, Volume 29, Issue 21, pp 18807–18814 | Cite as

High color rendering white light emission from single-phased Ca11(SiO4)4(BO3)2:Ce3+, Tb3+, Mn2+ phosphor for UV-based light emitting diodes

  • Jingshan Hou
  • Jinghui Liu
  • Jun Zou
  • Guoying Zhao
  • Yufeng Liu
  • Xiang-Fei Feng
  • Yongzheng Fang
Article
  • 39 Downloads

Abstract

A series of single-phased Ca11(SiO4)4(BO3)2:Ce3+, Tb3+, Mn2+ phosphors were prepared by conventional one-step reduction solid state reaction, and their luminescent properties were investigated. Red, green and blue light emission from Mn2+, Tb3+ and Ce3+ were well balanced in Ca11(SiO4)4(BO3)2 (abbreviated as CSB), and a white light emission was obtained with chromatic coordinate of (0.303, 0.309) under a 338 nm UV light excitation. Energy transfer processes from Ce3+ to Tb3+ and Ce3+ to Mn2+ in CSB were investigated and discussed. Finally, a white light emitting diode with high color rending index of Ra = 92.2 was fabricated by using a 365 nm UV chip with the optimized (Ca0.91Ce0.01Mn0.05Tb0.03)11(SiO4)4(BO3)2 phosphor.

Notes

Acknowledgements

This work is financially supported by the National Natural Science Foundation of China (NSFC) (Grant Numbers 51472162, 51672177, 61605115), the Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning (No. TP2014061 and TP2014062) and Shanghai Sailing Project (No. 15YF1411800).

