar
  7. 7.
    Olden, V., Thaulow, C., Johnson, R.: Modelling of hydrogen diffusion and hydrogen induced cracking in supermartensitic and duplex stainless steels. Mater. Des. 29, 1934–1948 (2008)Google Scholar
  8. 8.
    Villalba, E., Atrens, A.: Hydrogen embrittlement and rock bolt stress corrosion cracking. Eng. Fail. Anal. 16, 164–175 (2009)CrossRefGoogle Scholar
  9. 9.
    Wang, M., Akiyama, A., Tsuzaki, K.: Hydrogen degradation of a boron-bearing steel with 1050 and 1300 MPa strength levels. Scr. Mater. 52(5), 403–408 (2005)CrossRefGoogle Scholar
  10. 10.
    Wang, M., Akiyama, E., Tsuzaki, K.: Effect of hydrogen on the fracture behavior of high strength steel during slow strain rate test. Corros. Sci. 49(11), 4081–4097 (2007)CrossRefGoogle Scholar
  11. 11.
    Marcelo, A.L., Tokimatsu, R.C., Ferreira, I.: Hydrogen embrittlement in a AISI 1045 steel component of the sugarcane industry. Eng. Fail. Anal. 16, 468–474 (2009)CrossRefGoogle Scholar
  12. 12.
    Beachem, C.D.: New model for hydrogen-assisted cracking (hydrogen embrittlement). Metall. Trans. 3, 437–451 (1972)CrossRefGoogle Scholar
  13. 13.
    Birnbaun, H.K., Sofronis, P.: Hydrogen enhanced localized plasticity—a mechanism for hydrogen related fracture. Mater. Sci. Eng. A 176, 191–202 (1994)CrossRefGoogle Scholar
  14. 14.
    Lynch, S.P.: Scr. Mater. doi: 10.1016/j.scriptamat.2009.02.031
  15. 15.
    Woodtli, J., Kieselbach, R.: Damage due to hydrogen embrittlement and stress corrosion cracking. Eng. Fail. Anal. 7, 427–450 (2000)CrossRefGoogle Scholar
  16. 16.
    Jha, A.K., Narayanan, P.R., Sreekumar, K., Mittal, M.C., Ninan, K.N.: Hydrogen embrittlement of 3.5Ni–1.5Cr–0.5Mo steel fastener. Eng. Fail. Anal. 15, 431–439 (2008)CrossRefGoogle Scholar

Copyright information

© ASM International 2009

Authors and Affiliations

  1. 1.Materials Characterization Division, Materials and Metallurgy GroupVikram Sarabhai Space Centre, Indian Space Research OrganisationTrivandrumIndia

Personalised recommendations