Metallurgical and Materials Transactions A

, Volume 50, Issue 2, pp 581–589 | Cite as

Thermal Stability of Rolled Metastable Austenitic Stainless Steel 1.4307 Studied Using Positron Annihilation

  • E. DryzekEmail author
  • M. Sarnek
  • M. Wróbel
Open Access


Positron annihilation spectroscopy (PAS) was used in the study of cumulative isochronal and isothermal annealing of rolled 1.4307 (EN) stainless steel (SS). Due to different rolling temperatures, the SS samples varied in the α′-martensite volume fraction from 0.09 to 0.91. The measurements of positron annihilation characteristics, i.e., Doppler broadening (DB) of the annihilation line, showed a gradual annealing of vacancies in the temperature range between 200 °C and 400 °C, which indicated the first stage of recovery. This first stage of recovery did not change the microhardness. In the temperature range from 475 °C to 600 °C, a decrease in the microhardness and generation of new open volume defects accompanying the reversion of α′-martensite to austenite was observed. The amount of these defects correlated with the initial α′-martensite volume fraction. Their formation could be related to the volume contraction occurring during bcc/fcc transformation. The different chemical surroundings suggested that the positron trapping defects were associated with the metal carbide precipitates.

1 Introduction

Austenitic stainless steel (SS) is plastically deformed by a slip of dissociated dislocations because of low stacking fault energy (SFE). This effect produces hardening due to an increase in dislocation density (dislocation hardening), but also due to stacking faults and mechanical twins formation.[1,2] However, a large part of strain hardening results from the creation of deformation-induced martensite (DIM) caused by thermodynamic metastability of austenite at, or just below, room temperature (RT).[3,4] Annealing of cold-worked austenitic SS causes martensite reversion along with other phenomena including recovery, recrystallization, and carbide precipitation.[5,6] Several experimental techniques, such as microscopic examination, X-ray diffraction (XRD), and magnetic or mechanical properties measurements, have been applied to study the properties of cold-worked austenitic SS during annealing. However, new methods for fast industrial applications are investigated. Positron annihilation spectroscopy (PAS) offers further potential for such applications.

PAS is a well-known experimental method used for studying defects in crystalline solids such as metals, alloys, and semiconductors.[7] It is based on the following facts. When an energetic positron is implanted into a solid, it rapidly loses its energy, reaching thermal energy. After a short period of random walk, it annihilates with an electron, usually producing two high-energy annihilation photons. Their momentum carries information on the annihilation site’s surroundings. During their random walk, positrons can be trapped in crystal lattice imperfections, such as open volume defects, where the electron density is reduced in comparison to the perfect lattice. This causes changes of usually measured parameters: narrowing of the Doppler-broadened annihilation line and an increase in the positron lifetime. Vacancies, vacancy clusters, some grain boundaries, and interfaces, as well as the second-phase precipitations, can act as positron traps. Dislocations are also expected to provide trapping sites; however, they are rather shallow traps. The sensitivity of positron lifetime and width of the annihilation line form the basis for the two main PAS techniques, i.e., positron annihilation lifetime spectroscopy and doppler broadening (DB) of annihilation line to defect studies.

Our previous studies showed that reverse transformation of DIM in metastable austenitic SS is easily detected using PAS. The method revealed two processes that take place during annealing of compression-deformed SS samples that contain DIM: migration and sinking of vacancies and creation of additional lattice defects.[8,9] A significant change in the shape of the annihilation line was observed for the temperature range of α′-martensite reversions in the tension-deformed samples. The PL measurements indicated the presence of large vacancy clusters consisting of six to nine vacancies, which occurred at the interface between the austenite and α′ martensite phases due to the volume contraction accompanying the bcc/fcc transformation.[10] We believe that the nucleation and growth of metal carbide precipitates, mainly M23C6 type, could also provide positron trapping sites in the matrix-precipitate interfaces.[11]

The purpose of the present study was to investigate the use of the PAS technique to study 1.4307 (EN) SS samples deformed by rolling at different temperatures and to a much higher degree of deformation compared to our previous studies. This allowed us to examine how the amount of α′-martensite influenced defect formation during reverse transformation. We applied two different annealing methods: isochronal annealing and isothermal annealing at 550 °C and 650 °C. The temperatures of isothermal annealing were chosen to take into account the precipitation of M23C6 carbides leading to intergranular corrosion sensitivity of steel.[12] Other techniques, such as XRD, microhardness, and magnetic properties measurements, were used to supplement the PAS studies.

