A flexible silica aerogel with good thermal and acoustic insulation prepared via water solvent system

  • Xiaohua Li
  • Zichun YangEmail author
  • Kunfeng Li
  • Shuang Zhao
  • Zhifang Fei
  • Zhen Zhang
Original Paper: Nano- and macroporous materials (aerogels, xerogels, cryogels, etc.)

Abstract

In this paper, transparent flexible hydrophobic silica aerogels were prepared by replacing the traditional alcohol solvent with water, using methyltriethoxysilane (MTES) and cetyltrimethylammonium bromide (CTAB), via acid-base two steps method and CO2 supercritical drying. The role of surfactant CTAB in the gel–sol process was revealed, and the effect of CTAB concentration on the gel structure was analyzed. With the concentration increasing, the skeleton structure of the gel gradually changed from coarse graininess to continuous fiber. The obtained aerogels showed good elastic properties. With the increasing of density, the elastic modulus of aerogels gradually increased, so that the length could be restored to 63% of the original length after 50% compression strain. Aerogels also had low thermal conductivity and good thermal stability. The thermal conductivity at room temperature was only 0.0215 W/(m·K) and the initial decomposition temperature was up to 511 °C. For the aerogel with thickness of 11.8 mm and density of 60 mg/cm3, it showed good sound absorption and sound insulation properties. When the sound frequency was 2000 Hz, the sound absorption coefficient was 0.91, and the sound transmission loss between 500 and 1600 Hz was 13–21 dB. This work provides a facile approach to fabricate lightweight and flexible silica aerogels for thermal and acoustic insulation applications.

Highlights

  • The role of surfactant CTAB in the sol–gel process of methyltriethoxysilane (MTES) aqueous system was revealed, and the effect of CTAB concentration on the gel structure was analyzed.

  • Preparation of flexible and transparent silica aerogels in aqueous solvent system using methyltriethoxysilane (MTES) for the first time. The thermal conductivity of samples is between 0.0215 and 0.0255 W/(m·K) and the initial decomposition temperature of the sample is about 511 °C.

  • For the aerogel with thickness of 11.8 mm and density of 60 mg/cm3, the sound absorption coefficient was 0.91 when the sound frequency was 2000 Hz, and the sound transmission loss between 500 and 1600 Hz was 13–21 dB.

Keywords

MTES CTAB Silica aerogels Elastic Sound insulation Thermal conductivity 

Notes

Acknowledgements

This work was supported by the National Natural Science Foundation of China (Grant No. 51802347) and Natural Science Foundation of Hubei Province (Grant No. 2018CFB183).

