Acid-modified phonolite and foamed zeolite as supports for NiW catalysts for deoxygenation of waste rendering fat

  • J. M. Hidalgo
  • Z. Tišler
  • A. Vráblík
  • R. Velvarská
  • J. Lederer
Article
  • 5 Downloads

Abstract

Acid-modified phonolite material, Al2O3/foam zeolite and foam zeolite were used as supports for NiW catalysts. The zeolite type materials were prepared by a novel procedure from natural clinoptilolite. Phonolite materials were loaded with 5, 7.5 and 10 wt% of Ni containing 10, 7.5 and 5 wt% of W. Al2O3/foam zeolite contained 4 and 13 wt% of Ni and W and pure foamed zeolite was effectively loaded with 5 and 16 wt% of Ni and W. NiW/Al2O3 catalyst (3 wt% Ni and 11 wt% of W) was used for comparison of catalytic properties of synthesized materials. Catalytic tests were carried out in an autoclave pressurized at 7 MPa (H2) at room temperature and then heated to 365 °C for 1 h. Catalysts were characterized by N2 physisorption, XRD, XRF, NH3-TPD, CO2-TPD and H2-TPR. Catalyst properties were compared for the HDO of rendering fat into hydrocarbons. The liquid products were analyzed by simulated distillation, C, H, N, S elemental analysis, ATR and density (15 °C). Gaseous products were characterized by RGA-GC. Used catalysts were also analyzed by N2-TGA and O2-TGA. Novel phonolite modified solids and NiW/foam zeolite type materials were tested for the first time as catalysts being in some cases more active than NiW/Al2O3 material. Ni(5%)W(10%)/Acid phonolite and NiW/Foamed Zeolite resulted to be the most active materials for the HDO and hydrocracking reactions. The lowest amount of carbonaceous species on the surface of tested catalyst was found for the Ni(5%)W(10%)/Acid phonolite solid.

Keywords

HDO Decarboxylation Fat Phonolite Foam Zeolite 

Notes

Acknowledgements

The publication is a result of the project Development of the UniCRE Centre (LO1606) which has been financially supported by the Ministry of Education, Youth and Sports of the Czech Republic (MEYS) under the National Sustainability Programme I. The result was achieved using the infrastructure of the project Efficient Use of Energy Resources Using Catalytic Processes (LM2015039) which has been financially supported by MEYS within the targeted support of large infrastructures.

Supplementary material

11144_2018_1510_MOESM1_ESM.docx (235 kb)
Supplementary material 1 (DOCX 234 kb)

