Synthesis and characterization of novel fluorinated naphthalene-based poly(arylene ether ketone)s with low dielectric constants

  • Xiaoyu Liu
  • Xu Xu
  • Zhuang LiuEmail author
Article
  • 12 Downloads

Abstract

At present, in the integrated circuit technology, the requirements for polymeric interlayer dielectric materials are getting higher and higher, such as high thermostability, high modulus, low dielectric constant, excellent processability. In this paper, some soluble fluorinated naphthalene-based poly(arylene ether ketone)s were prepared from three types of novel fluorinated naphthalene-based bisphenol monomers. With the introduction of fluorine atoms and naphthalene rings, the obtained polymers exhibited more excellent thermal stability than traditional poly(ether ether ketone),which the glass transition temperatures (Tg) were above 167 °C, and decomposition temperatures at 5% (Td5) were above 528 °C under nitrogen. The tensile strengths of membranes were in the range of 62.86–104.13 MPa, tensile modulus in the range of 1.96–3.83 GPa. Moreover, the poly(arylene ether ketone)s with 1-(3,5-ditrifluoromethylbenzoyl) (NPEEK-3) exhibited the lowest dielectric constant at 1 MHz and water uptake which were 2.57 and 0.31%, respectively. The dielectric constant is much lower than commercialized poly(ether ether ketone) of 3.3.

Notes

Funding

This work was supported by the project of scientific research of the Education Department of Liaoning Province (Grant No. L2015481) and Scientific Research Foundation of Shenyang Agricultural University (Grant No. 880415038).