2 Materials and Methods

2.1 Sample Preparation

The measurements were carried out on the commercial 1.4307 (EN) SS, which is equivalent to AISI Grade 304L. Its chemical composition is given in Table I. SS samples of size 3 × 15 × 100 mm3 were subjected to 30-minute solution annealing at 1100 °C followed by cooling in air. After the heat treatment, the surfaces of the samples were etched with the use of hydrochloric acid and nitric acid water solution to obtain a clean surface.
Table I

Steel Composition (Weight Percent)

























To obtain a different amount of DIM, the samples were deformed at different temperatures. They were rolled one after another with the same settings of the mill. Multiple passes were used to obtain a final deformation. Before and immediately after each pass, sample A was immersed in liquid nitrogen (LN) for at least 15 minutes. Sample B was deformed at RT. Sample C was deformed at 200 °C and was heated in an air circulating furnace. The LN container and the furnace were located right next to the mill, and only a few seconds were required to transfer the samples to the mill. Due to the difference in deformation temperatures, the strain hardening was different and the final deformation ε varied slightly, as is shown in Table II.
Table II

Deformation Conditions, Saturation Magnetization per Unit Mass σs, and Volume Fraction of α′ Martensite fα′ Calculated from the σs Value Using Eq. [1]


Deformation ε (pct)

Deformation Temperature

σs (emu/g)

f α′




145.8 ± 2.1

0.91 ± 0.01




102.0 ± 0.5

0.64 ± 0.01



200 °C

14.7 ± 0.1

0.09 ± 0.01

RT—room temperature; LN—after immersion in liquid nitrogen

Three sets of specimens of 15 mm in length were cut from the rolled samples A, B, and C. Each set was used for positron annihilation measurements, which required two identical specimens, whereas additional specimens were used for XRD and microhardness measurements. Before the examination, the surface layer of all the samples was removed by electropolishing or etching to remove the possible effect of the preparation (i.e., cutting, polishing). The specimens were polished electrolytically according to Struers’ recommendation (A2 electrolyte, approximately 35 V). The samples that were used for optical microscopy (OM) observations were etched in an electrolyte consisting of 60 pct nitric acid and 40 pct H2O to reveal the general microstructure. To reveal the DIM, electropolishing was followed by etching in a mixture of 0.15 g of Na2S2O5 solved in 100 mL of distilled water and 10 mL of HCl solved in 100 mL of water.[13]

The specimens from the first set were subjected to cumulative isochronal annealing in the flow of nitrogen gas for 1 hour at temperatures in the range of 50 °C to 825 °C with 25 °C interval. The remaining two sets of samples were subjected to isothermal annealing at 550 °C and 650 °C, respectively. After annealing, the samples were etched to remove the oxidized surface layer. Finally, the samples were measured using the PAS, XRD, and microhardness techniques.

2.2 Magnetic Properties Measurements

The response of the deformed samples to the magnetic field was determined using an MPMS SQUID magnetometer. Magnetization curves up to 10 kOe were measured at RT for additional samples of dimensions approximately 3 × 2 × 1 mm3, cut using the low-speed diamond wheel saw, and etched to remove the layer deformed by cutting. The volume fraction of α′-martensite fα induced by plastic deformation was determined using the formula proposed by Mangonon and Thomas:[3]
$$ f_{{\alpha^{\prime}}} = {{\sigma_{s} } \mathord{\left/ {\vphantom {{\sigma_{s} } {160.4}}} \right. \kern-0pt} {160.4}} $$
where σs is the specific saturation magnetization per unit mass.

