Constrained Dendritic Growth and Solute Concentration Effects in Rapidly Solidified Co-Cr Alloys

  • A. L. Ramirez-LedesmaEmail author
  • H. F. Lopez
  • J. A. Juarez-Islas
Article
  • 73 Downloads

Abstract

Growth temperature and dendrite tip radius equations were employed in this work in order to predict the experimental conditions under which a Co-Cr alloy was produced having a single γ-phase microstructure free from interdendritic segregation. The outcome of these predictions indicated that in Co alloys containing 20 to 25 wt pct Cr, single γ-phase dendritic microstructures are achieved independently of the implemented solidification growth velocities. Moreover, these alloys are found to be essentially free from interdendritic segregation. Co alloys containing 30 to 35 wt pct Cr exhibit both the γ-phase and the eutectic constituent when solidification rates (V) are below 0.1 and 0.5 mm/s, respectively. Alternatively, the eutectic constituent is suppressed when the solidification growth velocities exceed these values. In particular, it is found that a single-phase microstructure can be achieved when the solidification growth rates exceed the transition velocity between constitutional supercooling and the absolute stability conditions.

Notes

Acknowledgments

The authors gratefully acknowledge the technical support from A. Tejeda and C. Flores-Morales and the financial support from UNAM/PAPIIT IT100316.

