Refractories and Industrial Ceramics

, Volume 59, Issue 5, pp 478–481 | Cite as

Heat-Resistant Concrete Based on Alumina Cement from Substandard Raw Material

  • R. M. Vorozhbiyan
  • G. N. ShabanovaEmail author
  • A. N. Korogodskaya

Results are provided for development of refractory concrete based on modified alumina cement using chemical industry waste. A quantitative ratio for mixed filler fractions, the effect of production factors on concrete strength, the dependence of its strength properties on form of filler, and solidification conditions are established. It is shown that with respect to physicomechanical and engineering properties the concretes developed is no worse than those existing in the market. With respect to all engineering properties this form of refractory product may be recommended as lining for high-temperature units.


alumina cement refractory concrete water-treatment sludge catalyst support waste 


  1. 1.
    R. M. Vorozhbiyan, G. N. Shabanova, and S. M. Korogodskaya, “Alumina cements based on CaO–NiO–Al2O3,” Novye Ogneupory Tekhn. Keram., No. 11/12, 11 – 14 (2012).Google Scholar
  2. 2.
    R. Vorozhbiian, H. Shabanova, T. Ryshchenko, “Alumina cement on chemical industry wastes,” 19 International Baustofftagung, 16 – 18 September, 2015, Tagungsbericht, Band 2, Weimar, Bundesrepublik, Deutschland (2015).Google Scholar
  3. 3.
    M. T. Mel’nik and N. Sh. Shapovalova, Refractory Cements [in Russian], Vysshaya Shkola, Kiev (1984).Google Scholar
  4. 4.
    T. V. Kuznetsova and I. Talaber, Alumina Cement [in Russian] Stroiizdat, Moscow (1988).Google Scholar
  5. 5.
    O. O. Pashchenko, V. P. Serbin, and O. O. Starchevs’ka, Viscous Materials [in Ukrainian], Vishcha Shkola, Kiev (1995).Google Scholar
  6. 6.
    A. A. Pashchenko, cement Theory [in Russian], Budevel’nik, Kiev (1991).Google Scholar
  7. 7.
    M. T. Mel’nik and N. N. Shapalova, “Refractory concrete based on alumina cement with addition of active alumina,” Ogneupory, No. 10, 56 – 57 (1974).Google Scholar
  8. 8.
    R. M. Vorozhbiyan, G. N. Shabanova, A. N. Korogodskaya, et al., “Basis of possible use of nickel catalyst waste in the production of alumina cement,” Zbirnik, Nauk. Prats’ VAT UkrNDIVognetriviv im A. S. Berezhnogo, No. 112, 223 – 229 (2012).Google Scholar
  9. 9.
    R. M. Vorozhbiyan, G. N. Shabanova, and A. N. Korogodskaya, “Questions of using water cleaning waste in alumina cement manufacture,” Visnik NTU KhGP, No. 27, 164 – 173 (2011).Google Scholar
  10. 10.
    R. M. Vorozhbiyan, G. M. Shabanova, A. M. Korohods’ka, et al., Equal characteristics of aluminum oxide cements with the use of approaches employed in chemical plants, Zb. Naukovykh Prats’ PAT UkrNDIVognetriviv im. A. S. Berezhnogo, No. 113, 86 – 93 (2013).Google Scholar
  11. 11.
    R. M. Vorozhbiyan, G. M. Shabanova, A. M. Korohods’ka, and T. D. Ryshchenko, High-efficiency specialized viscous materials based on alkali-earth oxides, Zb. Nauk. Prats’ Ukrains’k. Derzh. Akad. Zaliz. Transportu, No. 138, 27 – 32 (2011).Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  • R. M. Vorozhbiyan
    • 1
  • G. N. Shabanova
    • 1
    Email author
  • A. N. Korogodskaya
    • 1
  1. 1.NTU, KhPIKhar’kovUkraine

Personalised recommendations