Journal of Failure Analysis and Prevention

, Volume 7, Issue 4, pp 282–291 | Cite as

Structural Failure of a Telescopic Shiploader during Installation

Peer Reviewed

Abstract

Failure of a telescopic shiploader during installation was investigated by using visual inspection, optical and electron microscopy, fracture toughness and tensile tests, and finite element calculation. Failure of this structure occurred at the time of loading the balance weight during installation. After putting 77 of the 80 tons of the balance weight, two nonprismatic beams on the upper part of the structure failed suddenly. The results of the failure analysis show that brittle fracture of one of the main horizontal beams acted as a main initiating factor for failure of the structure. These results indicate that brittle behavior of this beam occurred because of microcracks developed during one of the several welding processes made on this beam. The welding produced abnormal microstructure and cracks in the damaged area of the beam. The combination led to fracture and failure of the beam.

Keywords

Shiploader Structural failure Brittle fracture Damage 

References

  1. 1.
    Paulo MST de Castro, Fernandes A.A.: Methodologies for failure analysis: a critical survey. Mater. Des. 25, 117–23 (2004)Google Scholar
  2. 2.
    Failure Analysis and Prevention, vol. 11, 9th edn., Metals Handbook, ASM International, Metals Park, OH (1988)Google Scholar
  3. 3.
    Broek, D.: The Practical Use of Fracture Mechanics. Kluwer Academic Publishers (1988)Google Scholar
  4. 4.
    Cagatay, I.H.: Failure of an industrial building during a recent earthquake in Turkey. Eng. Fail. Anal. 12(4), 497–507 (2005)CrossRefGoogle Scholar
  5. 5.
    Dickson, J.I., Abramovici, E., Marchand, N.S. (eds.): Failure Analysis: Techniques and Applications. ASM International, Materials Park, OH (1992)Google Scholar
  6. 6.
    Blauel, J.G., Burdekin, F.M.: Case study collection on the assessment of the significance of weld imperfections. Weld. World. 37(4), 194–216 (1996)Google Scholar
  7. 7.
    Blandford, G.E.: Review of progressive failure analysis for truss structures. Struct. Eng. 123(2), 122–129 (1997)CrossRefGoogle Scholar
  8. 8.
    Wintle, J.B., Pargeter, R.J.: Technical failure investigation of welding structures. Eng. Fail. Anal. 12(2), 1027–1037 (2005)CrossRefGoogle Scholar
  9. 9.
    Brooks, C.R., Choudhury, A.: Failure Analysis of Engineering Materials. McGraw-Hill, New York (2002) Google Scholar
  10. 10.
    Thomas, J.M.: Industrial experience with structural failure. In: Wierzbicki, T., Jones, N. (eds.) Structural Failure, pp. 511–545. Wiley (1989)Google Scholar
  11. 11.
    ASTM standard E399-90 (1997) Standard Test Method for Plane-Strain Fracture Toughness of Metallic Materials, ASTM (1997)Google Scholar
  12. 12.
    Davis, J.R.: Carbon and Alloy Steels. ASM International, Materials Park, OH (1996) Google Scholar
  13. 13.
    Young, W.C., Budynas, R.G.: Roark’s Formulas for Stress and Strain, 7th edn. McGraw-Hill, New York (2002)Google Scholar
  14. 14.
    Gulyaev, A.P.: Brittle fracture resistance. Met. Sci. Heat Treat. 34(2), 110–119 (1992)CrossRefGoogle Scholar
  15. 15.
    Britain, G.: Brittle Fracture in Steel Structure. Butterworths (1970)Google Scholar
  16. 16.
    Rutti, T.F., Wentzel, E.J.: Investigation of Failed Actuator Piston Road. In: Jones, D.R. (ed.) Failure Analysis Case Studies II, pp. 139–146. Elsevier Science Ltd. (2001)Google Scholar
  17. 17.
    Kuwamura, H., Iyama, J., Yokoyama, Y.: Brittle fracture of beam-to-column welded connections in tall buildings. Steel Const. Eng. 4(16), 1–16 (1997) Google Scholar

Copyright information

© ASM International 2007

Authors and Affiliations

  1. 1.Department of Materials Science and EngineeringShiraz UniversityShirazIran
  2. 2.Department of Civil EngineeringShiraz University of TechnologyShirazIran

Personalised recommendations