Experimental and Numerical Analysis of Restrained Early Age Cracking based on Electrical Resistivity Using Eccentric Sample

  • Maha A. Abusogi
  • Xiaosheng Wei (魏小胜)Email author
Cementitious Materials
  • 7 Downloads

Abstract

Crack potential and hydration processes of the cement pastes were monitored using an up-to-date eccentric steel cracking frame (ESCF), associated with the non-contact electrical resistivity apparatus, independently. The objective of employing the ESCF is to give a new method determining cracks of concrete at early age. The findings indicate that the lowest water-cement ratio paste reveals highest resistivity values, compasses an earlier inflection point and obtained higher stress. The eccentric restrained cracking test exhibited that lower water-cement ratio paste cracked at the earliest time, accordingly confirms cracking tendency is the highest. Tensile strength test and stresses utilizing ABAQUS simulation was performed. The crack initiation ages obtained are consistent with the experimental program results, which indicates that ABAQUS numerical analysis can well be utilized to predict the crack tendency of cement.

Key words

eccentric steel cracking frame electrical resistivity cracking time hydration numerical analysis 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. [1]
    ACI207.2R–07. Report on Thermal and Volume Change Effects on Cracking of Mass Concrete[R]. 2007Google Scholar
  2. [2]
    Dong W, Zhou X, Wu Z. A Fracture Mechanics–based Method for Prediction of Cracking of Circular and Elliptical Concrete Rings under Restrained Shrinkage[J]. J. Eng. F. Mech., 2014, 131: 687–701Google Scholar
  3. [3]
    Bentur A, Kovler K. Evaluation of Early Age Cracking Characteristics in Cementitious Systems[J]. J. Mat.Struct.,2003, 36(3): 183–190Google Scholar
  4. [4]
    Bawa SM, Wei X, Wang L. The Relationship between Electrical Resistivity of Cement Paste and Its Restrained Shrinkage Crack with the Aid of Novel Apparatus and ANSYS Simulation[J]. KSCE J. C.Eng., 2017, 21(1): 339–345CrossRefGoogle Scholar
  5. [5]
    Moon J–H, Rajabipour F, Pease B, et al. Quantifying the Influence of Specimen Geometry on the Results of the Restrained Ring Test[J]. J. ASTM. Int., 2006, 3(8): 1–14Google Scholar
  6. [6]
    Weiss WJ, Yang W, Shah SP. Influence of Specimen Size/Geometry on Shrinkage Cracking of Rings[J]. J. EngMech., 2000, 126(1): 93–101Google Scholar
  7. [7]
    Weiss WJ, Shah SP. Restrained Shrinkage Cracking: The Role of Shrinkage Reducing Admixtures and Specimen Geometry[J]. J. Mat. Struct., 2002, 35(2): 85–91CrossRefGoogle Scholar
  8. [8]
    Hossain AB, Weiss J. Assessing Residual Stress Development and Stress Relaxation in Restrained Concrete Ring Specimens[J]. J. C.Con. Comp., 2004, 26(5): 531–540CrossRefGoogle Scholar
  9. [9]
    Hossain AB, Weiss J. The role of Specimen Geometry and Boundary Conditions on Stress Development and Cracking in the Restrained Ring Test[J]. J. C.Con.Res., 2006, 36(1): 189–199CrossRefGoogle Scholar
  10. [10]
    Moon JH, Weiss J. Estimating Residual Stress in the Restrained Ring Test under Circumferential Drying[J]. J. C. Conc.Comp., 2006, 28(5): 486–496CrossRefGoogle Scholar
  11. [11]
    Passuello A, Moriconi G, Shah SP. Cracking Behavior of Concrete with Shrinkage Reducing Admixtures and PVA Fibers[J]. J. C. Conc. Comp., 2009, 31(10): 699–704CrossRefGoogle Scholar
  12. [12]
    He Z, Zhou X, Li Z. New Experimental Method for Studying Early–age Cracking of Cement–based Materials[J]. Materials J., 2004, 101(1): 50–56Google Scholar
