Ion transport dynamics in ionic liquid incorporated CuBTC–metal-organic framework based composite polymer electrolyte

  • Rituraj Dutta
  • Ashok KumarEmail author
Article
  • 93 Downloads

Abstract

Cu based metal-organic framework (MOF), copper 1,3,5-benzenetricarboxylate (CuBTC) has been incorporated with ionic liquid (IL) 1-butyl-3 methylimidazolium bromide at different wt% to be used as composite nanofiller in poly (ethylene oxide) polymer electrolyte system. Shifting of carboxylate vibrational modes is observed from FTIR and significant changes of binding energies of Cu spin–orbit peaks are obtained from XPS spectra suggesting strong interaction between Cu metal cluster of MOF and Br anions of the IL. Oscillation periodicity and local coordination structure of Cu K-edge are investigated in k-space and R-space from the scanning XANES and EXAFS spectra. Dielectric modulus spectra show non-Debye relaxation dynamics and optimum ionic conductivity of 5 × 10−3 S cm−1 is obtained for the nanocomposite containing 50 wt% IL at 380 K. The frequency dependent AC conductivity curves depict ion concentration and temperature independent scaling behavior by collapsing to a single curve. The electrochemical stability and cycling performance increases with increasing IL concentration and attains electrochemical stability of 6.1 V with discharge capacity of 152.5 mAh/g after 500 cycles at 50 wt% of IL.

Notes

Acknowledgements

The authors sincerely acknowledge the financial support from DST-INSPIRE (Grant No: DST/INSPIRE Fellowship/2015/IF150994), Govt. of India. Authors convey their sincere thanks to Professor S. N. Jha and Chandrani Nayak, Raja Raman Centre for Advanced Technology, Indore, India for supporting synchrotron beamline facility to carry on Scanning EXAFS and XANES experiments. Authors are also thankful to SAIF-NEIST, Jorhat for their support to carry on the XPS measurements.

