Application of Domestic Heat-Resistant Powders in Additive Techniques
- 6 Downloads
The products produced using additive techniques (with no use of conventional production techniques) are of high priority for aerospace and aircraft engine building. The possibility of using domestic heat-resistant powders in additive processes is investigated. It is shown that domestic heat-resistant materials are promising for additive techniques. It is found out that domestic powders have a wide size range and the defects, such as satellites and chips, are detected on the powder granule surface. It is revealed that the surface morphology and microstructure of particles are typical for heat-resistant nickel alloys. It is established that heat-resistant nickel-based EP741p alloy (SE USSI) can be used in additive techniques.
Keywordsadditive techniques heat-resistant nickel-based material flow rate of powder morphology microstructure
- 1.E. N. Kablov, O. G. Ospennikova, and B. S. Lomberg, “Strategic directions in developing structuralmaterials and their processing technologies for today and future aircraft engines,” Avtomat. Svarka, Nos. 10–11, 23–32 (2013).Google Scholar
- 2.J. Hart, Additive Manufacturing, Path: http://web.mit.edu/2.810/www/lecture/19-additive-mfg.pdf.
- 3.I. Yu. Smurov, S. G. Konov, and D. V. Kotoban, “Implementing additive processes and manufacturing in domestic industries,” Nov. Mater. Nauka Tech., No. 2, 11–22 (2015).Google Scholar
- 4.V. M. Dovbysh, P. V. Zabednov, and M. A. Zlenko, “Additive processes and metal,” // Path: http://nami.ru/uploads/docs/centr_technology_docs/55a62fc89524bAT_metall.pdf.
- 5.I. V. Boguslavskii, “Additive Processes in JSC UAC,” in: III International NDEXPO-2016 Forum Proceedings: High Technologies for Sustainable Development (April 5–7 2016, Moscow). JSC United Aircraft Corporation. Moscow (2016), pp. 87–96.Google Scholar
- 6.Yu. M. Gryaznov, S. V. Shotin, and V. N. Chuvil’deev, “Physical and mechanical properties and structure of Inconel 718 alloy, produced using layer-by-layer laser melting,” Fiz. Tverd. Tela, 1, No. 4, 46–51 (2014).Google Scholar
- 7.H. G. Gessinger, Powder Metallurgy of Heat-Resistant Alloys [Russian Translation]. Metalurgy, Chelyabinsk (1988), p. 320.Google Scholar
- 8.O. A. Glotka, Design and Analysis of Structure–Phase state of Ni–W and Fe–W Stacks Based on Refractory W–Ni–Fe Scrap for Alloying Special Materials in Gas Turbine Building [in Ukrainian], Abstract of PhD Thesis, Zaporizhya (2011), p. 18.Google Scholar