Antibacterial activity of sustainable composites derived from epoxidized natural rubber/silver-substituted zeolite/poly(lactic acid) blends

  • Phruedsaporn Taranamai
  • Pranee PhinyocheepEmail author
  • Watanalai Panbangred
  • Mayura Janhom
  • Philippe Daniel
Materials for life sciences


Sustainable composites derived from epoxidized natural rubber (ENR)/silver-substituted zeolite (AgZ)/poly(lactic acid) (PLA) blends possessing antibacterial activity were reported. ENR, herein, acted as an antibacterial promoter providing more hydrophilicity to the composites and facilitating water diffusion. Two methodologies were used to prepare composites, including solution casting (S) as well as solution casting followed by roll milling (SR). Both composites were compared in terms of morphology, AgZ dispersion, water absorption, and antibacterial activity. The shift of Tg and tan δ toward lower temperature of PLA composites consistently confirmed the compatibility between ENR and PLA by DSC and DMA results, respectively. The good AgZ distribution was observed in composites-SR, as confirmed by SEM/EDX. The results of agar disk diffusion susceptibility test showed that PLA, AgZ/PLA, and even ENR/AgZ/PLA composites-S showed no or less inhibition zone; meanwhile, ENR/AgZ/PLA composites-SR showed the significant inhibition zone against both Escherichia coli and Staphylococcus aureus. Besides, the antibacterial activity of the composites was required at least 5 wt% of AgZ. More than 98% inhibition of S. aureus growth by the composites-SR was observed during 2–24 h of cultivation, whereas AgZ/PLA provided the highest inhibition of only 75% at 24 h of cultivation. Hence, the incorporation of ENR enhances the bactericidal activity of the composites. In terms of mechanical properties, incorporating ENR into the composites decreased tensile modulus and strength, but increased the impact strength significantly. Therefore, the developed composites could be promising materials in food and biomedical fields in which antibacterial and impact resistance properties are required.



Partial support from an ERASMUS + grant 2015-1-FR01-KA107-014841 between Mahidol University and Le Mans University is gratefully acknowledged. Teaching assistance scholarship of Faculty of Science, Mahidol University to M. Taranamai is very much appreciated.

Compliance with ethical standards

Conflicts of interest

The authors declare no conflicts of interest.