2.3 XRD, Microhardness, and Microstructure Studies

The samples’ phase composition was tested using the XRD measurements carried out using the Philips X-Pert diffractometer with Cu Kα radiation. The structural analyses using OM and scanning electron microscopy (SEM) were performed to reveal a general microstructure and DIM. Optical micrographs were recorded with the Zeiss Axio Imager M1m. The SEM observations were carried out using FEI Inspect S50. Microhardness studies were performed using a Wilson Hardness™ TUKON™1 2500 (Instron ITW) device. The measurements were done using the Knoop indenter at normal load of 100 g. For each measurement, two sets of indentations for the mutually perpendicular position of the indenter’s longest axis were made (from 10 to 16 indentations for one set). The results were recalculated to the Vickers standard units. All recommendations of the ISO 4545 standard were respected.[14]

2.4 PAS Measurements

PAS measurements were carried out using the 22Na positron source encapsulated in 7-μm-thick Kapton foil. The DB of the 511 keV annihilation line was measured using a coaxial high-purity germanium (HPGe) detector with a 1.4 keV energy resolution at the full width at half maximum (FWHM) interpolated at 511 keV. The measurements were performed at RT after each annealing step. To characterize the annihilation line shape, we used the so-called S and Wr parameters. The S parameter is defined as the ratio of the area under the fixed central part of the annihilation line, i.e., the energy range 511.0 ± 1.1 keV, to the area under the entire peak. The S parameter is sensitive to the annihilation of positrons with low momentum electrons, which are present in open volume defects. The wing parameter Wr value is the ratio of the area under the right wing of the annihilation line to the area under the entire annihilation line. The Wr parameter is mainly influenced by the positron annihilation with core electrons, which have higher momenta. It is also affected by the chemical surroundings of the annihilation site. The Wr-parameter energy range was between 514.9 and 516.9 keV. Information on the defect type changes was derived from the correlation between the S and Wr parameters. The values of the S and Wr parameters were evaluated using the SP-11 code.[15]

The positron lifetime (PL) measurements were performed at RT for the as-deformed samples and the samples annealed at selected temperatures. The PL spectra of more than 1.5 × 106 counts were collected using the so-called fast-fast spectrometer with BaF2 scintillators. The time resolution of the spectrometer was equal to 270 ps (FWHM). All the obtained spectra were analyzed using the LT-code subtracting contribution of the positron source and background.[16]

3 Results

3.1 The Initial As-Deformed State

Figure 1 shows the XRD patterns for samples A, B, and C after rolling. For sample C deformed at 200 °C, peaks from the γ phase are predominant in comparison to two other samples deformed at lower temperatures, i.e., samples A and B deformed close to the LN and RT, respectively. For the latter, peaks originating from α′-martensite are mainly visible.
Fig. 1

XRD patterns for as-deformed samples A, B, and C rolled at different temperatures

Figure 2 depicts magnetization curves measured at RT. The values of the specific saturation magnetization per unit mass σs and the volume fraction of α′-martensite fα determined using Eq. [1] are given in Table II. The amount of DIM determined by the magnetization measurements was confirmed by the image analysis of the etched specimen microstructure. An exemplary result shown in Figure 3 refers to sample B rolled at RT, for which the amount of α′-martensite was determined at 0.64 ± 0.01. Grain boundaries and typical morphology of the strain-induced martensite can be seen in the microstructure examined both by SEM and OM (Figures 3(a) and (b), respectively).
Fig. 2

Magnetization curves for samples A, B, and C deformed by tension at different temperatures

Fig. 3

Microstructure of sample B rolled at RT: (a) SEM of a slightly etched specimen and (b) DIM revealing etching OM. The rolling direction is parallel to the scale bar

3.2 Isochronal Annealing

Figure 4 presents the results of the microhardness and DB measurements for isochronal annealing for samples A, B, and C. The Vickers microhardness values as a function of the annealing temperature are shown in Figure 4(a). Sample A, with the highest volume fraction of α′ martensite, shows the highest initial value of microhardness, 481 ± 17 HV. The microhardness value of sample B is slightly lower, 462 ± 14 HV. Sample C, with the lowest volume fraction of α′-martensite, has the lowest value, 421 ± 30 HV. Although the differences in the initial microhardness values are small, the dependence on the α′-martensite amount is clear: the higher the α′-martensite volume fraction, the higher the microhardness. The microhardness does not change significantly up to an annealing temperature of 425 °C. For samples A and B at a higher amount of α′-martensite, a slight increase is observed at a temperature of 475 °C. The softening of the material for samples A and B is seen for annealing temperatures higher than 475 °C. For sample C, the microhardness shows a decrease starting above 700 °C, where the values for all three samples are close to each other. The inserts show optical micrographs of the microstructure of sample C: rolled and after annealing at 550 °C and 750 °C, respectively. After the entire annealing cycle, the values of the microhardness are higher than those of the sample after solution annealing at 1100 °C and cooling in the air at approximately 190 ± 10 HV.
Fig. 4

