Sol–gel based thermally stable mesoporous TiO2 nanomatrix for fiber optic pH sensing
- 74 Downloads
Thermally stable acid catalyzed mesoporous titania (TiO2) nanomatrices are obtained by sol–gel method for fiber optic pH sensing. These synthesized nanoparticles are annealed at 300 °C, at two time intervals i.e., 1 h and 2 h, characterized with several analytical techniques such as FE-SEM/EDS, AFM, XRD, FTIR, TGA, and Brunauer–Emmett–Teller (BET) analysis. Microscopic analysis shows that synthesized nanoparticles have crack-free, dense and homogeneous surface with low surface roughness (4.4–5.9 nm). EDS mapping confirms the uniform distribution of Ti in all samples. XRD findings revealed the TiO2 anatase phase. BET analysis shows that the mesoporous synthesized TiO2 nanoparticles have surface areas 169 m2/g and average pore diameter 39.2 Å. However, surface area is decreased to 113 and 102 m2/g and average pore diameter increased up to 62.36 and 68.18 Å after 1 h and 2 h heat treatment, respectively. Furthermore, the sensing activity of phenolphthalein (phph) doped mesoporous TiO2 nanoparticles/matrix is found to be high at pH 12 without any leaching/cracking.
KeywordsSol-gel method Cracks allevation Mesoporous TiO2 nanoparticles Optical properties Fiber optic sensing activity
The authors like to express their gratitude to the Government of Malaysia through grant FRGS vote 03E89 for the financial support in this project. Thanks are also due to UTM through RMC for awarding the Postdoctoral fellowship to the first author.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 2.Hasan MM, Haseeb MA, Saidur R, Masjuki HH (2008) Effects of annealing treatment on optical properties of anatase TiO2 thin films. Int J Chem Biol Eng 1(2):92–96Google Scholar
- 10.Pecchi G, Ryes P, Lopez T, Gomez R, Moreno A, Fierro JLG (2002) Effect Of chlorine precursor in surface and catalytic properties of Fe/Tio2 catalysts. Bol Soc Chil Quim 47:191–197Google Scholar
- 14.Aleksandra L, Ines O, Ivana M, Otto SW (1998) pH optical sensors based on sol–gels: chemical doping versus covalent immobilization. Anal Chim Acta 367(1–3):159–165Google Scholar
- 16.Samira B, Kamyar S, Sharifah BAH (2013) Synthesis and characterization of anatase titanium dioxide nanoparticles using egg white solution via sol–gel method J Chem 2013:5848205Google Scholar