High-Temperature Strength of Copper-Based Condensed Materials

  • N. P. Rudnitskii
Article
  • 8 Downloads

The temperature dependences of Vickers microhardness, ultimate strength, and offset yield point in the temperature range between 290 and 1070 K were determined for the transversal direction in copper-based composites Cu–Zr–Y–Mo, Cu–Cr, Cu–C, and Cu–W. The materials produced by electron-beam evaporation/condensation are used for the manufacture of current collectors which, when in operation, are subjected to intensive wear and electrical erosion as well as to mechanical loading at elevated temperatures. This production method provides composite materials with a special layered structure, where copper layers are interspersed with dispersed-particle layers of other metals. The paper describes the procedures of Vickers microhardness and tensile testing at high temperatures. A general thermodynamic activation analysis of the derived relationships of hardness and strength has been performed for various copper-based composite systems in the range of (0.2–0.8)Tmelt of copper. A comparative analysis of the obtained values of the activation energy of plastic deformation of copper and copper-based composites as well as the theoretical and experimental data on deformation, internal friction, creep, and self-diffusion processes in copper has revealed that in a wide range of temperatures the activation energy of plastic deformation undergoes a significant change during a transition from one temperature region to another. This is indicative of a successive changeover of effective (governing) thermally activated mechanisms of plastic deformation. It is proved that a heat-induced change in the strength characteristics (hardness, ultimate strength, offset yield point) of the composites studied is controlled by the same plastic deformation mechanisms whose temperature regions coincide.

Keywords

hardness strength characteristics temperature microlayered condensed composites thermodynamic activation analysis 

References

  1. 1.
    N. I. Grechanyuk, R. V. Minakova, and G. E. Kopylova, “The state of the art and potential applications of the technology of high-rate electron beam evaporation and subsequent condensation of metals and nonmetals in vacuum to produce materials for electrical contacts and electrodes,” Poroshk. Metallurg., No. 3/4, 139–150 (2013).Google Scholar
  2. 2.
    V. A. Borisenko and V. P. Krashchenko, “Temperature dependences of hardness of group IB metals,” Acta Metall., 25, No. 3, 251–256 (1977).CrossRefGoogle Scholar
  3. 3.
    V. A. Borisenko, V. V. Bukhanovskii, N. I. Grechanyuk, et al., “Temperature dependences of static mechanical properties of an MDK-3 laminated composite,” Strength Mater., 37, No. 4, 416–421 (2005).CrossRefGoogle Scholar
  4. 4.
    V. V. Bukhanovs’kyi, M. P. Rudnyts’kyi, V. V. Kharchenko, and I. Mamuzic, “Relationship between hardness and strength characteristics of Cu–Cr microlayer composite material at elevated temperatures,” Strength Mater., 42, No. 2, 187–196 (2010).CrossRefGoogle Scholar
  5. 5.
    V. Bukhanovsky, M. Rudnytsky, M. Grechanyuk, et al., “Vapour-phase condenced composite materials based on copper and carbon,” Mater. Technol., 50, No. 4, 523–530 (2016).Google Scholar
  6. 6.
    V. V. Bukhanovs’kyi, M. P. Rudnyts’kyi, V. V. Kharchenko, et al., “Relationship between composition, structure, and mechanical properties of a condensed composite of copper–tungsten system,” Strength Mater., 43, No. 4, 426–437 (2011).CrossRefGoogle Scholar
  7. 7.
    V. P. Krashchenko and V. E. Statsenko, “Effect of temperature and strain rate on basic processes controlling the strength of copper,” Strength Mater., 13, No. 4, 487–492 (1981).CrossRefGoogle Scholar
  8. 8.
    M. M. Aleksyuk, V. A. Borisenko, and V. P. Krashchenko, Mechanical Testing at High Temperatures [in Russian], Naukova Dumka, Kiev (1980).Google Scholar
  9. 9.
    V. O. Borisenko and O. B. Oksametna, DSTU 2434-94. A Method of Determination of High-Temperature Hardness Using a Pyramidal Indenter and Bicylindrical Indenter [in Ukrainian], Effective since January 1, 1995.Google Scholar
  10. 10.
    V. V. Klyuev (Ed.), Test Equipment. Handbook [in Russian], in 2 volumes, Vol. 2, Mashinostroenie, Moscow (1982).Google Scholar
  11. 11.
    ISO 6892:1998(E). Metallic Materials – Tensile Testing at Ambient Temperature (1998).Google Scholar
  12. 12.
    ISO 783:1999(E). Metallic Materials – Tensile Testing at Elevated Temperature (1999).Google Scholar
  13. 13.
    V. A. Borisenko, Hardness and Strength of Refractory Materials at High Temperatures [in Russian], Naukova Dumka, Kiev (1984).Google Scholar
  14. 14.
    M. F. Ashby, “A first report on the deformation mechanism maps,” Acta Metall., 20, No. 7, 887–897 (1972).CrossRefGoogle Scholar
  15. 15.
    M. F. Ashby and H. J. Frost, “The kinetics of inelastic deformation above 0 K,” in: A. S. Argon (Ed.), Constitutive Equations in Plasticity, MIT Press, Cambridge (1975), pp. 117–147.Google Scholar
  16. 16.
    D. Maugis, “Creep, hot hardness and sintering in the adhesion of metals at high temperature,” Wear, 62, No. 2, 349–386 (1980).CrossRefGoogle Scholar
  17. 17.
    V. A. Borisenko and N. P. Rudnitskii, “Hardness of dispersion-hardened copper at temperatures 290–1070 K,” Strength Mater., 35, No. 4, 383–386 (2003).CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  • N. P. Rudnitskii
    • 1
  1. 1.Pisarenko Institute of Problems of StrengthNational Academy of Sciences of UkraineKievUkraine

Personalised recommendations