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. 1.
    Dorcheh AS, Abbasi MH (2008) Silica aerogel; synthesis, properties and characterization. J Mater Process Technol 199(1–3):10–26CrossRefGoogle Scholar
  2. 2.
    Du A, Zhou B, Zhang Z et al. (2013) A special material or a new state of matter: a review and reconsideration of the aerogel. Materials 6(3):941–968CrossRefGoogle Scholar
  3. 3.
    Kistler SS (1931) Coherent expanded-aerogels. J Chem Phys 36(1):52–64CrossRefGoogle Scholar
  4. 4.
    Pan Y, He S, Gong L et al. (2017) Low thermal-conductivity and high thermal stable silica aerogel based on MTMS/water-glass co-precursor prepared by freeze drying. Mater Des 113:246–253CrossRefGoogle Scholar
  5. 5.
    Fang ZF, Feng KL, Chun ZY et al. (2018) Synthesis and characterization of the APTES cross-linked polyimide aerogels. Mater Guide 32(20):138–142Google Scholar
  6. 6.
    Feng J, Le D, Nguyen ST et al. (2016) Silica–cellulose hybrid aerogels for thermal and acoustic insulation applications. Colloids Surf A: Physicochem Eng Asp 506:298–305CrossRefGoogle Scholar
  7. 7.
    Eskandari N, Motahari S, Atoufi Z et al. (2017) Thermal, mechanical, and acoustic properties of silica-aerogel/UPVC composites. J Appl Polym Sci 134:1–8Google Scholar
  8. 8.
    Yu Y, Wu X, Guo D, Fang J (2014) Preparation of flexible, hydrophobic, and oleophilic silica aerogels based on a methyltriethoxysilane precursor. J Mater Sci 49:7715–7722CrossRefGoogle Scholar
  9. 9.
    Sarawade PB, Kim JK, Kim HK et al. (2007) High specific surface area TEOS-based aerogels with large pore volume prepared at an ambient pressure. Appl Surf Sci 254(2):574–579CrossRefGoogle Scholar
  10. 10.
    Hæreid S, Dahle M, Lima S et al. (1995) Preparation and properties of monolithic silica xerogels from TEOS-based alcogels aged in silane solutions. J Non-Cryst Solids 186(2):96–103CrossRefGoogle Scholar
  11. 11.
    Hæreid S, Anderson J, Einarsrud MA et al. (1995) Thermal and temporal aging of TMOS-based aerogel precursors in water. J Non-Cryst Solids 185(3):221–226CrossRefGoogle Scholar
  12. 12.
    Tamon H, Sone T, Okazaki M (1997) Control of mesoporous structure of silica aerogel prepared from TMOS. J Colloid Interface Sci 188(1):162–167CrossRefGoogle Scholar
  13. 13.
    Hegde ND, Rao AV (2007) Physical properties of methyltrimethoxysilane based elastic silica aerogels prepared by the two-stage sol–gel process. J Mater Sci 42(16):6965–6971CrossRefGoogle Scholar
  14. 14.
    Dong H, Brennan JD (2006) Macroporous monolithic methylsilsesquioxanes prepared by a two-step acid/acid Processing Method. Chem Mater 18(17):4176–4182CrossRefGoogle Scholar
  15. 15.
    Nadargi DY, Latthe SS, Hirashima H, Rao AV (2009) Studies on rheological properties of methyltriethoxysilane (MTES) based flexible superhydrophobic silica aerogels. Microporous Mesoporous Mater 117:617–626CrossRefGoogle Scholar
  16. 16.
    Cui S, Liu Y, Fan MH et al. (2011) Temperature dependent microstructure of MTES modified hydrophobic silica aerogels. Mater Lett 65(4):606–609CrossRefGoogle Scholar
  17. 17.
    Nadargi DY, Rao AV (2009) Methyltriethoxysilane: New precursor for synthesizing silica aerogels. J Alloy Compd 467(1–2):0–404Google Scholar
  18. 18.
    Cheng X, Li C, Li Z, Shi X, Gong L, Zhang H (2017) Rapid synthesis of ambient pressure dried monolithic silica aerogels using water as the only solvent. Mater Lett 204:157–160CrossRefGoogle Scholar
  19. 19.
    Kanamori K, Aizawa M, Nakanishi K et al. (2010) New transparent methylsilsesquioxane aerogels and xerogels with improved mechanical properties. Adv Mater 19(12):1589–1593CrossRefGoogle Scholar
  20. 20.
    Arenas J, Crocker M (2010) Recent trends in porous sound-absorbing materials. Sound Vib 44:12–17Google Scholar
  21. 21.
    Francesca M, Anderson AM, Carroll MK et al. (2018) Acoustic measurements on monolithic aerogel samples and application of the selected solutions to standard window systems. Appl Acoust 142:123–131CrossRefGoogle Scholar
  22. 22.
    Patel V, Dharaiya N, Ray D et al. (2014) pH controlled size/shape in CTAB micelles with solubilized polar additives: A viscometry, scattering and spectral evaluation. Colloids Surf A: Physicochem Eng Asp 455:67–75CrossRefGoogle Scholar
  23. 23.
    Xing JX, Guo ZZ (2003) In: Zhang Y (ed.) Surfactant application principle. Chemical Industry Press, ChinaGoogle Scholar
  24. 24.
    Yan L, Ren H, Zhu J, Bi Y, Zhang L (2018) One-step eco-friendly fabrication of classically monolithic silica aerogels via water solvent system and ambient pressure drying. J Porous Mater 26(3):785–791Google Scholar
  25. 25.
    Lyon LA (2003) In: Birdi K. S. (ed.) Handbook of surface and colloid chemistry. 2nd edn. CRC Press, DenmarkGoogle Scholar
  26. 26.
    Fu JM, Ning ZG, Xi CD (2004) Catalytic kinetic behavior of CTAB micelle solution for basic hydrolysis of normal fatty acid ethyl ester. J Ningxia Univ: Nat Sci Ed 25(4):349–352Google Scholar
  27. 27.
    Kanamori K, Aizawa M, Nakanishi K, Hanada T (2008) Elastic organic–inorganic hybrid aerogels and xerogels. J Sol-Gel Sci Technol 48:172–181CrossRefGoogle Scholar
  28. 28.
    Kanamori K, Nakanishi K, Hanada T (2009) Sol-gel synthesis, porous structure, and mechanical property of polymethylsilsesquioxane aerogels. J Ceram Soc Jpn 117:1333–1338CrossRefGoogle Scholar
  29. 29.
    Ricciardi P, Belloni E, Cotana F (2014) Innovative panels with recycled materials:thermal and acoustic performance and life cycle assessment. Appl Energy 134:150–62CrossRefGoogle Scholar
  30. 30.
    Malakooti S, Churu HG, Lee A et al. (2017) Sound insulation properties in low-density, mechanically strong and ductile nanoporous polyurea aerogels. J. Non-Cryst Solids 476:36–45Google Scholar
  31. 31.
    Li YZ (2001) In: Cheng RX (ed.) Noise control technology. Chemical Industry Press, ChinaGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.School of Power EngineeringNavy University of EngineeringWuhanChina

Personalised recommendations