Effect of 1-h isochronal annealing on (a) the microhardness and the values of the (b) S- and (c) Wr-annihilation line shape parameters, respectively, for samples A, B, and C rolled at different temperatures; fα is the initial fraction of α′-martensite. The inserts show optical micrographs of the microstructure in the longitudinal sections of sample C rolled and after annealing at 550 °C and 750 °C. The rolling direction is parallel to the scale bar

Figures 4(b) and (c) show the S- and Wr-parameter values as a function of the annealing temperature. Initially, for the as-deformed samples, a higher deformation corresponds to a higher S-parameter value. The S-parameter decreases only slightly with a temperature increase up to 175 °C. The most pronounced decrease is clearly visible for a temperature in the range from 200 °C to 425 °C for sample A and from 200 °C to 450 °C for samples B and C. This decrease indicates a disappearance of positron trapping defects; however, it is not accompanied by a reduction of microhardness according to Figure 4(a). This annealing temperature range is the first recovery stage consisting of the diffusion and sinking of vacancies generated during deformation.[17, 18, 19] At 475 °C, the S parameter increases rapidly for all three samples, is maintained at the same level in the temperature range from 475 °C to 600 °C, and then decreases until 825 °C. As mentioned previously, the initial values of the S parameter are ordered by the degree of deformation, and from a temperature of 450 °C, their order is reversed, which is congruous with the increasing α′- martensite volume fraction (Table II). In spite of the significant differences in the α′- martensite volume fraction in the as-deformed samples, the differences in the S-parameter values in all three samples in the temperature range from 475 °C to 600 °C are small. The Wr-parameter dependences shown in Figure 4(c) are almost mirror images of the S-parameter dependences with respect to the temperature axis up to 425 °C and then above 600 °C. In the intermediate temperature region, there is a distinct dependence of the Wr-parameter maximal values at 425 °C and 450 °C on the α′-martensite fraction. The following decrease in the Wr parameter does not reflect the S-parameter dependence strictly.

Figure 5 depicts the S-Wr plots for the measured samples. The plots show a linear relationship for sample C within the entire temperature range. For samples A and B, the linear relationship is observed from RT to 350 °C, where a decrease in the S parameter in Figure 4(b) is accompanied by an increase in the Wr parameter in Figure 4(c). A linear relationship for the Wr-S function indicates that the main type of positron trapping defects does not change, but only their concentration does. The slopes of the lines − 16.6 ± 0.7 and − 16.4 ± 0.6 for samples A and B, respectively, are the same within the experimental error. However, for the temperature range between 400 °C and 600 °C, the points significantly diverge from the linear slope. This tendency starts at a relatively low annealing temperature, i.e., 375 °C, when the S parameter still decreases. This behavior is most pronounced for sample A with the highest α′-martensite volume fraction (Figure 5(a)). The diverging points form a loop and return to a straight line. The loop is marked by line segments connecting the points for the increasing annealing temperatures in Figure 5. For sample C, divergence from a straight line is relatively small. The slope of the straight line fitted to all the points for sample C is equal to –15.3 ± 0.5 and differs slightly from those for samples A and B, but the difference is still within the experimental error and can be caused by taking into account the points in the temperature region of the loop.
Fig. 5

S-Wr plots for the isochronal annealing of the samples rolled at different temperatures. (a), (b), and (c) The experimental points for samples A, B, and C, respectively. The arrows indicate the succession of the experimental points. Some points are labeled by the annealing temperature values; fα is the initial fraction of α′-martensite

The results of the PL measurements for all three samples after annealing at selected temperatures are presented in Table III. Only one PL was resolved in all the spectra, and it can be treated as the mean PL, as discussed in Reference 10. It can be seen that the changes of the PL for samples A and B reflect the dependence of the S parameter on the annealing temperature, i.e., a decrease at 350 °C and then an increase at 500 °C followed by another decrease at 800 °C. However, for sample C, with the lowest amount of α′-martensite, the PL does not increase after annealing at 500 °C.
Table III

PL Values in Picoseconds Measured for As-Deformed Samples and after Annealing at Selected Temperatures; the Accuracy of the Obtained Values is ± 1 ps


A (fα′ = 0.91)

B (fα′= 0.64)

C (fα′ = 0.09)

