A facile synthesis of heteroatom-doped carbon framework anchored with TiO2 nanoparticles for high performance lithium ion battery anodes
- 189 Downloads
Titanium dioxide (TiO2)-based materials have been well studied because of the high safety and excellent cycling performance when employed as anode materials for lithium ion batteries (LIBs), whereas, the relatively low theoretical capacity (only 335 mAh g−1) and serious kinetic problems such as poor electrical conductivity (~ 10−13S cm−1) and low lithium diffusion coefficient (~ 10−9 to 10−13 cm2 s−1) hinder the development of the TiO2-based anode materials. To overcome these drawbacks, we present a facile strategy to synthesize N/S dual-doping carbon framework anchored with TiO2 nanoparticles (NSC@TiO2) as LIBs anode. Typically, TiO2 nanoparticles are anchored into the porous graphene-based sheets with N, S dual doping feature, which is produced by carbonization and KOH activation process. The as-obtained NSC@TiO2 electrode exhibits a high specific capacity of 250 mAh g−1 with a coulombic efficiency of 99% after 500 cycles at 200 mA g−1 and excellent rate performance, indicating its promising as anode material for LIBs.
KeywordsLithium ion batteries N/S dual-doping Nanoparticles Anode materials Energy storage
This study was funded by the National Nature Science Foundation of China (Grant no. 51204209).
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- Kamata M, Fujine S, Yoneda K, Kanda K, Esaka T (1999) Diffusion coefficient measurement of lithium ion in sintered li1.33ti1.67o4 by means of neutron radiography. Solid State Ionics 123(1):165Google Scholar
- Yu Z, Song J, Gordin ML, Yi R, Tang D, Wang D (2015) Phosphorus‐graphene nanosheet hybrids as lithium‐ion anode with exceptional high‐temperature cycling stability. Adv Sci 2(1–2). https://doi.org/10.1002/advs.201400020