References

  1. 1.
    S.J. Dalgarno, P.K. Thallapally, L.J. Barbour, J.L. Atwood, Chem. Soc. Rev. 36(2), 236 (2007)Google Scholar
  2. 2.
    J.A. Bohrmanand, M.A. Carreon, Chem. Commun. 48(42), 5130 (2012)Google Scholar
  3. 3.
    A.A. Talin, A. Centrone, A.C. Ford, M.E. Foster, V. Stavila, P. Haney, A. Kinney, V. Szalai, F. El Gabaly, H.P. Yoon, F. Léonard, M.D. Allendorf, Science 343, 66 (2014)Google Scholar
  4. 4.
    K.R. Seddon, Chem. Technol. Biotechnol. 68(4), 351 (1997)Google Scholar
  5. 5.
    K. Fujie, K. Otsubo, R. Ikeda, T. Yamada, H. Kitagaw, Chem. Sci. 6, 4306 (2015)Google Scholar
  6. 6.
    Y. Chen, Z. Hu, M.K. Gupta, J. Jiang, J. Phys. Chem. C 115(44), 21736 (2011)Google Scholar
  7. 7.
    C. Prestipino, L. Regli, J.G. Vitillo, F. Bonino, A. Damin, C. Lamberti, A. Zecchina, P.L. Solari, K.O. Kongshaug, S. Bordiga, Chem. Mater. 18, 1337 (2006)Google Scholar
  8. 8.
    L. Sciortino, A. Alessi, F. Messina, G. Buscarino, F.M. Gelardi, J. Phys. Chem. C 119, 7826 (2015)Google Scholar
  9. 9.
    X. Sang, J. Zhang, J. Xiang, J. Cui, L. Zheng, J. Zhang, Z. Wu, Z. Li, G. Mo, Y. Xu, J. Song, C. Liu, X. Tan, T. Luo, B. Zhang, B. Han, Nat. Commun. 8, 1 (2017)Google Scholar
  10. 10.
    F.L. Morel, S. Pin, T. Huthwelker, M. Ranocchiari, J.A. van Bokhoven, Phys. Chem. Chem. Phys. 17, 3326 (2015)Google Scholar
  11. 11.
    W. Lu, X. Wu, New J. Chem. 42, 3180 (2018)Google Scholar
  12. 12.
    Y. Sun, H. Huang, H. Vardhan, B. Aguila, C. Zhong, J.A. Perman, A.M. Al-Enizi, A. Nafady, S. Ma, ACS Appl. Mater. Interfaces (2018) (in press)Google Scholar
  13. 13.
    E. Quartarone, P. Mustarelli, Chem. Soc. Rev. 40, 2525 (2011)Google Scholar
  14. 14.
    P.V. Wright, Br. Polym. J. 7(5), 319 (1975)Google Scholar
  15. 15.
    A.R. Polu, H.W. Rhee, Int. J. Hydrog. Energy 42(10), 7212 (2017)Google Scholar
  16. 16.
    A. Hofmann, M. Schulz, T. Hanemann, Electrochim. Acta 89, 823 (2013)Google Scholar
  17. 17.
    W. Wieczorek, Z. Florjanczyk, J.R. Stevens, Electrochim. Acta 40, 2251 (1995)Google Scholar
  18. 18.
    C. Liquan, Materials for Solid State Batteries (World Scientific, Singapore, 1986)Google Scholar
  19. 19.
    F. Croce. G.B. Appetecchi, L. Persi, B. Scrosati, Nature 394, 456 (1998)Google Scholar
  20. 20.
    C. Gerbaldi, J.R. Nair, A.M. Kulandainathan, R.S. Kumar, C. Ferrara, P. Mustarelli, A.M. Stephan, J. Mater. Chem. A 2, 9948 (2014)Google Scholar
  21. 21.
    L. Brinda, K.S. Rajan, J.B.B. Ryappan, J. Appl. Sci. 12, 1778 (2012)Google Scholar
  22. 22.
    Y. Yang, P. Shukla, S. Wang, V. Rudolph, X.-M. Chen, Z. Zhu, RSC Adv. 3, 17065 (2013)Google Scholar
  23. 23.
    M.K. Trivedi, S. Patil, H. Shettigar, K. Bairwa, S. Jana, Pharm. Anal. Acta 6(7), 1000395 (2015)Google Scholar
  24. 24.
    N.R. Dhumal, M.P. Singh, J.A. Anderson, J. Kiefer, H.J. Kim, J. Phys. Chem. C 120(6), 3295 (2016)Google Scholar
  25. 25.
    I. Pucic, T. Jurkin, Radiat. Phys. Chem. 81(9), 1426 (2012)Google Scholar
  26. 26.
    A.S. Duke, E.A. Dolgopolova, R.P. Galhenage, S.C. Ammal, A. Heyden, M.D. Smith, D.A. Chen, N.B. Shustova, J. Phys. Chem. C 119, 27457 (2015)Google Scholar
  27. 27.
    Q. Luo, B. An, M. Ji, S.-E. Park, C. Hao, Y. Li, J. Porous Mater. 22(1), 247 (2015)Google Scholar
  28. 28.
    A.N. Papathanassiou, O. Mykhailiv, L. Echegoyen, I. Sakellis, M.E. Plonska-Brzezinska, J. Phys. D 49, 285305 (2016)Google Scholar
  29. 29.
    A. Kumar, R. Sharma, M. Suresh, M.K. Das, K.K. Kar, J. Elastomers Plast. 49(6), 513 (2017)Google Scholar
  30. 30.
    J. Hazarika, A. Kumar, Synth. Met. 198, 239 (2014)Google Scholar
  31. 31.
    V.K. Singh, R.K. Singh, J. Mater. Chem. C 3, 7305 (2015)Google Scholar
  32. 32.
    A.K. Nath, A. Kumar, Solid State Ionics 253, 8 (2013)Google Scholar
  33. 33.
    H. Yang, G.V. Zhuang, P.N. Ross, J. Power Sources 161(1), 573 (2006)Google Scholar
  34. 34.
    S. Sinha, S.K. Chatterjee, J. Ghosh, A.K. Meikap, J. Phys. D 47, 275301 (2014)Google Scholar
  35. 35.
    A.K. Jonscher, Nature 267, 673 (1977)Google Scholar
  36. 36.
    B. Roling, C. Martiny, K. Funke, J. Non-Cryst. Solids 249, 201 (1999)Google Scholar
  37. 37.
    A.K. Nath, A. Kumar, Ionics 20, 1711 (2014)Google Scholar
  38. 38.
    K. Funke, R.D. Banhatti, S. Bruckner, C. Cramer, C. Krieger, A. Mandanici, C. Martiny, I. Ross, Phys. Chem. Phys. 4(14), 3155 (2002)Google Scholar
  39. 39.
    A.N. Papathanassiou, I. Sakellis, J. Grammatikakis, Appl. Phys. Lett. 97, 041913 (2010)Google Scholar
  40. 40.
    C.H. Park, D.W. Kim, J. Prakash, Y.K. Sun, Solid State Ionics 159, 111 (2003)Google Scholar
  41. 41.
    G. Vijayakumar, S.N. Karthick, A.R. SathiyaPriya, S. Ramalingam, A. Subramania, J. Solid State Electrochem. 12(9), 1135 (2008)Google Scholar
  42. 42.
    P.F. Ortega, J.P.C. Trigueiro, G.G. Silva, R.L. Lavall, Electrochim. Acta 188, 809 (2016)Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Materials Research Laboratory, Department of PhysicsTezpur UniversityTezpurIndia

Personalised recommendations