As deformed




350 °C




500 °C




800 °C




3.3 Isothermal Annealing

The XRD patterns for the samples after annealing at 550 °C for 670 ks are shown in Figure 6. Peaks 110α, 200α, and 211α denote that even such long annealing did not cause a total α′ martensite reversion. Other visible peaks are also present, which can be caused by carbides, mainly M23C6. Carbide precipitation at these temperatures is typical of the investigated SS.[20]
Fig. 6

XRD patterns for the rolled samples A, B, and C after annealing at 550 °C for 670 ks

The results of the microhardness and DB measurements for samples isothermally annealed at 650 °C and 550 °C are depicted in Figure 7. Annealing at 650 °C for 51 ks decreases the microhardness to about 200 HV, while annealing at 550 °C for 670 ks results in values of 300 to 380 HV. For sample C annealed at 650 °C, the S parameter decreases in the entire time range. For samples A and B, the S parameter slightly increases after annealing at 1.8 ks and then decreases. This behavior causes a change in the sequence of the S-parameter values, as it takes place during isochronal annealing at temperatures higher than 500 °C. After annealing for 51 ks at 650 °C, the S-parameter values are close to that obtained for the solution-treated sample annealed additionally for 3.6 ks at 700 °C and cooled slowly with the furnace. The latter treatment allows us to remove thermally generated vacancies that remained in the sample as a result of relatively fast cooling in air from temperature 1100 °C. Then the annealing at 650 °C for 51 ks removes defects where positrons could potentially localize in all three samples. The Wr-parameter dependences on the annealing temperature reflect those of the S parameter.
Fig. 7

Effect of the annealing time at 650 °C and 550 °C on (a) the microhardness and the values of the (b) S and (c) Wr parameters and, respectively, for samples A, B, and C rolled at different temperatures; fα is the initial fraction of α′-martensite

For annealing at 550 °C, there is a decrease in the S-parameter values after the first 1.8 ks. Similarly to annealing at 650 °C, the S-parameter values change their sequence in comparison to the initial one. Then, the S parameter slightly increases for all the samples, and after a slight decrease, it remains constant, not reaching the final value obtained for the samples annealed at 650 °C. Even a long annealing at 550 °C does not remove sites where positrons are localized.

For the samples annealed at 650 °C, a straight line can be fitted to all experimental points in the S-Wr plot (Figure 8(a)). The slope of the line equal to − 17.1 ± 0.5 is similar to those obtained for isochronal annealing. For annealing at 550 °C, the straight line in the S-Wr plot fitted for sample C has a slope equal to − 16.5 ± 0.9 (Figure 8(d)). The experimental points for samples A and B diverge from the straight line, as it takes place for isochronal annealing.
Fig. 8

S-Wr plots for the isothermal annealing of samples A, B, and C rolled at different temperatures; fα is the initial fraction of α′-martensite. (a) The plot for annealing at 650 °C contains the experimental points for all three samples. The symbols for the individual samples are the same as when annealed at 550 °C. The dashed straight line is fitted to all the points. (b), (c), and (d) The experimental points for samples A, B, and C, respectively, isothermally annealed at 550 °C. The dashed straight line is fitted to the data for sample C. The arrows indicate the succession of the experimental points. Some points are labeled by the annealing time values

4 Discussion

Annealing of cold-worked austenitic SS may involve complex microstructural processes such as martensite reversion, precipitation, recovery, recrystallization, and grain growth. Bearing this in mind, the obtained results can be explained as follows.

4.1 Isochronal Annealing

Figure 4(a) indicates a softening of the material caused by α′-martensite reversion for temperatures above 475 °C in samples A and B. For sample C, with a lower amount of α′-martensite, a decrease in the microhardness above 700 °C follows the values for samples A and B. It is caused by recrystallization.[21] Optical micrographs in the Figure 4 inserts show that after annealing at 750 °C, sample C was completely recrystallized, while after annealing at 550 °C, its microstructure did not differ significantly from the initial microstructure. Cios et al. showed that the completely recrystallized material does not contain DIM.[22]

