Formation of Accumulated Misorientation During Directional Solidification of Ni-Based Single-Crystal Superalloys

  • Songsong Hu
  • Lin LiuEmail author
  • Wenchao YangEmail author
  • Dejian Sun
  • Miao Huo
  • Taiwen Huang
  • Jun Zhang
  • Haijun Su
  • Hengzhi Fu
Communication
  • 47 Downloads

Abstract

The formation of accumulated misorientation during directional solidification of Ni-based single-crystal superalloys with 〈001〉 direction deviating from cylinder axis by 20 deg was investigated at different withdrawal rates. The accumulated misorientation increased from the converging side of the dendrite with respect to the mold wall to the diverging side in the radial direction. With increased solidification distance, the accumulated misorientation in the solidification direction reached 7.6 deg, and was not significantly affected by withdrawal rates.

Notes

This work was supported by the National Natural Science Foundation of China (Grant Numbers 51331005, 51771148, 51631008, 51690163, 51501152, 51501151), the National Key Research and Development Program (Grant Number 2016YFB0701400), and Excellent Doctorate Cultivating Foundation of Northwestern Polytechnical University.

References

  1. 1.
    [1] E. Wu, G. Sun, B. Chen, T. Pirling, D.J. Hughes, S. Wang and J. Zhang: Acta Mater., 2013, vol. 61, pp. 2308-2319.CrossRefGoogle Scholar
  2. 2.
    [2] F. Ram, Z. Li, S. Zaeffere, S.M.H. Haghighat, Z. Zhu, D. Raabe and R.C. Reed: Acta Mater., 2016, vol. 109, pp. 151-161.CrossRefGoogle Scholar
  3. 3.
    [3] W. Bogdanowicz, R. Albrecht, J. Sieniawski and K. Kubiak: J. Cryst. Growth, 2014, vol. 401, pp. 418-422.CrossRefGoogle Scholar
  4. 4.
    [4] F. Wang, D.X. Ma and A.B. Polaczek: Metall. Mater. Trans. A, 2017, vol. 48A, pp. 5442-5448.CrossRefGoogle Scholar
  5. 5.
    [5] F. Wang, Z. Wu, C. Huang, D. Ma, J. Jakumeit and A.B. Polaczek: Metall. Mater. Trans. A, 2017, vol. 48A, pp. 5924-5939.CrossRefGoogle Scholar
  6. 6.
    [6] M. Huo, L. Liu, W. C. Yang, D. J. Sun, S. S. Hu, J. Zhang and H. Z. Fu: Adv. Eng. Mater., 2018, vol. 20, pp. 1701189-7.Google Scholar
  7. 7.
    [7] C.L. Brundidge, J.D. Miller and T.M. Pollock: Metall. Mater. Trans. A, 2011, vol. 42, pp. 2723-2732.CrossRefGoogle Scholar
  8. 8.
    [8] D.J. Sun, L. Liu, T.W. Huang, W.C. Yang, Y.F. Li, Q.Z. Yue, J. Zhang and H.Z. Fu: Prog. Nat. Sci: Mater., 2018, vol. 28, pp. 489-495.CrossRefGoogle Scholar
  9. 9.
    [9] D. Bellet, P. Bastie and J. Baruchel: J. Phys. D: Appl. Phys., 1993, vol. 26, pp. 50-52.CrossRefGoogle Scholar
  10. 10.
    [10] M. Newell, K. Devendra, P.A. Jennings and N. D’Souza: Mater. Sci. Eng. A, 2005, vol. 412, pp. 307-315.CrossRefGoogle Scholar
  11. 11.
    [11] J.W. Aveson, P.A. Tennant, B.J. Foss, B.A. Shollock, H.J. Stone and N. D’Souza: Acta Mater., 2013, vol. 61, pp. 5162-5171.CrossRefGoogle Scholar
  12. 12.
    [12] J.W. Aveson, G. Reinhart, H. Nguyen-Thi, N. Mangelinck-Noël, N. D’Souza and H.J. Stone: MATEC Web Conf., 2014, vol. 14, pp. 05003.CrossRefGoogle Scholar
  13. 13.
    [13] C. Ai, J. Zhou, H. Zhang, Y. Pei, S. Li and S. Gong: J. Alloy Compd., 2015, vol. 637, pp. 77-83.CrossRefGoogle Scholar
  14. 14.
    [14] J.D. Miller, L. Yuan, P.D. Lee, and T.M. Pollock: Acta Mater., 2014, vol. 69, pp 47-59.CrossRefGoogle Scholar
  15. 15.
    [15] T. Takaki and H. Kashima: J. Cryst. Growth, 2011, vol. 337, pp. 97-101.CrossRefGoogle Scholar

Copyright information

© The Minerals, Metals & Materials Society and ASM International 2019

Authors and Affiliations

  • Songsong Hu
    • 1
  • Lin Liu
    • 1
    Email author
  • Wenchao Yang
    • 1
    Email author
  • Dejian Sun
    • 1
  • Miao Huo
    • 1
  • Taiwen Huang
    • 1
  • Jun Zhang
    • 1
  • Haijun Su
    • 1
  • Hengzhi Fu
    • 1
  1. 1.State Key Laboratory of Solidification ProcessingNorthwestern Polytechnical UniversityXi’anChina

Personalised recommendations