References

  1. 1.
    Bezergianni S, Dimitriadis A, Kikhtyanin O, Kubička D (2018) Refinery co-processing of renewable feeds. Prog Energy Combust Sci 68:29–64CrossRefGoogle Scholar
  2. 2.
    Kovács S, Boda L, Leveles L, Thernesz A, Hancsók J (2010) Chem Eng Trans 21:1974–9791Google Scholar
  3. 3.
    Arun N, Sharma RV, Dalai AK (2015) Green diesel synthesis by hydrodeoxygenation of bio-based feedstocks: strategies for catalyst design and development. Renew Sust Energ Rev 48:240–255CrossRefGoogle Scholar
  4. 4.
    Bezergianni S, Dimitriadis A (2013) Comparison between different types of renewable diesel. Renew Sustain Energy Rev 21:110–116CrossRefGoogle Scholar
  5. 5.
    Eller Z, Varga Z, Hancsok J (2016) Advanced production process of jet fuel components from technical grade coconut oil with special hydrocracking. Fuel 182:713–720CrossRefGoogle Scholar
  6. 6.
    Baladincz P, Hancsók J (2015) Fuel from waste animal fats. Chem Eng J 282:152–160CrossRefGoogle Scholar
  7. 7.
    Woodgate SL, Johan T (2014) Food processing: principles and applications, 2nd edn. Wiley, New JerseyGoogle Scholar
  8. 8.
    Czech Biomass Association, Biom.cz (2009) online article, Prague. https://biom.cz/cz/odborne-clanky/vyuziti-kafierniho-tuku-k-vyrobe-biopaliva. ISSN: 1801-2655. Accessed 23 Aug 2018
  9. 9.
    Keramost a.s. Czech Republic (2018) Phonolite supplied by the company Keramost, Most. http://www.keramost.cz/en/products/-/phonolite. Accessed 23 Aug 2018
  10. 10.
    Domaracka L, Strba L, Krsak B, Muchova M (2015) Possibilities of profitable business with nature zeolite—an example from the Nižný Hrabovec Deposit, Slovakia. IJSRIT 2:12–19Google Scholar
  11. 11.
    Clinoptilolite supplied by the company unipoint ag. https://www.unipoint.ch/pages/english/klinofeed.php. Accessed 23 Aug 2018
  12. 12.
    Hidalgo Herrador JM, Tišler Z, Hajková P, Soukupová L, Zárybnická L, Černá K (2017) Cold plasma and acid treatment modification effects on phonolite. Acta Chim Slov 64:598–602CrossRefPubMedGoogle Scholar
  13. 13.
    ASTM D2887 (2016) Standard test method for boiling range distribution of petroleum fractions by gas chromatography. ASTM International, West ConshohockenGoogle Scholar
  14. 14.
    ASTM D5291 (2010) Standard test methods for instrumental determination of carbon, hydrogen, and nitrogen in petroleum products and lubricants. ASTM International, West ConshohockenGoogle Scholar
  15. 15.
    ASTM D4629 (2012) Standard test method for trace nitrogen in liquid petroleum hydrocarbons by syringe/inlet oxidative combustion and chemiluminescence detection. ASTM International, West ConshohockenGoogle Scholar
  16. 16.
    ASTM D5453 (2016) Standard test method for determination of total sulfur in light hydrocarbons, spark ignition engine fuel, diesel engine fuel, and engine oil by ultraviolet fluorescence. ASTM International, West ConshohockenGoogle Scholar
  17. 17.
    December 2014, Scientific Reports 4:7413,  https://doi.org/10.1038/srep07413, Source, PubMed, License CC BY-NC-SA 4.0, Hu LongHu Long, Tielin ShiTielin Shi, Hao Hu, Zirong Tang
  18. 18.
    Wang XG, Yang NH, Yuan L, Pang SJ (1998) High-resolution electron microscopy analysis of microstructural changes in WOx electrochromic films. Surf Coat Technol 110:184–187CrossRefGoogle Scholar
  19. 19.
    Chauruka SR, Hassanpour A, Brydson R, Roberts KJ, Ghadiri M, Stitt H (2015) Effect of mill type on the size reduction and phase transformation of gamma alumina. Chem Eng Sci 134:774–783CrossRefGoogle Scholar
  20. 20.
    Mansouri N, Rikhtegar N, Panahi HA, Atabi F, Shahraki BK (2013) Porosity, Characterization and structural properties of natural zeolite clinoptilolite as a sorbent. Environ Prot Eng 39:139–152Google Scholar
  21. 21.
    Toteva V, Georgiev A, Topalova L (2009) Oxidative desulphurization of light cycle oil: monitoring by FTIR spectroscopy. Fuel Process Technol 90:965–970CrossRefGoogle Scholar
  22. 22.
    Vlachos N, Skopelitis Y, Psaroudaki M, Konstantinidou V, Chatzilazarou A, Tegou E (2006) Applications of Fourier transform-infrared spectroscopy to edible oils. Anal Chim Acta 573:459–465CrossRefPubMedGoogle Scholar
  23. 23.
    Morgan T, Santillan-Jimenez E, Harman-Ware AE, Ji Y, Grubb D, Crocker M (2012) Catalytic deoxygenation of triglycerides to hydrocarbons over supported nickel catalysts. Chem Eng J 189–190:346–355CrossRefGoogle Scholar
  24. 24.
    Hancsók J, Sági D, Valyon J (2018) Diesel fuel blending components from mixture of waste animal fat and light cycle oil from fluid catalytic cracking. J Environ Manage 223:92–100CrossRefPubMedGoogle Scholar
  25. 25.
    Mikulec J, Cvengros J, Jorikova L, Banic M, Kleinova A (2009) Diesel production technology from renewable sources—second generation fuels. Chem Eng Trans 18:475–480Google Scholar
  26. 26.
    Kim D, Vardon DR, Murali D, Sharma BK, Strathmann TJ (2016) Valorization of waste lipids through hydrothermal catalytic conversion to liquid hydrocarbon fuels with in situ hydrogen production. ACS Sustain Chem Eng 4:1775–1784CrossRefGoogle Scholar

Copyright information

© Akadémiai Kiadó, Budapest, Hungary 2018

Authors and Affiliations

  1. 1.Unipetrol Centre for Research and Education/UNICREZáluží 1Czech Republic

Personalised recommendations