An increase in the S parameter at 475 °C coincides with the small maximum of microhardness for samples A and B with a higher amount of α′-martensite. The increase in microhardness may be caused by precipitation of carbides. Carbide precipitation in austenitic SS at approximately 500 °C is known to be responsible for steel’s sensitization to intergranular corrosion. However, at temperatures lower than 450 °C, the rate of Cr diffusion is slow and the Cr content of M23C6 carbides decreases with the decreasing sensitization temperature. The carbides that precipitate during low-temperature aging have a composition that approaches the matrix composition.[23]

When considering an increase in the microhardness at 475 °C for samples A and B, one can speculate that it may have been caused by an increase in the volume fraction of α′-martensite. The anomalous evolution of deformation-induced α′-martensite, i.e., an increase in its volume fraction was reported for isothermal annealing, however, performed at slightly lower temperatures, i.e., from 300 °C to 400 °C.[24,25] One of the explanations for this phenomenon also takes into account the precipitation of carbides. This leads to composition inhomogeneities that locally increase MS in the regions depleted of alloying elements, causing the formation of more martensite on cooling.[24]

Precipitation of carbides was proposed as an explanation of an increase and subsequent decrease in the S parameter or mean PL values with increasing annealing temperature.[17] The effect was reported for Ti-doped austenitic SS.[26,27] This behavior was attributed to trapping of positrons in misfit dislocations at precipitate-matrix interfaces, more so as TiC precipitates inside grains. The increasing number of precipitates causes an increase in the S parameter or mean PL value. The growth and coarsening of precipitates reduce the number density of precipitates and decrease the S parameter as well as the mean positron lifetime. Similar behavior was also observed for the annealing of electron-irradiated, deformed, or sensitized Type 304 austenitic SS by Yabuuchi et al. and was attributed to the formation of metal carbide precipitates M23C6.[19] In the case of not-deformed samples, the increase in the S parameter was explained by the Kirkendall effect rather than by positron trapping in the misfit dislocations at the M23C6 precipitate interface. This explanation is based on the fact that if grains are large, nearly all positrons annihilate inside the grains. The probability of positrons being trapped in the misfit dislocations at the precipitate interface at grain boundaries should be low. Additionally, migration of Cr atoms to grain boundaries results in a flow of vacancies into the grains. The quenching of samples after annealing should retain the vacancies as positron trapping sites. However, this effect cannot be used for the explanation of the results presented in this article because the samples were slowly cooled after each annealing step, which should have caused the removal of vacancies. Vacancy defects inside precipitates were also suggested as possible candidates for positron trapping sites.[11]

It is known that cold working accelerates the precipitation of both carbides and intermetallic phases in SS.[27,29] When deformation-induced α′-martensite is present, the interphase boundaries arising as a result of its reversion are the sites of M23C6 nucleation and growth.[28] In our case, it should be noted that the higher the α′-martensite volume fraction, the higher the values of the S parameter in the temperature range from 475 °C to 600 °C, in spite of the lower deformation degree (Figure 4 (b)). This behavior indicates the influence of the initial α′-martensite volume fraction on the formation of positron trapping defects. The reversion of α′-martensite provides sites for metal carbide nucleation, whereas volume excess resulting from the bcc/fcc change may contribute to an excess of vacancy-type defects at the interphase boundaries.

The influence of the initial α′-martensite fraction is visible for the Wr parameter in the region of its maximum (Figure 4(c)). Moreover, the S-Wr plot indicates changes in the chemical surrounding of the sites of positron annihilation, which are more pronounced for samples A and B with a higher α′-martensite fraction. The divergence of the experimental points from the straight line in the S-Wr plot already starts at 375 °C (Figure 5(a)). The changes continue (the experimental points form a loop), and this behavior is reflected in an increase and subsequent decrease in the concentration of defects with a chemical surrounding different from that introduced by plastic deformation. Moreover, this chemical surrounding also evolves with altering carbide composition, i.e., Fe and Cr content of M23C6 carbides precipitating during annealing at increasingly higher temperatures. The decrease in the Wr-parameter value for temperatures from 425 °C to 625 °C may be caused by the influence of annihilation with core electrons of carbon since the coincidence DB spectrum for graphite has much lower values for core electron annihilation energies than those for steel, as observed by Rajaraman et al.[27]