References

  1. 1.
    E. Aram, S. Mehdipour-Ataei, J. Appl. Polym. Sci. 128, 4387 (2013)CrossRefGoogle Scholar
  2. 2.
    L. Tao, H. Yang, J. Liu, L. Fan, S. Yang, Polymer 50, 6009 (2009)CrossRefGoogle Scholar
  3. 3.
    G.D. Fu, Z. Yuan, E.T. Kang, K.G. Neoh, D.M. Lai, A.C. Huan, Adv. Funct. Mater. 15, 315 (2005)CrossRefGoogle Scholar
  4. 4.
    K. Zhang, Q. Zhuang, Y. Zhou, X. Liu, G. Yang, Z. Han, J. Polym. Sci. A 50, 5115 (2012)CrossRefGoogle Scholar
  5. 5.
    Y. Su, F. Chang, Polymer 44, 7989 (2003)CrossRefGoogle Scholar
  6. 6.
    M. Tseng, Y. Liu, Polymer 51, 5567 (2010)CrossRefGoogle Scholar
  7. 7.
    S. Devaraju, M.R. Vengatesan, M. Selvi, J.K. Song, M. Alagar, Polym. Compos. 34, 904 (2013)CrossRefGoogle Scholar
  8. 8.
    F. Eckstorff, Y. Zhu, R. Maurer, T.E. Müller, S. Scholz, J.A. Lercher, Polymer 52, 2492 (2011)CrossRefGoogle Scholar
  9. 9.
    K. Goto, J. Komada, J. Kida, S. Tamai, J. Photopolym. Sci. Technol. 17, 215 (2004)CrossRefGoogle Scholar
  10. 10.
    J. Xie, W. Peng, G. Li, J. Jiang. Polym. Bull. 67, 45 (2011)CrossRefGoogle Scholar
  11. 11.
    J.B. Rose, Polymer 15, 456 (1974)CrossRefGoogle Scholar
  12. 12.
    D.P. Jones, D.C. Leach, D.R. Moore, Polymer 26, 1385 (1985)CrossRefGoogle Scholar
  13. 13.
    A.A. Goodwin, M.M. Browne, High Perform. Polym. 9, 1 (1997)CrossRefGoogle Scholar
  14. 14.
    D. Veazey, T. Hsu, E.D. Gomez, J. Appl. Polym. Sci. 134, 1 (2017)CrossRefGoogle Scholar
  15. 15.
    F. Wang, J. Roovers, P.M. Toporowski, Macromolecules 26, 3826 (1993)CrossRefGoogle Scholar
  16. 16.
    R. Singh, A.S. Hay, Macromolecules 24, 2637 (1991)CrossRefGoogle Scholar
  17. 17.
    Y. Zhang, X. Sun, Y. Niu, R. Xu, G. Wang, Z. Jiang, Polymer 47, 1569 (2006)CrossRefGoogle Scholar
  18. 18.
    M. Cai, F. Xiao, N. Ding, C. Song, Polym. Adv. Technol. 20, 981 (2009)CrossRefGoogle Scholar
  19. 19.
    D. Wang, S. Zhang, Y. Zhang, H. Wang, J. Mu, G. Wang, Z. Jiang, Dyes Pigments 79, 217 (2008)CrossRefGoogle Scholar
  20. 20.
    J.W. Fitch, V.S. Reddy, P.W. Youngman, G.A. Wohlfahrt, P.E. Cassidy, Polymer 41, 2301 (2000)CrossRefGoogle Scholar
  21. 21.
    J. Cao, W. Su, Z. Wu, T. Kitayama, K. Hatada, J. Appl. Polym. Sci. 59, 905 (2015)CrossRefGoogle Scholar
  22. 22.
    Y. Guo, S. Zhang, L. Yang, F. Li, W. Li, Y. Du, G. Wang, High Perform. Polym. 26, 703 (2014)CrossRefGoogle Scholar
  23. 23.
    S.V. Trukhanov, A.V. Trukhanov, V.A. Turchenko, V.G. Kostishyn, L.V. Panina, I.S. Kazakevich, A.M. Balagurov, J. Alloys Compd. 689, 383 (2016)CrossRefGoogle Scholar
  24. 24.
    O.S. Yakovenko, LYu. Matzui, L.L. Vovchenko, A.V. Trukhanov, I.S. Kazakevich, S.V. Trukhanov, Y.I. Prylutskyy, U. Ritter, J. Mater. Sci. 52, 5345 (2017)CrossRefGoogle Scholar
  25. 25.
    V.A. Turchenko, S.V. Trukhanov, A.M. Balagurov, V.G. Kostishyn, A.V. Trukhanov, L.V. Panina, E.L. Trukhanova, J. Magn. Magn. Mater. 464, 139 (2018)CrossRefGoogle Scholar
  26. 26.
    O.S. Yakovenko, LYu. Matzui, L.L. Vovchenko, O.V. Lozitsky, O.I. Prokopov, O.A. Lazarenko, A.V. Zhuravkov, V.V. Oliynyk, V.L. Launets, S.V. Trukhanov, A.V. Trukhanov, Mol. Cryst. Liq. Cryst. 661, 68 (2018)CrossRefGoogle Scholar
  27. 27.
    Y. Zhang, H. Jiang, J. Liu, C. Zhao, H. Na, J. Appl. Polym. Sci. 135, 46857 (2018)CrossRefGoogle Scholar
  28. 28.
    T. Endo, Macromolecules 27, 3447 (1994)CrossRefGoogle Scholar
  29. 29.
    S. Matsumura, N. Kihara, T. Takata, Macromolecules 34, 2848 (2001)CrossRefGoogle Scholar
  30. 30.
    Y. Sasada, Y. Shibasaki, M. Suzuki, M. Ueda, Polymer 44, 355 (2003)CrossRefGoogle Scholar
  31. 31.
    J. Zhu, K. Shao, G. Zhang, C. Zhao, Y. Zhang, H. Li, M. Han, H. Lin, D. Xu, H. Yu, H. Na, Polymer 51, 3047 (2010)CrossRefGoogle Scholar
  32. 32.
    P.A. Kohl, Annu. Rev. Chem. Biomol. Eng. 2, 379 (2011)CrossRefGoogle Scholar
  33. 33.
    Y. Zhang, B. Liu, Y. Zhang, Y. Na, Z. Jiang, Polym. Bull. 61, 699 (2008)CrossRefGoogle Scholar
  34. 34.
    J.E. Douglas, Z.Y. Wang, Macromol. Rapid Commun. 17, 795 (1996)CrossRefGoogle Scholar
  35. 35.
    Z.Y. Wang, A.L. Guen, Macromolecules 28, 3728 (1995)CrossRefGoogle Scholar
  36. 36.
    H. Wen, P. Wang, S. Cheng, T. Yan, M. Cai, High Perform. Polym. 27, 705 (2015)CrossRefGoogle Scholar
  37. 37.
    F. Mercer, T. Goodman, J. Wojtowicz, D. Duff, J. Polym Sci. A 30, 1767 (1992)CrossRefGoogle Scholar
  38. 38.
    F.W. Harris, S.L. Hsu, High Perform. Polym. 1, 3 (1989)CrossRefGoogle Scholar
  39. 39.
    B. Liu, Y. Dai, G.P. Robertson, M.D. Guiver, W. Hu, Z. Jiang, Polymer 46, 11279 (2005)CrossRefGoogle Scholar
  40. 40.
    B. Liu, W. Hu, C. Chen, Z. Jiang, W. Zhang, Z. Wu, T. Matsumoto, Polymer 45, 3241 (2004)CrossRefGoogle Scholar
  41. 41.
    Y. Niu, X. Zhu, L. Liu, Y. Zhang, G. Wang, Z. Jiang, React. Funct. Polym. 66, 559 (2006)CrossRefGoogle Scholar
  42. 42.
    Z. Liu, X. Li, K. Shen, P. Feng, Y. Zhang, X. Xu, W. Hu, Z. Jiang, J. Mater. Chem. A 1, 6481 (2013)CrossRefGoogle Scholar
  43. 43.
    G. Hougham, G. Tesoro, J. Shaw, Macromolecules 27, 3642 (1994)CrossRefGoogle Scholar
  44. 44.
    S.H. Hsiao, C.P. Yang, S.C. Huang, J. Polym. Sci. A 42, 2377 (2004)CrossRefGoogle Scholar
  45. 45.
    S. Zhang, Y. Li, T. Ma, J. Zhao, X. Xu, F. Yang, X. Xiang, Polym. Chem. 1, 485 (2010)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.College of ScienceShenyang Agricultural UniversityShenyangChina
  2. 2.College of ChemistryLiaoning UniversityShenyangChina

Personalised recommendations