Optical and thermal quenching properties of Al-doped Ba1.98SiO4:0.02Eu2+ phosphor synthesized with different Si3N4/SiO2 ratio
- 29 Downloads
An intense emission green color phosphor of Al-doped Ba1.98SiO4:0.02Eu2+ synthesized with different Si3N4/SiO2 ratio was prepared by conventional sintering method. The X-ray diffraction patterns, the photoluminescence, scanning micrograph and thermal quenching properties of Ba1.98SiO4:0.02Eu2+ with different Si3N4/SiO2 ratio were investigated in detail. As the Si3N4/SiO2 ratio increases, the emission intensity enhanced gradually until the optimum Si3N4/SiO2 ratio reached 3/2. The PL intensity with Si3N4/SiO2 = 3/2 is about four times of the initial intensity of Ba1.98SiO4:0.02Eu2+ phosphor and the reason was discussed clearly. Furthermore, when we introduced Al3+ ions into the host, the samples exhibited outstanding optical properties and smaller thermal quenching behavior compared with Ba1.98SiO4:0.02Eu2+ phosphor. The emission intensity of Ba1.98Si1−xAlxO4:0.02Eu2+ series increased until x reached 7% and the emission intensity of x = 0.07 is 5 times of the originated intensity of Ba1.98SiO4:0.02Eu2+ synthesized without Si3N4. The smaller thermal quenching behavior of Al-doped phosphors was studied clearly, too. All the results suggested that Al-doped Ba1.98SiO4:0.02Eu2+ phosphor synthesized with Si3N4/SiO2 = 3/2 can be a candidate green phosphor for WLEDs.
This work is supported by the National Natural Science Foundation of China (Nos. 11704043, 51702378) and the Special Foundation for theoretical physics Research Program of China (Nos. 11747113, 11747117).
- 7.R.J. Xie, N. Hirosaki, M. Mitomo, K. Takahashi, K. Sakuma, Highly efficient white-light-emitting diodes fabricated with short-wavelength yellow oxynitride phosphors. Appl. Phys. Lett. 88, 101–104 (2006)Google Scholar
- 16.J. Li, L. Xu, T. Wang, Fold EQE improvement up to 6.27% of solution-processed all-inorganic perovskite CsPbBr3 QLEDs via surface ligand density control. Adv Mater. 29(5), (2017)Google Scholar
- 17.T.C. Liu, B.M. Cheng, S.F. Hu, Highly stable red oxynitride β-SiAlON:Pr3+ phosphor for light-emitting diodes. Cheminform 42:44, (2011)Google Scholar
- 18.O. Yamamoto, M. Ishida, Y. Saitoh, Influence of Mg2+ on the formation of β-SiAlON by the carbothermal reduction-nitridation of homogeneous gel. Inorg. Chem. 3(3), 715–719 (2001)Google Scholar
- 21.K.A. Denault, J. Brgoch, M.W. Gaultois, A. Mikhailovsky, R. Petry, H. Winkler, S.P. DenBaars, R. Seshadri, Consequences of optimal bond valence on structural rigidity and improved luminescence properties in SrxBa2–xSiO4:Eu2+ orthosilicate phosphors. Chem. Mater. 26, 2275–2282 (2014)CrossRefGoogle Scholar
- 25.L. Litian, N. Lixin, Z. Rongfu, J. Chunyan, P. Mingying, H. Yucheng, C. Jun, H. Yan, T. Ye, H. Liang, Site occupation and photoluminescence properties of Ce3+ in Sr4Ca4La2 (PO4)6O2: experiments and ab initio calculations. Opt. Mater. 57, 7090–7096 (2018)Google Scholar
- 35.L. Zhichao, Z. Lei, C. Wenbo, F. Xiaotong, Y. Xiuxia, Q. Jianbei, X. Xuhui, Multiple anti-counterfeiting realized in NaBaScSi2O7 with a single activator of Eu2+. J. Mater. Chem. C. 6, 11137–11143 (2018)Google Scholar
- 37.C.R. Ronda, Luminescence: from theory to applications. Wiley, New York (2008)Google Scholar
- 38.S. Shigeo, M. William, Phosphor handbook. (1998)Google Scholar
- 40.C.L. Wang, Y.H. Jin*, Y. Lv, G.F. Ju, D. Liu, L. Chen, Z.Z. Li, Y.H. Hu, Trap distribution tailoring guided design of a super-long persistent phosphor Ba2SiO4:Eu2+, Ho3+ and photostimulable luminescence for optical information storage, J. Mater. Chem. C, 22, (2018)Google Scholar