Water Migration in One-Side Heated Concrete: 4D In-Situ CT Monitoring of the Moisture-Clog-Effect
Explosive spalling due to fire exposure in concrete structures can lead severe damage and, in the worst case, to premature component failure. For this reason, an in situ investigation of water migration in concrete due to surface heating was undertaken. During these experiments, a miniaturized concrete specimen within a confining and insulating double-hull was subjected to surface heating during simultaneous X-ray computed tomography (CT) scanning. Through the use of subtraction-based image analysis techniques, it was possible to observe and quantify not only drying within areas of the concrete matrix close to the heated surface, but also the migration of moisture to both pore and matrix regions deeper within the specimen. It was also discovered that the correction of CT images for specimen deformation using DVC and variable detector performance using calibrated image filters significantly improved the quality of the results. This clearly demonstrates the potential of X-ray CT for evaluation of other rapid-density-change phenomena in concrete and other building materials.
KeywordsIn-Situ X-ray CT DVC Heated concrete Water migration Fire
The authors would like to acknowledge their gratitude to Dr. Illerhaus, Mr. Meinel and Mr. Onel for their support and advice regarding CT scanning techniques and analysis methods. The work was internally funded by the Bundesanstalt für Materialforschung und –prüfung (BAM) through the Menschen-Ideen-Strukturen (MIS) Program.
- 1.Kordina, K.: Planung unterirdischer Verkehrsanlagen gegen Brandgefahren. In: Tunnel (2004)Google Scholar
- 3.Jansson, R., Boström, L.: Fire spalling—the moisture effect. In: Dehn F., Koenders, E.A.B. (eds.) 1st International Workshop on Concrete Spalling due to Fire Exposure, Leipzig. pp. 120–129 (2009)Google Scholar
- 7.Powierza, B.: In-Situ CT observation of water migration in heated concrete. In: 3rd International Conference on Tomography of Materials and Structures, Lund, Sweden (2017)Google Scholar
- 8.Stelzner, L., et al.: Analysis of moisture transport in unilateral-heated dense high-strength concrete. In: 5th International Workshop on Concrete Spalling due to Fire Exposure, Borås, Sweden (2017)Google Scholar
- 11.Martz, H.E., et al.: Computerized-tomography analysis of reinforced-concrete. ACI Mater. J. 90(3), 259–264 (1993)Google Scholar
- 12.Morgan, I.L., et al.: Examination of concrete by computerized-tomography. J. Am. Concr. Inst. 77(1), 23–27 (1980)Google Scholar
- 19.Oesch, T.S.: In-Situ CT investigation of pull-out failure for reinforcing bars embedded in conventional and high-performance concretes. In: 6th Conference on Industrial Computed Tomography (ICT), Wels, Austria: NDT.net (2016)Google Scholar
- 20.Paetsch, O., et al.: 3D corrosion detection in time-dependent CT images of concrete. In: Digital Industrial Radiology and Computed Tomography Conference, Ghent, Belgium (2015)Google Scholar
- 27.Schneider, U.: Compressive strength for service and accident conditions. Mater. Struct. 28(181), 410–414 (1995)Google Scholar
- 28.Kalifa, P., Menneteau, F.-D., Quenard, D.: Spalling and pore pressure in HPC at high temperatures. Papers presented at the symposium on transport properties and microstructure of cement-based systems, vol. 30, pp. 1915–1927 (2000)Google Scholar
- 36.DIN, V., 1-2 Eurocode 2: Planung von Stahlbeton-und Spann-betontragwerken-Teil 1-2: Allgemeine Regeln-Tragwerksbemessung für den Brandfall, Ausgabe Dezember (2010)Google Scholar