Water-suspended graphene as electrolyte additive in zinc-air alkaline battery system
- 102 Downloads
Zinc-air (Zn-air) batteries possess high-energy density due to surplus air involved in reduction reaction at air cathode and are an important energy source used for automobiles and grid storage. In this study, the scope of improvements in the efficiency of Zn-air batteries are investigated through addition of water-soluble graphene (WSG) as a corrosion inhibitor in 1 M KOH electrolyte. Phase and microstructure analysis for the synthesized WSG shows the formation of few layers of graphene due to the presence of an intense XRD peak of carbon at 26.3° and the flake-like structure confirmed by SEM. The discharge capacity, corrosion behavior, and electrochemical impedance analysis performed on conventional Zn-air battery shows improved performance when tested with WSG as an additive in 1 M KOH electrolyte. Results from short-circuit test show that immersion of WSG in 1 M KOH electrolyte increased the current density from 20.3 to 26.43 mAcm−2. Whereas, galvanostatic discharge measurement reveals that Zn-air battery in WSG added with 1 M KOH electrolyte has a specific discharge capacity of ~ 212.6 mAhg−1 higher than that obtained in 1 M KOH electrolyte (~ 160.4 mAhg−1).Overall, the WSG-based Zn-air battery shows good self-discharge capacity and higher electrochemical activity during discharge holds promise as an electrolyte additive for Zn-air system.
KeywordsZinc-air battery Electrochemical property Graphene Corrosion resistance Discharge
One of the authors, M. Selvam, is thankful to the Department of Science and Technology (DST), New Delhi, for providing the INSPIRE fellowship (IF110749) to carry out this research work.
- 4.Linden D, Reddy TB (2001) Zinc/Air Batteries—Button Configuration. Handbooks of batteries, Chapter 13. McGraw-HillGoogle Scholar
- 10.Lee JS, Kim ST, Cao R, Choi NS, Liu M, Lee KT, Cho J (2011) Metal–air batteries with high energy density: Li–air versus Zn–air. Adv Energy Mater 134:50Google Scholar
- 12.Li Y, Yan Z, Wang Q, Ye H, Li M, Zhu L, Cao X (2018) Ultrathin, highly branched carbon nanotube cluster with outstanding oxygen electrocatalytic performance. Electrochem Acta 282:224–232Google Scholar
- 14.Wang Q, Li Y, Wang K, Zhou J, Zhu L, Gu L, Hu J, Cao X (2017) Mass production of porous biocarbon self-doped by phosphorus and nitrogen for cost-effective zinc-air batteries. Electrochem Acta 257–250Google Scholar
- 15.Othman R, Yahaya AH, Arof AK (2013) Zinc-air cell with KOH-treated agar layer between electrode and electrolyte containing hydroponics gel. J New Mater Electrochem Syst 5(3):177–182Google Scholar
- 23.Liu J, Xue DF (2010) Hollow nanostructured anode materials for Li-ion batteries. Nanoscale Res Lett 1:525–1534Google Scholar
- 31.Lan C-J, Tsung-Shune C, Lin PH, Perng TP (2006) Zn-Al alloy as a new anode-metal of a zinc-air battery. J New Mat Electrochem Syst 9:27–32Google Scholar
- 35.Huang G, Zhao Y, Wang Y, Zhang H, Pan F (2013) Performance of Mg–air battery based on AZ31 alloy sheet with twins. Mater Lett 11:346–349Google Scholar