References

  1. 1.
    D.W. Wen, H. Kato, M. Kobayashi, S. Yamamoto, M. Mitsuishi, M. Kakihana, J. Mater. Chem. C 5, 4578 (2017)CrossRefGoogle Scholar
  2. 2.
    A.J. Huang, Z.W. Yang, C.Y. Yu, Z.Z. Chai, J.B. Qiu, Z.G. Song, J. Phys. Chem. C 121, 5267 (2017)CrossRefGoogle Scholar
  3. 3.
    K.T. Bicanic, X.Y. Li, R.P. Sabatini, N. Hossain, C.F. Wang, F.J. Fan, H.Y. Liang, S. Hoogland, E.H. Sargent, ACS Photonics 3, 2243 (2016)CrossRefGoogle Scholar
  4. 4.
    C.H. Huang, W.R. Liu, T.M. Chen, J. Phys. Chem. C 114, 18698 (2010)CrossRefGoogle Scholar
  5. 5.
    C.H. Huang, P.J. Wu, J.F. Lee, T.M. Chen, J. Mater. Chem. 21, 10489 (2011)CrossRefGoogle Scholar
  6. 6.
    X.J. Zhang, L. Huang, F.J. Pan, M.M. Wu, J. Wang, Y. Chen, Q. Su, ACS Appl. Mater. Interfaces 6, 2709 (2014)CrossRefGoogle Scholar
  7. 7.
    Y.M. Zhu, L.Y. Cao, M.G. Brik, X.J. Zhang, L. Huang, T.T. Xuan, J. Wang, J. Mater. Chem. C 5, 6420 (2017)CrossRefGoogle Scholar
  8. 8.
    H.L. Shi, J. Chen, J.Q. Huang, Q.Q. Hu, Z.H. Deng, Y.G. Cao, X.Y. Yuan, Phys. Status Solidi A 211, 1596 (2014)CrossRefGoogle Scholar
  9. 9.
    H.J. Yang, G.S. Zhu, L. Yuan, C. Zhang, F.S. Li, H.R. Xu, A.B. Yu, J. Am. Ceram. Soc. 95, 49 (2012)CrossRefGoogle Scholar
  10. 10.
    S.N. Li, P. Huang, C. Cui, L. Wang, Y. Tian, Q.F. Shi, Appl. Phys. A 123, 271 (2017)CrossRefGoogle Scholar
  11. 11.
    V. Bachmann, C. Ronda, A. Meijerink, Chem. Mater. 21, 2077 (2009)CrossRefGoogle Scholar
  12. 12.
    C.H. Huang, T.M. Chen, J. Phys. Chem. C 115, 2349 (2011)CrossRefGoogle Scholar
  13. 13.
    P.H. Chuang, C.C. Lin, R.S. Liu, ACS Appl. Mater. Interfaces 6, 15379 (2014)CrossRefGoogle Scholar
  14. 14.
    Z.J. Wang, P.L. Li, Z.P. Yang, Q.L. Guo, G.Y. Dong, Ceram. Int. 40, 15283 (2014)CrossRefGoogle Scholar
  15. 15.
    Y.L. Jia, R. Pang, H.F. Li, W.Z. Sun, J.P. Fu, L.H. Jiang, S. Zhang, Q. Su, C.Y. Li, R.S. Liu, Dalton Trans. 44, 11399 (2015)CrossRefGoogle Scholar
  16. 16.
    J.S. Hou, W.Z. Jiang, Y.Z. Fang, F.Q. Huang, J. Mater. Chem. C 1, 5892 (2013)CrossRefGoogle Scholar
  17. 17.
    C.H. Huang, T.M. Chen, W.R. Liu, Y.C. Chiu, Y.T. Ye, S.M. Jang, ACS Appl. Mater. Interfaces 2, 259 (2010)CrossRefGoogle Scholar
  18. 18.
    S.A. Khan, H. Zhong, W.W. Ji, L.Y. Hao, H. Abadikhah, X. Xu, N.Z. Khan, S. Agathopoulos, ACS Omega 2, 6270 (2017)CrossRefGoogle Scholar
  19. 19.
    X. Chen, P.P. Dai, X.T. Zhang, C. Li, S. Lu, X.L. Wang, Y. Jia, Y.C. Liu, Inorg. Chem. 53, 3441 (2014)CrossRefGoogle Scholar
  20. 20.
    S.A. Khan, Z. Hao, W.W. Hu, L.Y. Hao, X. Xu, N.Z. Khan, S. Agathopoulos, J. Mater. Sci. 52, 10927 (2017)CrossRefGoogle Scholar
  21. 21.
    X.J. Zhang, J.B. Yu, J. Wang, C.B. Zhu, J.H. Zhang, R. Zou, B.F. Lei, Y.L. Liu, M.M. Wu, ACS Appl. Mater. Interfaces 7, 28122 (2015)CrossRefGoogle Scholar
  22. 22.
    G.G. Li, Y. Zhang, D.L. Geng, M.M. Shang, C. Peng, Z.Y. Cheng, J. Lin, ACS Appl. Mater. Interfaces 4, 296 (2012)CrossRefGoogle Scholar
  23. 23.
    M.X. Zhao, Z.J. Zhao, L.X. Yu, L.Q. Yang, J.B. Jiang, X. Li, G.H. Li, J. Mater. Sci.: Mater. Electron. 29, 1832 (2018)Google Scholar
  24. 24.
    S.P. Lee, C.H. Huang, T.S. Chan, T.M. Chen, ACS Appl. Mater. Interfaces 6, 7260 (2014)CrossRefGoogle Scholar
  25. 25.
    P. Wagatha, V. Weiler, P.J. Schmidt, W. Schnick, Chem. Mater. 30, 1755 (2018)CrossRefGoogle Scholar
  26. 26.
    Z.Q. Jiang, X.C. Yu, J. Gou, L. Duan, X.H. Su, G.E. Fan, Y. Duan, J. Mater. Sci.: Mater. Electron. 28, 3630 (2017)Google Scholar
  27. 27.
    G.G. Li, D.L. Geng, M.M. Shang, Y. Zhang, C. Peng, Z.Y. Cheng, J. Lin, J. Phys. Chem. C 115, 21882 (2011)CrossRefGoogle Scholar
  28. 28.
    L.H. Jiang, R. Pang, D. Li, W.Z. Sun, Y. Jia, H.F. Li, J.P. Fu, C.Y. Li, S. Zhang, Dalton Trans. 44, 17241 (2015)CrossRefGoogle Scholar
  29. 29.
    A.N. Guan, G.F. Wang, S.Y. Xia, X.G. Zhang, X.X. Hu, L.Y. Zhou, Y.B. Meng, C.Y. Yao, H.M. Pan, J. Electron. Mater. 46, 1451 (2016)CrossRefGoogle Scholar
  30. 30.
    L.L. W, B.K. Moon, S.H. Park, J.H. Kim, J.S. Shi, K.H. Kim, J.H. Jeong, RSC Adv. 6, 79317 (2016)CrossRefGoogle Scholar
  31. 31.
    Y.M. Zhu, L. Huang, R. Zou, J.H. Zhang, J.B. Yu, M.M. Wu, J. Wang, Q. Su, J. Mater. Chem. C 4, 5690 (2016)CrossRefGoogle Scholar
  32. 32.
    M.M. Shang, S.S. Liang, H.Z. Lian, J. Lin, Inorg. Chem. 56, 6131 (2017)CrossRefGoogle Scholar
  33. 33.
    Z. Xia, R.S. Liu, J. Phys. Chem. C 116, 15604 (2012)CrossRefGoogle Scholar
  34. 34.
    X.G. Zhang, M.L. Gong, Dalton Trans. 43, 2465 (2014)CrossRefGoogle Scholar
  35. 35.
    V.B. Mikhailik, H. Kraus, D. Wahl, M. Itoh, M. Koike, I.K. Bailiff, Phys. Rev. B 69, 205110 (2004)CrossRefGoogle Scholar
  36. 36.
    J.S. Hou, W.Z. Jiang, Y.Z. Fang, Y.M. Wang, X. Yin, F.Q. Huang, ECS J. Solid State Sci. Technol. 1, R57 (2012)CrossRefGoogle Scholar
  37. 37.
    G.X. Jiang, B.B. Yang, G.Y. Zhao, Y.F. Liu, J. Zou, H.T. Sun, H.Y. Ou, Y.Z. Fang, J.S. Hou, Opt. Mater. 83, 93 (2018)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  1. 1.School of Materials Science and EngineeringShanghai Institute of TechnologyShanghaiChina
  2. 2.School of ScienceShanghai Institute of TechnologyShanghaiChina
  3. 3.Department of Cardiology, Xinhua Hospital, School of MedicineShanghai Jiao Tong UniversityShanghaiChina

Personalised recommendations