Our previous studies of martensite reversion in 1.4307 SS deformed in uniaxial tension revealed the presence of clusters of six to nine vacancies for the sample deformed at LN temperature to 5 pct elongation with the α′-martensite volume fraction of 0.25. For the sample deformed to 32 pct elongation with the α′-martensite volume fraction of 0.19, the vacancy clusters, if present, were smaller and had a lower concentration.[10] The PL spectra measured for the rolled samples after annealing at 500 °C, in the region of the higher S-parameter values, i.e., a step in Figure 4(b), exhibit only one component, which can be treated as the mean positron lifetime, i.e., 139, 136, and 130 ps for samples A, B, and C, respectively. If the differences in the deformation mode can be neglected, the results for the tension-deformed samples and the lack of evidence of vacancy clusters for the rolled samples seem to indicate that the conditions favorable for vacancy cluster formation are the following: a relatively high initial α′-martensite volume fraction and a low degree of deformation.

4.2 Isothermal Annealing

The linear relationship of the experimental points in Figure 8(a) for all three samples annealed at 650 °C suggests no noticeable change in the type of positron trapping sites. However, there are differences between the samples in the S- and Wr-parameter dependences due to an α′-martensite volume fraction. For samples with higher α′-martensite volume fractions, the higher value of the S parameter for an annealing time from 1.8 to 25.8 ks indicates higher concentrations of defects (Figure 7(b)). These differences disappear after annealing for 51 ks. A similar influence of the α′-martensite fraction can be seen for samples annealed at 550 °C, and it does not change when annealing time is increased. A closer inspection of the S-Wr plots for samples isochronally annealed at 550 °C reveals that the experimental points for samples B and C diverge from the straight line fitted for sample A. Then they converge for the annealing time of 43.1 ks, for which there is a local maximum of the S-parameter value. This effect can be explained by the nucleation and then coarsening of carbide precipitates, the presence of which was confirmed by XRD patterns (Figure 6). For longer annealing times, the points diverge again from the straight line. This behavior, which starts at 87.6 ks, indicates a subsequent alteration of positron trapping sites, which can be connected to the early stages of intermetallic phase precipitation.

5 Conclusions

The PAS application to the study of the annealing behavior of rolled metastable SS 1.4307 with different amounts of deformation-induced α′-martensite yields valuable information. The main results can be summarized as follows.
  1. 1.

    The first stage of recovery indicated by a decrease in the S parameter for isochronal annealing in the temperature range between 200 °C and 425 °C results in annealing of vacancies induced by plastic deformation.

  2. 2.

    The reverse transformation of α′-martensite in the temperature range between 475 °C and 600 °C indicated by a decrease in microhardness is accompanied by the generation of new positron trapping defects with a different chemical surrounding from those induced initially by rolling.

  3. 3.

    The initial α′-martensite volume fraction influences the formation of these defects.

  4. 4.

    The various chemical surroundings of the positron trapping defects indicate that they are misfit dislocations at the interface of metal carbide precipitates nucleating at defects generated by α′-martensite reversion.



  1. 1.

    Wilson Hardness and TUKON are a registered trademarks of Illinois Tool Works Inc. (ITW), Glenview, IL.


