Effects of Si/B ratios on glass structure, crystallization and dielectric properties of CaO–SiO2–B2O3 glasses

  • Jiao HanEmail author
  • Peijia Bai
  • Yiming ZengEmail author
  • Mingwei Li
Article
  • 8 Downloads

Abstract

The glass structure, crystallization and dielectric properties of CaO–SiO2–B2O3 glasses with varying Si/B ratios (with constant Si/Ca ratio) have been investigated in this work. The density experimental results of glasses showed that the densities increased firstly and then decreased with the increasing Si/B ratios. The molar volumes of glasses increased slightly while oxygen densities of glasses decreased with the increasing of Si/B ratios. The FT-IR results of glasses revealed that the amounts of BIV units decreased while the (SiO4) tetrahedron increased with the increasing Si/B ratios. The DSC showed that the glass transition temperature Tg increased from 743 to 757 °C with increasing Si/B ratio. The crystallization activation energies (E) for CaSiO3 and CaB2O4 first increased until Si/B = 2.1 and then decreased slightly with the increasing Si/B ratio. For glass–ceramics samples sintered at 820 °C, all samples had the crystalline phases of CaSiO3 and CaB2O4 phases. The glass–ceramics sample with Si/B = 1.5 had the lowest dielectric constant εr = 4.8.

Notes

Acknowledgements

This work was supported by the fund of the Basic Applied Research Foundation of Yunnan Province (Grant No. 2016FD125, 2016FB083), Key New Product Project of Yunnan Province (Grant No.2016BA009), Research Project of The National Key laboratory of Chinese academy of sciences (Grant No. KLIFMD201605).

References

  1. 1.
    Z. Qing, Mater. Lett. 212, 126 (2018)CrossRefGoogle Scholar
  2. 2.
    K. Manu, M.T. Sebastian, Ceram. Int. 42, 1210 (2016)CrossRefGoogle Scholar
  3. 3.
    C.C. Chiang, S.F. Wang, Y.R. Wang, Y.F. Hsu, J. Alloys Compd. 461, 612 (2008)CrossRefGoogle Scholar
  4. 4.
    H. Zhu, H. Zhou, M. Liu, P. Wei, G. Xu, G. Ning, J. Mater. Sci. 20, 1135 (2008)Google Scholar
  5. 5.
    T.H. Lee, S.H. Cho, T.G. Lee, H.T. Kim, I.K. You, S. Nahm, J. Am. Ceram. Soc. 2018, 101 (2018)Google Scholar
  6. 6.
    X. Luo, L. Ren, Y. Xia, Y. Hu, W. Gong, M. Cai, H. Zhou, Ceram. Int. 43, 6791 (2017)CrossRefGoogle Scholar
  7. 7.
    L. Ren, X. Luo, L. Hu, Q. Sun, Y. Xia, Y. Hu, W. Gong, H. Zhou, J. Eur. Ceram. Soc. 37, 619 (2017)CrossRefGoogle Scholar
  8. 8.
    Y. Lai, Y. Zeng, X. Tang, H. Zhang, J. Han, H. Su, RSC Adv. 6, 93722 (2016)CrossRefGoogle Scholar
  9. 9.
    J. Han, Y. Lai, Y. Xiang, S. Wu, Y. Zeng, H. Yang, Y. Mao, Y. Yang, RSC Adv. 7, 14709 (2017)CrossRefGoogle Scholar
  10. 10.
    J. Han, Y. Lai, Y. Xiang, S. Wu, Y. Xu, Y. Zeng, J. Chen, J. Liu, J. Mater. Sci. 28, 6131 (2017)Google Scholar
  11. 11.
    G.J. Mohini, N. Krishnamacharyulu, G.S. Baskaran, P.V. Rao, N. Veeraiah, Appl. Surf. Sci. 287, 46 (2013)CrossRefGoogle Scholar
  12. 12.
    S.C. Colak, I. Akyuz, F. Atay, J. Non-Cryst. Solids 432, 406 (2016)CrossRefGoogle Scholar
  13. 13.
    J.Z. Liu, X.F. Wu, N.X. Xu, Q.L. Zhang, H. Yang, J. Mater. Sci. 26, 8899 (2015)Google Scholar
  14. 14.
    J.-S. Park, Y. Kim, H. Shin, J.-H. Moon, W. Lim, J. Am. Ceram. Soc. 91, 3630 (2008)CrossRefGoogle Scholar
  15. 15.
    Y. Xiang, J. Han, Y. Lai, S. Li, S. Wu, Y. Xu, Y. Zeng, L. Zhou, Z. Huang, J. Mater. Sci. 28, 9911 (2017)Google Scholar
  16. 16.
    A. Gaddam, H.R. Fernandes, J.M.F. Ferreira, RSC Adv. 5, 41066 (2015)CrossRefGoogle Scholar
  17. 17.
    K. Singh, I. Bala, V. Kumar, Ceram. Int. 35, 3401 (2009)CrossRefGoogle Scholar
  18. 18.
    A. Winterstein-Beckmann, D. Möncke, D. Palles, E.I. Kamitsos, L. Wondraczek, J. Non-Cryst. Solids 405, 196 (2014)CrossRefGoogle Scholar
  19. 19.
    G. El-Damrawi, K. El-Egili, Physica B 299, 180 (2001)CrossRefGoogle Scholar
  20. 20.
    M. Sitarz, J. Non-Cryst. Solids 357, 1603 (2011)CrossRefGoogle Scholar
  21. 21.
    K. Rao, Structural Chemistry of Glasses, (Elsevier, Amsterdam, 2002Google Scholar
  22. 22.
    Y. Sun, Z. Zhang, Metall. Mater. Trans. B 46, 1549 (2015)CrossRefGoogle Scholar
  23. 23.
    M. Ren, X. Lu, L. Deng, P.H. Kuo, J. Du, PCCP 20, 14090 (2018)CrossRefGoogle Scholar
  24. 24.
    J.H. Jean, C.R. Chang, C.D. Lei, J. Am. Ceram. Soc. 87, 1244 (2004)CrossRefGoogle Scholar
  25. 25.
    C.R. Chang, J.H. Jean, J. Am. Ceram. Soc. 82, 1725 (1999)CrossRefGoogle Scholar
  26. 26.
    D.P. Mukherjee, S.K. Das, Ceram. Int. 40, 12459 (2014)CrossRefGoogle Scholar
  27. 27.
    T.Y. Liu, G.H. Chen, J. Song, C.L. Yuan, Ceram. Int. 39, 5553 (2013)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum MetalsKunming Institute of Precious MetalsKunmingPeople’s Republic of China

Personalised recommendations