  1. 1.
    Kenawy E-R, Worley SD, Broughton R (2007) The chemistry and applications of antimicrobial polymers: a state-of-the-art review. Biomacromol 8:1359–1384. CrossRefGoogle Scholar
  2. 2.
    Francolini I, Donelli G, Stoodley P (2003) Polymer designs to control biofilm growth on medical devices. Rev Environ Sci Biotechnol 2:307–319. CrossRefGoogle Scholar
  3. 3.
    Imazato S (2003) Antibacterial properties of resin composites and dentin bonding systems. Dent Mater 19:449–457. CrossRefGoogle Scholar
  4. 4.
    Markarian J (2009) Antimicrobials find new healthcare applications. Plastic Addit Compd 11:18–22. Google Scholar
  5. 5.
    Appendini P, Hotchkiss JH (2002) Review of antimicrobial food packaging. Innov Food Sci Emerg Technol 3:113–126. CrossRefGoogle Scholar
  6. 6.
    Monteiro DR, Gorup LF, Takamiya AS, Ruvollo-Filho AC, Camargo E, Barbosa DB (2009) The growing importance of materials that prevent microbial adhesion: antimicrobial effect of medical devices containing silver. Int J Antimicrob Agents 34:103–110. CrossRefGoogle Scholar
  7. 7.
    Khare MD, Bukhari SS, Swann A, Spiers P, McLaren I, Myers J (2007) Reduction of catheter-related colonisation by the use of a silver zeolite-impregnated central vascular catheter in adult critical care. J Infect 54:146–150. CrossRefGoogle Scholar
  8. 8.
    Inoue Y, Hoshino M, Takahashi H et al (2002) Bactericidal activity of Ag–zeolite mediated by reactive oxygen species under aerated conditions. J Inorg Biochem 92:37–42. CrossRefGoogle Scholar
  9. 9.
    Quintavalla S, Vicini L (2002) Antimicrobial food packaging in meat industry. Meat Sci 62:373–380. CrossRefGoogle Scholar
  10. 10.
    Loertzer H, Soukup J, Hamza A et al (2006) Use of catheters with the AgION antimicrobial system in kidney transplant recipients to reduce infection risk. Transplant Proc 38:707–710. CrossRefGoogle Scholar
  11. 11.
    Rusin P, Bright K, Gerba C (2003) Rapid reduction of Legionella pneumophila on stainless steel with zeolite coatings containing silver and zinc ions. Lett Appl Microbiol 36:69–72. CrossRefGoogle Scholar
  12. 12.
    Cowan MM, Abshire KZ, Houk SL, Evans SM (2003) Antimicrobial efficacy of a silver-zeolite matrix coating on stainless steel. J Ind Microbiol Biotechnol 30:102–106. CrossRefGoogle Scholar
  13. 13.
    Galeano B, Korff E, Nicholson WL (2003) Inactivation of vegetative cells, but not spores, of Bacillus anthracis, B. cereus, and B. subtilis on stainless steel surfaces coated with an antimicrobial silver- and zinc-containing zeolite formulation. Appl Environ Microbiol 69:4329–4331CrossRefGoogle Scholar
  14. 14.
    Casemiro LA, Martins CHG, Pires-de-Souza F, Panzeri H (2008) Antimicrobial and mechanical properties of acrylic resins with incorporated silver–zinc zeolite—part I. Gerodontology 25:187–194. CrossRefGoogle Scholar
  15. 15.
    Abe Y, Ishii M, Takeuchi M, Ueshige M, Tanaka S, Akagawa Y (2004) Effect of saliva on an antimicrobial tissue conditioner containing silver–zeolite. J Oral Rehabil 31:568–573. CrossRefGoogle Scholar
  16. 16.
    Hotta M, Nakajima H, Yamamoto K, Aono M (1998) Antibacterial temporary filling materials: the effect of adding various ratios of Ag–Zn–Zeolite. J Oral Rehabil 25:485–489. CrossRefGoogle Scholar
  17. 17.
    Yeo SY, Lee HJ, Jeong SH (2003) Preparation of nanocomposite fibers for permanent antibacterial effect. J Mater Sci 38:2143–2147. CrossRefGoogle Scholar
  18. 18.
    Silver S (2003) Bacterial silver resistance: molecular biology and uses and misuses of silver compounds. FEMS Microbiol Rev 27:341–353. CrossRefGoogle Scholar
  19. 19.
    Yoshida CMP, Bastos CEN, Franco TT (2010) Modeling of potassium sorbate diffusion through chitosan films. LWT Food Sci Technol 43:584–589. CrossRefGoogle Scholar
  20. 20.
    Ouattara B, Simard RE, Piette G, Bégin A, Holley RA (2000) Diffusion of acetic and propionic acids from Chitosan-based antimicrobial packaging films. J Food Sci 65:768–773. CrossRefGoogle Scholar
  21. 21.
    Odani H, Uchikura M, Ogino Y, Kurata M (1983) Diffusion and solution of methanol vapor in poly(2-vinylpyridine)- block- polyisoprene and poly(2-vinylpyridine)-block-polystyrene. J Membr Sci 15:193–208. CrossRefGoogle Scholar
  22. 22.
    Ahmed J, Hiremath N, Jacob H (2017) Antimicrobial efficacies of essential oils/nanoparticles incorporated polylactide films against L. monocytogenes and S. typhimurium on contaminated cheese. Int J Food Prop 20:53–67. CrossRefGoogle Scholar
  23. 23.
    Fernández A, Soriano E, Hernández-Muñoz P, Gavara R (2010) Migration of antimicrobial silver from composites of polylactide with silver zeolites. J Food Sci 75:E186–E193. CrossRefGoogle Scholar
  24. 24.
    Pongtanayut K, Thongpin C, Santawitee O (2013) The effect of rubber on morphology, thermal properties and mechanical properties of PLA/NR and PLA/ENR blends. Energy Procedia 34:888–897. CrossRefGoogle Scholar
  25. 25.
    Zakaria Z, Islam MS, Hassan A et al (2013) Mechanical properties and morphological characterization of PLA/Chitosan/epoxidized natural rubber composites. Adv Mater Sci Eng. Google Scholar
  26. 26.
    Wang Y, Chen K, Xu C, Chen Y (2015) Supertoughened biobased poly(lactic acid)–epoxidized natural rubber thermoplastic vulcanizates: fabrication, co-continuous phase structure, interfacial in situ compatibilization, and toughening mechanism. J Phys Chem B 119:12138–12146. CrossRefGoogle Scholar
  27. 27.
    Jaratrotkamjorn R, