Microwave synthesis of nanocrystalline LaCoO3 samples and their catalytic activity towards decomposition of isopropanol

  • 21 Accesses


Nanocrystalline LaCoO3 powders were fabricated via the sol–gel microwave-induced combustion approach using metal nitrates as oxidant and citric acid as fuel. Calcination of the precursor was performed in the temperature range 400–800 °C. The precursor of the LaCoO3 powder as well as the calcination products were investigated using thermal analysis (TGA and DTA), FTIR, XRD and N2 adsorption techniques. In a dynamic air atmosphere, calcination was implemented in the temperature range 400–800 °C. XRD patterns show the fabrication of the perovskite rhombohedral phase of LaCoO3. The average nanoparticle size calculated from the XRD patterns was in the range 8–21 nm. Surface area measurements calculated from the N2 adsorption isotherms show low surface area values. The porosity of these materials was identified to be microporous in nature. SEM and TEM tests endorsed the findings. Analysis of TGA and DTA showed a sharp exothermic peak of about 358 °C and a steady weight loss of up to about 600 °C. The vapor-phase dehydration/dehydrogenation of isopropanol, in the temperature range 350–425 °C, was adopted to assess the catalytic performance. The activity of the LaMnO3 catalysts is mainly directed towards the dehydrogenation reaction forming acetone as a main product. The maximum yield was found for the sample calcined at 600 °C. A strong correlation was identified between the selectivity of dehydrogenation and the redox couple species evaluated. A potential reaction mechanism was suggested that would be compatible with the data obtained.

This is a preview of subscription content, log in to check access.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Scheme 1
Scheme 2
Scheme 3


  1. 1.

    Rougier A, Soiron S, Haihal I, Aymard L, Taouk B, Tarascon JM (2002) Influence of grinding on the catalytic properties of oxides. Power Technol 128:139–147. https://www.academia.edu/16318763/

  2. 2.

    Fang CY, Randan CA, Lanagan MT, Agrawal DK (2009) Microwave processing of electroceramic materials and devices. J Electroceram 22: 125–130. https://www.mri.psu.edu/sites/default/files/file_attach/178

  3. 3.

    Chal R, Gerardin C, Bulut M, Van Donk S (2010) Overview and industrial assessment of synthesis strategies towards zeolites with mesopores. Chem Cat Chem 3:67–81. https://doi.org/10.1002/cctc.201000158

  4. 4.

    Mizuno N, Misono M (1998) Heterogeneous catalysis. Chem Rev 98:199–218. https://doi.org/10.1021/cr960401q

  5. 5.

    Russo U, Nodari L, Faticanti M, Kuncser V, Filoti G (2005) Local interactions and electronic phenomena in substituted LaFeO3 perovskites. Solid State Ionics 176:97–102. https://doi.org/10.1016/j.ssi.2004.06.001

  6. 6.

    Giannakas AE, Ladavos AC, Pomonis PJ (2004) Preparation, characterization and investigation of catalytic activity for NO + CO reaction of LaMnO3 and LaFeO3 perovskites prepared via microemulsion method. Appl Catal B Environ 49:147–158. https://www.academia.edu/5954070

  7. 7.

    Misono M, Lombardo EA (1990) Elimination of pollutant gases—oxidation of CO, reduction and decomposition of NO. Catal Today 8:249–261. https://doi.org/10.1016/0920-5861(90)87021-T

  8. 8.

    Tejuca LG, Fierro JLG (1992) Composition and structure of perovskite surfaces. Catal Rev Sci Eng 34:4. https://books.google.com.sa/books?hl=ar&lr=&id=q0dZDwAAQBAJ&oi=fnd&pg=PA195

  9. 9.

    Rosset M, Perez-Lopez OW (2019) Cu–Ca–Al catalysts derived from hydrocalumite and their application to ethanol dehydrogenation. React Kinet Mech Catal 126:497–511. https://doi.org/10.1007/s11144-018-1513-y

  10. 10.

    Ponomareva EA, Krasnikova IV, Egorova EV, Mishakov IV, Vedyagin AA (2017) Dehydrogenation of ethanol over carbon-supported Cu–Co catalysts modified by catalytic chemical vapor deposition React Kinet Mech Catal 122: 399–408. doi:10.1007/s11144–017–1220–0.

  11. 11.

    Khalasmeida S, Sydorchuk V, Skubiszewska-Zieba J, Leboda R, Zazhigalov V (2010) Synthesis, thermoanalytical, and spectroscopical studies of dispersed barium titanate. J Therm Anal Calorim 101:779–784. https://doi.org/10.1007/s10973-010-0755-3

  12. 12.

    Khalameida S, Sydorchuk V, Leboda R, Skubiszewska-Zieba J, Zazhigalov V (2014) Preparation of nano-dispersed lithium niobate by mechanochemical route. J Therm Anal Calorim 115:579–586. https://doi.org/10.1007/s10973-013-3343-5

  13. 13.

    Sydorchuk V, Lutsyuk I, Shved V, Hreb V, Kondyr A, Zakutevskyy O, Vasylechko L (2020) PrCo1−xFexO3 perovskite powders for possible photocatalytic applications. Res Chem Intermed. https://doi.org/10.1007/s11164-019-04071-0

  14. 14.

    Kanhere P, Chen Z (2014) A review on visible light active perovskite-based photocatalysts. Molecules 19:19995–20022. https://doi.org/10.3390/molecules191219995

  15. 15.

    Tijare SN, Bakardjieva S, Subrt J, Joshi MV, Rayalu SS, Hishita S, Labhsetwar N (2014) Synthesis and visible light photocatalytic activity of nanocrystalline PrFeO3 perovskite for hydrogen generation in ethanol–water system. J Chem Sci 126:517–525. https://doi.org/10.1007/s12039-014-0596-x

  16. 16.

    Oygarden V, Lein HL, Grande T (2012) Structure, thermal expansion and electrical conductivity of Nb-substituted LaCoO3. J Solid State Chem 192:246–254. https://doi.org/10.1016/j.jssc.2012.04.026

  17. 17.

    Zuev AY, Vylkov AI, Tsvetkov DS (2011) Defect structure and oxide ion transport in Sr- and Cr-doped LaCoO3 − δ. Solid State Ionics 192:220–224. https://doi.org/10.1016/j.ssi.2010.05.049

  18. 18.

    Minh NQ (2004) Solid oxide fuel cell technology—features and applications. Solid State Ionics 174:271–277. https://doi.org/10.1016/j.ssi.2004.07.042

  19. 19.

    Kucharczyk B, Tylus W (2004) Effect of Pd or Ag additive on the activity and stability of monolithic LaCoO3 perovskites for catalytic combustion of methane. Catal Today 90:121–126. https://doi.org/10.1016/j.cattod.2004.04.016

  20. 20.

    Dinka P, Mukasyan AS (2007) Perovskite catalysts for the auto-reforming of sulfur containing fuels. J Power Sources 167:472–481. https://doi.org/10.1016/j.jpowsour.2007.02.058

  21. 21.

    Niu JR, Deng JG, Liu W, Zhang L, Wang GZ, Dai HX, He H, Zi XH (2007) Nanosized perovskite-type oxides La1−xSrxMO3−δ (M = Co, Mn; x = 0, 0.4) for the catalytic removal of ethyl acetate. Catal Today 126:420–429. https://doi.org/10.1016/j.cattod.2007.06.027

  22. 22.

    Delmastro A, Mazza D, Ronchetti S, Vallino M, Spinicci R, Brovetto P, Salis M (2001) Synthesis and characterization of non-stoichiometric LaFeO3 perovskite. Mater Sci Eng B 79:140–145. https://doi.org/10.1016/S0921-5107(00)00570-5

  23. 23.

    Campagnoli E, Tavares A, Fabbrini L, Rossetti I (2005) Effect of preparation method on activity and stability of LaMnO3 and LaCoO3 catalysts for the flameless combustion of methane. Appl Catal B 55:133–139. https://doi.org/10.1016/j.apcatb.2004.07.010

  24. 24.

    Qi X, Zhou J, Yue Z, Gui Z, Li L (2003) A simple way to prepare nanosized LaFeO3 powders at room temperature. Ceram Int 29:347–349. https://doi.org/10.1016/S0272-8842(02)00119-0

  25. 25.

    Jadhav AD, Gaikwad AB, Samuel V, Ravi V (2007) A low temperature route to prepare LaFeO3 and LaCoO3. Mater Lett 61:2030–2032. https://doi.org/10.1016/j.matlet.2006.08.009

  26. 26.

    Li S, Jing L, Fu W, Yang L, Xin B, Fu H (2007) Photoinduced charge property of nanosized perovskite-type LaFeO3 and its relationships with photocatalytic activity under visible irradiation. Mater Res Bull 42:203–212. https://doi.org/10.1016/j.materresbull.2006.06.010

  27. 27.

    Zheng WJ, Liu RH, Peng DK, Meng GY (2000) Hydrothermal synthesis of LaFeO3 under carbonate-containing medium. Mater Lett 43:19–22. https://doi.org/10.1016/S0167-577X(99)00223-2

  28. 28.

    Nakayama S, Okazaki M, Aung YL (2003) Preparations of perovskite-type oxides LaCoO3 from three different methods and their evaluation by homogeneity, sinterability and conductivity. Solid State Ionics 158:133–139. https://doi.org/10.1016/S0167-2738(02)00767-1

  29. 29.

    Pettiti I, Colonna S, Rossi SD, Faticanti M, Minellia G, Portaa P (2004) XAS characterization and CO oxidation on δ-alumina supported La, Mn, Co and Fe oxides. Phys Chem Chem Phys 6:1350. https://pubs.rsc.org/en/content/articlelanding/2004/cp/b316211g/unauth#!divAbstract

  30. 30.

    Patterson AL (1939) The Scherrer formula for X-ray particle size determination. Phys Rev 56:978. https://doi.org/10.1103/PhysRev.56.978

  31. 31.

    Khetre SM, Jadhav HV, Bangale SV, Jagdale PN, Bamane SR (2011). Use of mixed metal oxide as a catalyst in the decomposition of hydrogen peroxid. Adv Appl Sci Res 2: 252–259. www.pelagiaresearchlibrary.com

  32. 32.

    Nayak VS, Moffat JB (1993) Comparison of the surface properties of the metal—oxygen cluster compounds, 12-tungstophosphoric acid and ammonium 12-tungstophosphate from the sorption of benzene, nitrogen and pyridine. J Mol Catal 80:75–93. https://doi.org/10.1016/0304-5102(93)87111-K

  33. 33.

    Girgis MM, El-Awad AM (1993) Kinetics and mechanism of thermal decomposition of lithium oxalate catalyzed by Cd1−xCoxFe2O4(x = 0.0, 0.5 and 1.0) ferrospinel additives. Thermo-chim Acta 214:291–303. https://doi.org/10.1016/0040-6031(93)80066-J

  34. 34.

    Gabr RM, Girgis MM, El-Awad AM (1991) Role of CdO/Cd2+ content on the electrical conductivity and catalytic behaviour of Co1.0−x−Cd −Fe2.0 oxide/spinel system (0.0 %3c x %3c 0.5) for the decomposition of 2 propanol. Mater Chem Phys 28:413–429. https://doi.org/10.1016/0254-0584(91)90076-7

  35. 35.

    Hennings D, Mayr W (1978) Thermal decomposition of (BaTi) citrates into barium titanate. J Solid State Chem 26:329–338. https://doi.org/10.1016/0022-4596(78)90167-6

  36. 36.

    Gajbbiye NS, Bhattacharya V, Darshane VS (1995) Thermal decomposition of zinc-iron citrate precursor. Thermo-chim Acta 264:219–230. https://doi.org/10.1016/0040-6031(95)02331-U

  37. 37.

    Li GJ, Huang XX, Shi Y, Guo JK (2001) Preparation and characteristics of nanocrystalline NiO by organic solvent metho. Mater Lett 51:325–330. https://doi.org/10.1016/S0167-577X(01)00312-3

  38. 38.

    Pandey S, Mishra SB (2011) Sol–gel derived organic–inorganic hybrid materials: synthesis, characterizations and applications. J Sol-Gel Sci Technol 59:73–94. https://doi.org/10.1007/s10971-011-2465-0

  39. 39.

    Hosseini SA, Sadeghi MT, Alemi A, Niaei A, Salari D, Ahmadi L (2010) Synthesis, characterization, and performance of LaZnxFe1-xO3 perovskite nanocatalysts for toluene combustion. Chin J Catal 31:747–750. https://doi.org/10.1016/S1872-2067(09)60083-8

  40. 40.

    Hosseini SA, Salari D, Niaei A, Oskoui SA (2013) Physical–chemical property and activity evaluation of LaB0.5Co0.5O3 (B = Cr, Mn, Cu) and LaMnxCo1−xO3 (x = 0.1, 0.25, 0.5) nano perovskites in VOC combustion. J Ind Eng Chem 19:1903–1909. https://aet.irost.ir/article_844_7a8af94fcad7fc1b66525fbfee72e764

  41. 41.

    Wu WW, Li SS, Wu XH, Liao S, Cai JC (2010) Novel method for preparing NH4NiPO4·6H2O: hydrogen bonding coacervate selective self-assembly. J Chem 28:2389–2393. https://doi.org/10.1002/cjoc.201190009

  42. 42.

    Chandradass J, Bae DS, Kim KH (2011) A simple method to prepare indium oxide nanoparticles: Structural, microstructural and magnetic properties. Adv Powder Technol 22:370–374. https://doi.org/10.1016/j.apt.2010.05.006

  43. 43.

    Choso T, Tabata K (1997) Synthesis of LaMnO3+δby firing gels using citric acid. J Solid State Chem 129:60–65. https://doi.org/10.1006/jssc.1996.7229

  44. 44.

    Li H, Shao T, Li D, Chen D (2005) Nonisothermal reaction kinetics of diasporic bauxite. Thermo Chim Acta 427:9–12. https://doi.org/10.1016/j.tca.2004.08.016

  45. 45.

    Wenwei W, Jinchao C, Xuehang W, Sen L, Kaituo W, Lin T (2013) Nanocrystalline LaMnO3 preparation and kinetics of crystallization process. Adv Powder Technol 24:154–159. https://doi.org/10.1016/j.apt.2012.04.004

  46. 46.

    Kikkawa T, Yoshinaka M, Hirota K, Yamaguchi O (1995) Synthesis of LaCrO3 by the hydrazine method. J Mater Sci Lett 14:1071–1073. https://doi.org/https://doi.org/

  47. 47.

    Ridal K, Peña MA, Sastre E, Martnez-Arias A (2012) Effect of calcination temperature on structural properties and catalytic activity in oxidation reactions of LaNiO3 perovskite prepared by Pechini method. J Rare Earths 30:210–216. https://doi.org/10.1016/S1002-0721(12)60025-8

  48. 48.

    Ghiasi E, Malekzadeh A, Ghiasi M (2013) Moderate concentration of citric acid for the formation of LaMnO3 and LaCoO3 nano-perovskites. J Rare Earths 31:997–1002. https://doi.org/10.1016/S1002-0721(13)60020-4

  49. 49.

    Pecchi G, Campos C, Peña O (2009) Thermal stability against reduction of LaMn1−yCoyO3 perovskites. Mater Res Bull 44:846–853. https://doi.org/10.1016/j.materresbull.2008.09.009

  50. 50.

    Li JX, Le YY, Dai WL, Li HX, Fan KN (2008) Self-assembled Mg5(CO3)4(OH)2·4H2O nanosheet as an effective catalyst in the Baeyer-Villiger oxidation of cyclohexanone. Catal Commun 9:1334–13341. https://doi.org/10.1016/j.catcom.2007.11.029

  51. 51.

    Khazaei M, Malekzadeh A, Amini F, Mortazavi Y, Khodadadi A (2010) Effect of citric acid concentration as emulsifier on perovskite phase formation of nano-sized SrMnO3 and SrCoO3 samples. Cryst Res Technol 45:1064–1068. https://doi.org/10.1002/crat.201000258

  52. 52.

    Wang H, Liu J, Zhao Z, Wei Y, Xu Ch (2012) Comparative study of nanometric Co-, Mn- and Fe-based perovskite-type complex oxide catalysts for the simultaneous elimination of soot and NOx from diesel engine exhaust. Catal Today 184:288–300. https://doi.org/10.1016/j.cattod.2012.01.005

  53. 53.

    Brunauer SJ, Deming LS, Deming W, Teller, (1940) On a theory of the van der Waals adsorption of gases. J Am Chem Soc 62:1723–1732. https://doi.org/10.1021/ja01864a025

  54. 54.

    Emmett BH, Brunauer S (1937) Accumulation of alkali promoters on surfaces of iron synthetic ammonia catalysts. J Am Chem Soc 59:310–315. https://doi.org/10.1021/ja01281a026

  55. 55.

    De Boer JH, Everette EP, Stone FS (1958) The structure and properties of porous materials. Butterworths, London, p 68

  56. 56.

    Choudhary VR, Pataskar SG (1985) Thermal decomposition of ammonium copper chromate: effect of the addition of barium. Thermo-chim Acta 95:87–98. https://doi.org/10.1016/0040-6031(85)80035-6

  57. 57.

    Hammami R, Aïssa SB, Batis H (2009) Effects of thermal treatment on physico-chemical and catalytic properties of lanthanum manganite LaMnO3+y. Appl Catal A 353:145–153. https://doi.org/10.1016/j.apcata.2008.10.048

  58. 58.

    Kuhn JN, Ozkan US (2008) Surface properties of Sr- and Co-doped LaFeO3. J Catal 253:200–211. https://doi.org/10.1016/j.jcat.2007.10.005

  59. 59.

    Ancion C, Poncelet G (1994) Transformation of isopropanol over Pt/HxVMoO5.5 hydrogen bronze. Appl Catal A 108:31–40. https://doi.org/10.1016/0926-860X(94)85178-6

  60. 60.