  13. [13]
    He Z, Li Z. Influence of Alkali on Restrained Shrinkage Behavior of Cement–based Materials[J]. J. Cement and concrete research, 2005, 35(3): 457–463CrossRefGoogle Scholar
  14. [14]
    He Z, Li Z, Chen M, et al. Properties of Shrinkage–reducing Admixture–modified Pastes and Mortar[J]. J. Mat. Struct., 2006, 9(4): 445–453Google Scholar
  15. [15]
    Abusogi MA, Xiaosheng W, lei F. Using Eccentrically Sample to Find the Relationship between Resistivity and Cracking Time in Cement Paste Vides Mechanical Strength and Electrical Resistivity[J]. A. J. Civil Eng. Arch., 2017, 5(4): 154–159Google Scholar
  16. [16]
    Wei X, Xiao L, Li Z. Electrical Measurement to Assess Hydration Process and the Porosity Formation[J]. J. WUT–Mat. Sc.Edition, 2008, 23(5): 761–766Google Scholar
  17. [17]
    Beaudoin J, Gu P, Myers R. Flexural Strength of Cement Paste Composites Containing Micron and Sub–micron Nickel Particulates[J]. J. C. Con. Res., 1997, 27(1): 23–27CrossRefGoogle Scholar
  18. [18]
    Collins F, Sanjayan J. Cracking Tendency of Alkali–activated Slag Concrete Subjected to Restrained Shrinkage[J]. J. Cement and Concrete Research, 2000, 30(5): 791–798CrossRefGoogle Scholar
  19. [19]
    Kim K–H, Jeon S–E, Kim J–K, et al. An Experimental Study on Thermal Conductivity of Concrete[J]. J. Cement and Concrete Research, 2003, 33(3): 363–371CrossRefGoogle Scholar
  20. [20]
    PZhi, J Xianyu, J Nanguo. Theoretical Modeling of Concrete Moisture Diffusion Surface Factor, Earth and Space 2010: Engineering, Science [J]. J. Const, Op in C Environ, 2010: 3 610–3 616Google Scholar
  21. [21]
    Kang S–T, Kim J–S, Lee Y, et al. Moisture Diffusivity of Early Age Concrete Considering Temperature and Porosity[J]. KSCE J of C. Eng., 2012, 16(1): 179–188CrossRefGoogle Scholar
  22. [22]
    Zhang J, Hou D, Gao Y, et al. Determination of Moisture Diffusion Coefficient of Concrete at Early Age from Interior Humidity Measurements [J]. J. D. Tech., 2011, 29(6): 689–696CrossRefGoogle Scholar
  23. [23]
    N da Amorim Coelho, LJ Pedroso, JH da Silva Rêgo, et al. Use of ANSYS for Thermal Analysis in Mass Concrete[J]. J. of C. Eng. and Arch., 2014, 8(7)Google Scholar
  24. [24]
    Choktaweekarn P, Tangtermsirikul S. A Model for Predicting Coefficient of Thermal Expansion of Cementitious Paste[J]. J. Sci. Asia., 2009, 35(1): 57–63CrossRefGoogle Scholar
  25. [25]
    Yuan Y, Wan Z. Prediction of Cracking Within Early–age Concrete Due to Thermal, Drying and Creep Behavior[J]. J. C. C. R, 2002, 32(7): 1 053–1 059Google Scholar
  26. [26]
    Bazant ZP. Mathematical Modeling of Creep and Shrinkage of Concrete[ M]. Wiley, 1988Google Scholar
  27. [27]
    Wei X, Li Z. Early hy, Dration Process of Portland Cement Paste by Electrical Measurement[J]. J. Mat. C.Eng., 2006, 18(1): 99–105CrossRefGoogle Scholar
  28. [28]
    Liao Y, Wei X, Li G. Early Hydration of Calcium Sulfoaluminate Cement Through Electrical Resistivity Measurement and Microstructure Investigations[J]. J. Cons. Bldg. Mat.,2011,25(4): 1 572–1 579Google Scholar
  29. [29]
    Kovler K, Sikuler J, Bentur A. Restrained Shrinkage Tests of Fibre–reinforced Concrete Ring Specimens: Effect of Core Thermal Expansion [J]. J. Mat. Struct., 1993, 26(4):231–237Google Scholar

Copyright information

© Wuhan University of Technology and Springer-Verlag GmbH Germany, part of Springer Nature 2018

Authors and Affiliations

  1. 1.School of Civil Engineering and MechanicsHuazhong University of Science and TechnologyWuhanChina

Personalised recommendations