  1. 1.
    R. Fawley, M.A. Quader, and R.A. Dodd: Trans. TMS-AIME, 1968, vol. 242, pp. 771–76.Google Scholar
  2. 2.
    R.E. Schramm and R.P. Reed: Metall. Trans. A, 1975, vol. 6A, pp. 1345–51.CrossRefGoogle Scholar
  3. 3.
    P.L. Mangonon, Jr. and G. Thomas: Metall. Trans., 1970, vol. 1, pp. 1577–86.CrossRefGoogle Scholar
  4. 4.
    V. Seetharaman and R. Krishnan: J. Mater. Sci., 1981, vol. 16, pp. 523–30.CrossRefGoogle Scholar
  5. 5.
    J. Singh: J. Mater. Sci., 1985, vol. 20, pp. 3157–66.CrossRefGoogle Scholar
  6. 6.
    A.F. Padilha, R.L. Plaut, and P.R. Rios: ISIJ Int., 2003, vol. 43, pp. 135–43.CrossRefGoogle Scholar
  7. 7.
    R Krause-Rehberg and HS Leipner: Solid-State Sciences, Springer, Berlin 1999, vol. 127.Google Scholar
  8. 8.
    E. Dryzek, M. Sarnek, and K. Siemek: Nukleonika, 2013, vol. 58, pp. 213–17.Google Scholar
  9. 9.
    E. Dryzek and M. Sarnek: Acta Phys. Polon. A, 2014, vol. 125, pp. 710–13.CrossRefGoogle Scholar
  10. 10.
    E. Dryzek, M. Sarnek, and M. Wróbel: J. Mater. Sci., 2014, vol. 49, pp. 8449–58.CrossRefGoogle Scholar
  11. 11.
    S HariBabu, G Amarendra, R Rajaraman, CS Sundar: (2013) J. Phys.: Conf. Ser. 443:012010.Google Scholar
  12. 12.
    A.S. Lima and A.M. Nascimento: J. Mater. Sci., 2005, vol. 40, pp. 139–44.CrossRefGoogle Scholar
  13. 13.
    M. Shirdel, H. Mirzadeh, and M.H. Parsa: Mater. Sci. Eng. A, 2015, vol. 624, pp. 256–60.CrossRefGoogle Scholar
  14. 14.
    ISO 4545:1:2017: “Metallic Materials –Knoop Hardness Test – Part 1: Test Method.”Google Scholar
  15. 15.
  16. 16.
    J. Kansy: Nucl. Instr. Meth. A, 1996, vol. 374, pp. 235–44.CrossRefGoogle Scholar
  17. 17.
    J. Dryzek, C. Wesseling, E. Dryzek, and B. Cleff: Mater. Lett., 1994, vol. 21, pp. 209–14.CrossRefGoogle Scholar
  18. 18.
    U. Holzwarth, A. Barbieri, S. Hansen-Ilzhöfer, P. Schaaff, and M. Haaks: Appl. Phys. A, 2001, vol. 73, pp. 467–75.CrossRefGoogle Scholar
  19. 19.
    A. Yabuuchi, M. Maekawa, and A. Kawasuso: J. Nucl. Mater., 2011, vol. 419, pp. 9–14.CrossRefGoogle Scholar
  20. 20.
    M.F. McGuire: Stainless Steels for Design Engineers, ASM International, Materials Park, OH, 2008.Google Scholar
  21. 21.
    L.F.M. Martins, R.L. Plaut, and A.F. Padilha: ISIJ Int., 1998, vol. 38, pp. 572–79.CrossRefGoogle Scholar
  22. 22.
    G. Cios, T. Tokarski, A. Żywczak, R. Dziurka, M. Stępień, Ł. Gondek, M. Marciszko, B. Pawłowski, K. Wieczerzak, and P. Bała: Metall. Mater. Trans. A, 2018, vol. 48A, pp. 4999–5008.Google Scholar
  23. 23.
    C.G. Schmidt, R.D. Caligiuri, L.E. Eiselstein, S.S. Wing, and D. Cubicciotti: Metall. Trans. A, 1987, vol. 18A, pp. 1483–93.CrossRefGoogle Scholar
  24. 24.
    F Gauzzi, R Montanari, G Principi, ME Tata (2006) Mater. Sci. Eng. A, 438–440:202–06.CrossRefGoogle Scholar
  25. 25.
    S.S.M. Tavares, D. Fruchart, and S. Miraglia: J. Alloys Compd., 2000, vol. 307, pp. 311–17.CrossRefGoogle Scholar
  26. 26.
    J Arunkumar, S Abhaya, R Rajaraman, G Amarendra, KGM Nair, CS Sundar, R Baldev(2009) J. Nucl. Mater. 384:245–48.CrossRefGoogle Scholar
  27. 27.
    R. Rajaraman, G. Amarendra, and C.S. Sundar: Phys. Status Solidi C, 2009, vol. 6, pp. 2285–90.CrossRefGoogle Scholar
  28. 28.
    E.A. Trillo, R. Beltran, J.G. Maldonado, R.J. Romero, L.E. Murr, W.W. Fisher, and A.H. Advani: Mater. Charact., 1995 vol. 35, pp. 99–112.CrossRefGoogle Scholar
  29. 29.
    Y.J. Oh and J.H. Hong: J. Nucl. Mater., 2000, vol. 278, pp. 242–50.CrossRefGoogle Scholar

Copyright information

© The Author(s) 2018

Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (, which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Authors and Affiliations

  1. 1.Institute of Nuclear PhysicsPolish Academy of SciencesKrakówPoland
  2. 2.Cracow University of EconomicsKrakówPoland
  3. 3.AGH University of Science and TechnologyKrakówPoland

Personalised recommendations