Microwave dielectric properties of the (1 − x)(Mg0.97Zn0.03)(Ti0.97Sn0.03)O3–x(Ca0.8Na0.1Sm0.1)TiO3 ceramic system
- 61 Downloads
Microwave dielectric ceramics of (1 − x)(Mg0.97Zn0.03)(Ti0.97Sn0.03)O3–x(Ca0.8Na0.1Sm0.1)TiO3 (MZTS–CNST, 0.05 ≤ x ≤ 0.08) were fabricated by a conventional solid-state reaction method. The effects of the sintering temperature and composition on the phases, microstructures, and microwave dielectric properties were studied. A relatively low sintering temperature of 1325 °C is needed for the MZTS–CNST ceramic samples. The optional microwave dielectric properties were achieved at x = 0.08 with εr = 21.5, Q × f = 60,110 GHz, and a near-zero τf of 1.69 ppm/ °C.
This work was supported by the Foundation of Hubei Provincial Department of Education (No. Q20171009).
- 5.X.M. Xue, H.T. Yu, G.L. Xu, Phase composition and microwave dielectric properties of Mg-excess MgTiO3 ceramics. J. Mater. Sci. 24, 1287–1291 (2013)Google Scholar
- 11.L.X. Li, S. Li, T. Tian, X.S. Lyu, J. Ye, H. Sun, Microwave dielectric properties of (1 − x)MgTiO3-x(Ca0.6Na0.2Sm0.2)TiO3 ceramic system. J. Mater. Sci. 27, 1286–1292 (2016)Google Scholar
- 18.M. Guo, Y.X. Li, G. Dou, S.P. Gong, The effect of titanium compounds addition on the microwave dielectric properties of the ZnO-Nb2O5 ceramics for LTCC. J. Mater. Sci. 25, 4319–4325 (2014)Google Scholar
- 20.M. Guo, G. Dou, Y.X. Li, S.P. Gong, The improvement research on microwave dielectric properties of magnesium tungstate for LTCC. J. Mater. Sci. 26, 608–612 (2015)Google Scholar