Characterization of Microstructure, Mechanical Properties and Formability of Cryorolled AA5083 Alloy Sheets
- 88 Downloads
In this work, microstructure, mechanical properties and formability of cryorolled and annealed AA5083 alloy sheets have been characterized and a comparison has been made with cold rolled and annealed sheets. Five-millimeter-thick sheets of this alloy were cryorolled in multiple passes to a final thickness of 1 mm (80% reduction with a true strain of 1.6). Effect of annealing time and temperature on hardness has been studied, and it has been found that a short annealing at 275 °C for 15 min after cryorolling would yield a good combination of strength and ductility. Microstructural investigations showed that the cryorolled and short annealed samples possess bimodal grain structure which is responsible for better mechanical properties than cold rolled sheets. From the experimentally determined forming limit diagrams, the limit strains of cryorolled sheets have been found to be almost equal to conventional cold rolled and annealed sheets in all modes of deformation. No major differences have been found in strain distribution also. This work clearly demonstrates that cryorolling of AA5083 alloy sheets followed by a short annealing with bimodal grain structure can be used for sheet metal forming applications with higher strength and toughness than conventional sheets without any reduction in formability.
Keywordsaluminum alloy cold rolling cryorolling formability ultrafine grain structure
The authors acknowledge the help received from Prof. R. Jayaganthan, IIT Roorkee, Prof. I. Samjdar, IIT Bombay and Dr. S. Panigrahi, IIT Madras in characterization of the cold rolled and cryorolled samples.
- 1.I.J. Polmear, Light Alloys, Metallurgy of the Light Metals, 2nd ed., Edward Arnold, Melbourne, 1989, p 101–111Google Scholar
- 2.I.R. Dover and J.D. Embury, The Influence of Microstructural Features on the Formability of Aluminium Alloys, Mater. Forum, 1986, 9(4), p 188–201Google Scholar
- 6.D. Singh, P. Nageswararao, and R. Jayaganthan, Microstructural Studies of Al 5083 Alloy Deformed through Cryorolling, Adv. Mater. Res., 2012, 585, p 376–380. https://doi.org/10.4028/www.scientific.net/AMR.585.376 CrossRefGoogle Scholar
- 13.L.W. Quan, W.N. Mu, L. Kang, X. Ma, P. Han, and M.L. Huang, The Effect of Cryorolling on the Microstructure of Al-Cu-Mg Alloy, Mater. Sci. Forum, 2016, 877, p 188–193. https://doi.org/10.4028/www.scientific.net/MSF.877.188 CrossRefGoogle Scholar
- 26.I.A. Ovid’Ko and T.G. Langdon, Enhanced Ductility of Nanocrystalline and Ultrafine-Grained Metals, Rev. Adv. Mater. Sci., 2012, 30(2), p 103–111Google Scholar
- 28.Y. Wei, Y. Li, L. Zhu, Y. Liu, X. Lei, G. Wang, Y. Wu, Z. Mi, J. Liu, and H. Wang, Evading the Strength–ductility Trade-off Dilemma in Steel through Gradient Hierarchical Nanotwins, Nat. Commun., 2014, 5, p 3580Google Scholar
- 37.A.S. Taylor, M. Weiss, T. Hilditch, P.D. Hodgson, and N. Stanford, Cryo-Rolling and Formability of 2024 Aluminium, Mater. Sci. Forum, 2013, 765, p 434–438. https://doi.org/10.4028/www.scientific.net/MSF.765.434 CrossRefGoogle Scholar
- 41.K. Nakazima, T. Kikuma, and K. Hasuka, Study on the Formability of Steel Sheets, Yawata Tech. Rep., 1968, 264, p 8517–8530Google Scholar