References

  1. 1.
    M. Niinomi, T. Narushima and M. Nakai: Advances in Metallic Biomaterials, Springer, Berlin, Heidelberg, 2015.Google Scholar
  2. 2.
    L. Ren and K. Yang: J. Mater. Sci. Technol., 2013, vol. 29, pp. 1005–10.CrossRefGoogle Scholar
  3. 3.
    T. Hanawa: Mater. Sci. Eng. A, 1999, vol. 267, pp. 260–66.CrossRefGoogle Scholar
  4. 4.
    M. Niinomi: Int. J. Fatigue, 2007, vol. 29, pp. 992–1000.CrossRefGoogle Scholar
  5. 5.
    R.M. Berlin, L.J. Gustavson, and K.K. Wang: in: Cobalt Base Alloys for Biomedical Applications, J.A. Disegi, R.L. Kennedy, and R. Pilliar, eds., ASTM International, West Conshohocken, PA, USA, 1999, pp. 62–70.Google Scholar
  6. 6.
    R. Kaiser, K. Williamson, C. O’Brien and D. J. Browne: Metall. Mater. Trans. A, 2013, vol. 44, pp. 5333–42.CrossRefGoogle Scholar
  7. 7.
    M. Gómez, H. Mancha, A. Salinas, J. L. Rodríguez, J. Escobedo, M. Castro and M. Méndez: J. Biomed. Mater. Res. A, 1997, vol. 34, pp. 157–63.CrossRefGoogle Scholar
  8. 8.
    M. Caudillo, M. Herrera–Trejo, M. R. Castro, E. Ramírez, C. R. González and J. I. Juárez: J. Biomed. Mater. Res. A, 2002, vol. 59, pp. 378–85.CrossRefGoogle Scholar
  9. 9.
    T. Narushima, Sh. Mineta, Y. Kurihara and K. Ueda: JOM, 2013, vol. 65, pp. 489–504.CrossRefGoogle Scholar
  10. 10.
    R. Rosenthal, B. R. Cardoso, I. S. Bott, R. P. R. Paranhos and E. A. Carvalho: J. Mater. Sci., 2010, vol. 45, pp. 4021–28.CrossRefGoogle Scholar
  11. 11.
    J. V. Giacchi, C. N. Morando, O. Formaro and H. A. Palacio: Mater. Charact., 2011, vol. 62, pp. 53–61.CrossRefGoogle Scholar
  12. 12.
    C. M. Agrawal: JOM, 1998, vol. 50, pp. 31–5.CrossRefGoogle Scholar
  13. 13.
    J. J. Jacobs, A. K. Skipor, P. A. Campbell, N. J. Hallab, R. M. Urban and H. C. Amstutz: J. Arthroplasty, 2004, vol. 19, pp. 59–65.CrossRefGoogle Scholar
  14. 14.
    S. Weiss and B. Mitevski: Materials, 2015, vol. 8, 2467–79.CrossRefGoogle Scholar
  15. 15.
    S. Diaz-Rodriguez, P. Chevallier and D. Mantovani: Plasma Process Polym., 2018, vol. 15, pp. 1–6.CrossRefGoogle Scholar
  16. 16.
    M. Niinomi: Metall. Mater. Trans. A, 2002, vol. 33, pp. 477–86.CrossRefGoogle Scholar
  17. 17.
    N. Sato, M. Kinbara, T. Kuroishi, K. Kimura, Y. Iwakura, H. Ohtsu, S. Sugawara and Y. Endo: Clin. Exp. Allergy, 2007, vol. 37, pp. 743–51.CrossRefGoogle Scholar
  18. 18.
    Sh.-H. Sun, Y. Koizumi, Sh. Kurosu, Y.-P. Li, H. Matsumoto and A. Chiba: Acta Mater., 2014, vol. 64, pp. 154–68.CrossRefGoogle Scholar
  19. 19.
    A. L. Ramirez-Ledesma, E. Lopez-Molina, H. F. Lopez and J. A. Juarez-Islas: Acta Mater., 2016, vol. 111, pp. 138–47.CrossRefGoogle Scholar
  20. 20.
    A.L. Ramirez Ledesma, H. Lopez, and J.A. Juarez-Islas: Metals, 2016, vol. 6, pp. 1–17.Google Scholar
  21. 21.
    R. V. Marrey, R. Burgermeister, R. B. Grishaber and R. O. Ritchie: Biomaterials, 2006, vol. 27, pp. 1988–2000.CrossRefGoogle Scholar
  22. 22.
    G. Mani, M. D. Feldman, D. Patel and C. M. Agrawal: Biomaterials, 2007, vol. 28, pp. 1689–1710.CrossRefGoogle Scholar
  23. 23.
    C. González, J. Genesca, O. Álvarez and J. A. Juarez-Islas: Metall. Mater. Trans. A, 2003, vol. 34, pp. 2991–97.CrossRefGoogle Scholar
  24. 24.
    W. Kurz and D. J. Fisher: Fundamentals of Solidification, Trans. Tech. Publications, Switzerland, Germany, 1984.Google Scholar
  25. 25.
    J. A. Juarez-Islas: J. Mater. Sci., 1991, vol. 26, pp. 5004–12.CrossRefGoogle Scholar
  26. 26.
    K. A. Jackson and D. Hunt: T. Metall. Soc. AIME, 1966, vol. 236, pp. 1129–42.Google Scholar
  27. 27.
    W. Kurz, B. Giovanola and R. Trivedi: Acta Metall., 1986, vol. 34, pp. 823–30.CrossRefGoogle Scholar
  28. 28.
    M. Abramowitz and I.A. Stegun, eds., Handbook of Mathematical Functions, Dover, New York, 1968.Google Scholar
  29. 29.
    L. Xin, L. Yanmin, W. Meng, F. Liping, C. Jing and H. Weidong: Sci. China Ser. E, 2003, vol. 46, pp. 475–89.CrossRefGoogle Scholar
  30. 30.
    S. R. Levine: Metall. Mater. Trans. A, 1978, vol. 9, pp. 1237–50.CrossRefGoogle Scholar
  31. 31.
    K. Ishida and T. Nishizawa: Bull. Alloy Phase Diagr., 1990, vol. 11, pp. 357–70.CrossRefGoogle Scholar
  32. 32.
    B. Wei, D. M. Herlach, F. Sommer and W. Kurz: Mat. Sci. Eng. A, 1993, vol. 173, pp. 357–61.CrossRefGoogle Scholar
  33. 33.
    A. Mani, Salinas-Rodriguez, and H. F. Lopez: Mater. Sci. Eng., A, 2011, vol. 528, pp. 3037–43.Google Scholar
  34. 34.
    S.-H. Lee, E. Takahashi, N. Nomura, and A. Chiba: Mater. Trans. JIM, 2005, vol. 46, pp. 1790–93.Google Scholar
  35. 35.
    B. Paul, R. Kapoor, J. K. Chakravartty, A. C. Bidaye, I. G. Sharma and A K. Suri: Scripta Mater., 2009, vol. 60, pp. 104–7.CrossRefGoogle Scholar
  36. 36.
    J. S. Langer and H. Müller-Krumbhaar: Acta Metall., 1978, vol. 26, pp. 1681–87.CrossRefGoogle Scholar
  37. 37.
    W. W. Müllins and R. F. Sekerka: J. Appl. Phys., 1964, vol. 35, pp. 444–51.CrossRefGoogle Scholar
  38. 38.
    W. Kurz and D. J. Fisher: Acta Metall., 1981, vol. 29, pp. 11–20.CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society and ASM International 2019

Authors and Affiliations

  • A. L. Ramirez-Ledesma
    • 1
    Email author
  • H. F. Lopez
    • 2
  • J. A. Juarez-Islas
    • 3
  1. 1.Department of Mechanical EngineeringPolitecnico di MilanoMilanItaly
  2. 2.Materials Science and Engineering Department, CEASUniversity of Wisconsin MilwaukeeMilwaukeeUSA
  3. 3.Instituto de Investigaciones en MaterialesUniversidad Nacional Autónoma de MéxicoMéxicoMexico

Personalised recommendations