Effect of Ladle Changeover Condition on Transient Three-Phase Flow in a Five-Strand Bloom Casting Tundish

  • Hua Zhang
  • Qing FangEmail author
  • Ronghua Luo
  • Chao Liu
  • Yi Wang
  • Hongwei NiEmail author
Article
  • 41 Downloads

Abstract

The transient three-phase flow behavior in a five-strand bloom casting tundish during the ladle changeover process considering a constant casting speed was investigated by the VOF model, and the effect of ladle throughput rate, shroud immersion depth, turbulence inhibitor structure and ladle changeover time on the turbulent flow, and level fluctuations during the filling process were analyzed to optimize the flow pattern in the tundish during ladle changeover. The results showed that the exposed area of molten steel in the impact zone increases as the ladle throughput rate increases during the filling process and that the exposure of molten steel is eliminated when the ladle throughput rate is 1.5Qsteady. As the immersion depth of the shroud increases, a slight decrease in slag entrainment happens, while the exposed area of molten steel first decreases and then increases. The shroud immersion depth should be 310 mm. When the optimized turbulence inhibitor is used, the wave crests of the steel level are greatly reduced, the height of the level fluctuation is alleviated with the maximum value decreasing from 33 mm to approximately 10 mm, and the exposure of molten steel is eliminated. When the ladle changeover time is between 2 and 3 minutes, the exposed area of molten steel during the stable period of the filling process is in the range from 150 to 170 cm2, which is substantially less than the exposed area of 500 cm2 when the ladle changeover time is 4 minutes. Therefore, the ladle changeover time should be controlled within 3 minutes. The flaw detection disqualification rate caused by ladle changeover operation is decreased from 43.8 to 25.8 pct of the total disqualified steel rails after optimization.

Notes

Acknowledgment

The authors would like to express their gratitude for the financial support provided by the National Natural Science Foundation of China (51774217 and 51604201) and the Research Project of Hubei Provincial Department of Education (D20171104).

References

  1. 1.
    K. Chattopadhyay, M. Isac and R.I.L. Guthrie: ISIJ Int., 2010, vol. 50, pp. 331-348.CrossRefGoogle Scholar
  2. 2.
    Y. Sahai: Metall. Mater. Trans. B, 2016, vol. 47B, pp. 2095-2106.CrossRefGoogle Scholar
  3. 3.
    S. Chatterjee, D. Li and K Chattopadhyay: Metall. Mater. Trans. B, 2018, vol. 49B, pp. 756-766.CrossRefGoogle Scholar
  4. 4.
    A. Vakhrushev, M. Wu, A. Ludwig, G. Nitzl, Y. Tang, G. Hackl and R. Wincor: Steel Res. Int., 2017, vol. 88, 1600276.CrossRefGoogle Scholar
  5. 5.
    A. Cwudziński: Int. J. Cast Metals Res., 2017, vol. 30, pp. 50-60.CrossRefGoogle Scholar
  6. 6.
    J. Zhang, S. Yang, M. Li, Z. Chen, Z. Jiang and J. Li: Ironmak. Steelmak., 2017, vol. 44, pp. 732-738.CrossRefGoogle Scholar
  7. 7.
    R. Bölling, H. Odenthal and H. Pfeifer: Steel Res. Int., 2005, vol. 76, pp. 71-80.CrossRefGoogle Scholar
  8. 8.
    J.M.F. Oro, C.S. Morros, J.R. Somoano, and M.A. Ordieres: ASME fluids Engineering Division Summer Meeting, 2009, pp. 2183–94.Google Scholar
  9. 9.
    M.I.H. Siddiqui, P.K. Jha: Steel Res. Int., 2016, vol. 87, pp. 733-744.CrossRefGoogle Scholar
  10. 10.
    S. Kant, P.K. Jha and P. Kumar: Ironmak. Steelmak., 2011, vol. 38, pp. 391-397.CrossRefGoogle Scholar
  11. 11.
    K. Takahashi, M. Ando and T. Ishii: ISIJ Int., 2014, vol. 54, pp. 304-310.CrossRefGoogle Scholar
  12. 12.
    H. Ling, L. Zhang and H. Li: Metall. Mater. Trans. B, 2016, vol. 47B, pp. 2991-3012.CrossRefGoogle Scholar
  13. 13.
    H. Ling, L. Zhang and H. Wang: Metall. Res. Technol., 2017, vol. 114, pp. 516.CrossRefGoogle Scholar
  14. 14.
    H. Ling and L. Zhang: JOM, 2013, vol. 65, pp. 1155-1163.CrossRefGoogle Scholar
  15. 15.
    S. Garcia-Hernandez, R.D. Morales, D.J.B. Jose, I. Calderon-Ramos and E. Gutierrez: Steel Res. Int., 2016, vol. 87, pp. 1154-1167.CrossRefGoogle Scholar
  16. 16.
    R.D. Morales, S. Garcia-Hernandez, J.D.J. Barreto, A. Ceballos-Huerta, I. Calderon-Ramos and E. Gutierrez: Metall. Mater. Trans. B, 2016, vol. 47B, pp. 2595-2606.CrossRefGoogle Scholar
  17. 17.
    M. M. Machado-Lopez, J. A. Ramos-Banderas, E. Torres-Alonso, J. J. Barreto, S. Garcia-Hernandez: Ironmak. Steelmak., 2013, vol. 40, pp. 326-334.CrossRefGoogle Scholar
  18. 18.
    ANSYS Fluent 15.0 Theory Guide, Southpointe, 2013.Google Scholar

Copyright information

© The Minerals, Metals & Materials Society and ASM International 2019

Authors and Affiliations

  1. 1.The State Key Laboratory of Refractories and MetallurgyWuhan University of Science and TechnologyWuhanP.R. China
  2. 2.Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of EducationWuhan University of Science and TechnologyWuhanP.R. China
  3. 3.Valin Xiangtan Iron and Steel Co., LtdXiangtanP.R. China

Personalised recommendations