    Tomzak DC, Allen JL, Poeppelmeier KR (1994) Characterization of the acidic and basic properties of αLiAIO2, γLiAIO2, and calcined “HAIO2” using isopropyl alcohol. J Catal 146:155–165. https://doi.org/10.1016/0021-9517(94)90018-3

  61. 61.

    Pines H, Manassen J (1966) The mechanism of dehydration of alcohols over alumina catalysts. Adv Catal 16:49–93. https://doi.org/10.1016/S0360-0564(08)60351-X

  62. 62.

    Bond GC, Flamerz S (1987) Structure and reactivity of titania-supported oxides. Part 3: reaction of isopropanol over vanadia-titania catalysts. Appl Catal 33:219–230. https://doi.org/10.1016/S0166-9834(00)80594-1

  63. 63.

    Trikalitis PN, Pomonis PJ (1995) Catalytic activity and selectivity of perovskites La1−xSrxV1−x3+Vx4+O3 for the transformation of isopropanol. Appl Catal A 131:309–322. https://doi.org/10.1016/0926-860X(95)00121-2

  64. 64.

    Khalameida S, Diyuk V, Zaderko A, Sydorchuk V, Skubiszewska-Zięba J (2018) The study of modified zirconium catalysts for selective dehydration of propanol. J Therm Anal Calorim 131:2361–2371. https://doi.org/10.1007/s10973-017-6733-2

  65. 65.

    Hashimoto K, Toukai N (1999) Dehydrogenation of alcohols over potassium zinc aluminum silicate hydroxide. J Mol Catal A 145:273–280. https://doi.org/10.1016/S1381-1169(99)00018-7

  66. 66.

    Wang JA, Bokhimi X, Novaro O, López T, Gómez R (1999) Effects of the surface structure and experimental parameters on the isopropanol decomposition catalyzed with sol–gel MgO. J Mol Catal A 145:291–300. https://doi.org/10.1016/S1381-1169(99)00035-7

  67. 67.

    Bautista FM, Campelo JM, Garcia A, Luna D, Marinas JM, Romero AA, Urbano MR (1997) N-Alkylation of aniline with methanol over CrPO4and CrPO4–AlPO4(5–50 wt% AlPO4) catalysts. J Catal 172:103–109. https://doi.org/10.1006/jcat.1997.1868

  68. 68.

    Hosseini SA, Salari D, Niaei A, Oskoui SA (2013) Physical–chemical property and activity evaluation of LaB0.5Co0.5O3 (B = Cr, Mn, Cu) and LaMnxCo1−xO3 (x = 0.1, 0.25, 0.5) nano perovskites in VOC combustion. J Ind Eng Chem 19:1903–1909. https://doi.org/10.1016/j.jiec.2013.02.034

  69. 69.

    Ashfaq A, Oak SG, Darshane VS (1995) Decomposition of cyclohexanol on the spinel system CuCr2−xFexO4. Bull Chem Soc Jpn 68:3651–3657. https://doi.org/10.1246/bcsj.68.3651

  70. 70.

    Wolkenstein T (1960) The electron theory of catalysis on semiconductors. Adv Catal 12:189–264. https://doi.org/10.1016/S0360-0564(08)60603-3

  71. 71.

    Balasubramanian K, Kuriacose JC (1984 ) Proc. 8th Int. Congr. Catal., Berlin (West).

  72. 72.

    Girgis MM, El-Awad AM (1993) The formation, electrical conduction and catalytic behaviour of ferrospinels Cd1.0−xCoxFe2O4, 0.0 ⩽ x ⩽ 0.5. Mater Chem and Phys 36:48–56. https://doi.org/10.1016/0254-0584(93)90006-8

  73. 73.

    Gabr RM, El-Awad AM, Girgis MM (1991) Role of the structural and electronic properties of Cr1−xFexVO4 (0⩽x⩽1) solid solutions on their catalytic activity. Mater Chem Phys 30:69–75. https://doi.org/10.1016/0254-0584(91)90156-O

  74. 74.

    Lundeen AJ, Van Hoozer R (1963) Selective catalytic dehydration of 2-alcohols; a new synthesis of 1-olefins. J Am Chem Soc 85:2180–2181. https://doi.org/10.1021/ja00897a041

Download references

Author information

Correspondence to Rasha M. K. Mohamed.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Mohamed, R.M.K., Girgis, M.M., El-Awad, A.M. et al. Microwave synthesis of nanocrystalline LaCoO3 samples and their catalytic activity towards decomposition of isopropanol. Reac Kinet Mech Cat (2020). https://doi.org/10.1007/s11144-020-01733-8

Download citation


  • LaCoO3 perovskite
  • Auto-combustion
  • Microwave synthesis
  • 2-propanol catalytic reaction