Study on the Failure Mechanism of the Polymorphic Mixture for Remanufactured Machinery Parts
- 10 Downloads
The polymorphic mixture failure mode for multiple heterogeneity of remanufactured (RM) machinery parts makes it difficult to assess their lifetime. The Weibull distribution failure model of RM parts (substrate, coating layer, bonding surface and sudden failure) is constructed with failure time statistics of the parts in service, the latter is used to characterize the failure patterns of RM parts. In view of the multiple heterogeneity of RM parts, the Kaplan–Meier type decoupling method is used to analyze four sets of failure statistics, and each state of the Weibull failure function of the above parts is solved. It reveals the in-service failure mechanism of polymorphic mixtures for multiple heterogeneity of RM machinery parts. The validity and feasibility of the model are verified by the case study. Research results provide the theoretical basis for the design and preparation of a RM alloy powder and the improvement of RM technology. Moreover, the method for lifetime prediction and failure time evaluation of RM parts is proposed and validated.
Keywordsremanufacturing Weibull distribution failure time uncertainty alloy powder
This research was jointly supported by the Research Project (No. 2016jb08) and Support Program (No. SZXYQNL2017005) of Suzhou University, Key Project of Natural Science Research in Universities of Anhui Province of China (No. KJ2017A438), Chinese Postdoctoral Science Foundation (No. 2017M611574), and Humanities and Social Science Research Project of the Ministry of Education of China (No. 17YJC630082).
- 1.B. S. Xu, Theory and Technology of Equipment Remanufacturing Engineering [in Chinese], National Defense Industrial Press, Beijing (2007).Google Scholar
- 3.C. Liu, M. Liu, and L. Xing, “A research on the uncertainty measure and its application to the journal surface roughness of remanufactured engine crankshaft,” Automot. Eng., 37, No. 3, 341–345 (2015).Google Scholar
- 8.H. D. Wang, Z. Zhang, G. Li, et al., “Investigation of contact fatigue failure mode and mechanism of plasma spraying coating,” Tribology, 32, No. 3, 251–257 (2012).Google Scholar
- 9.F. Li and H. Shen, “Analysis method of reliability in remanufacturing design based on knowledge reusing,” Mach. Tool Hydr., 38, No. 11, 144–146 (2010).Google Scholar
- 10.Y. Shen, S. Song, Y. Wang, and C. Du, “Reliability of welded surfacing layer for remanufacture of vehicle’s drive axle housing,” China Mech. Eng., 24, No. 5, 676–680 (2013).Google Scholar
- 11.H. Cao, S. Tong, H. Chen, and L. Shu, “Analysis of remanufacturing process and residual stress of axis parts based on thermal spraying,” China Mech. Eng., 25, No. 24, 3368–3372 (2014).Google Scholar
- 12.X. L. Lu, H. D. Wang, and B. S. Xu, “Research status of on-line monitoring of remanufacturing parts coatings in service process,” Nondestruct. Test., 35, No. 2, 18–22 (2013).Google Scholar
- 13.T. Zhang, Automobile Product Remanufacturing Model and Its Reliability Analysis [in Chinese], Jilin University (2011).Google Scholar
- 17.C. Liu, Research on the On-Line Quality Control Mechanism of Remanufacturing Assembly Process for Complex Mechanical Products under Uncertainty [in Chinese], Hefei Polytechnic University (2016).Google Scholar
- 19.G. B. Zhang and S. H. Guo, “Reliability evaluation of machining tool center based on competing Weibull model,” Comput. Integr. Manuf. Syst., 21, No. 1, 180–186 (2015).Google Scholar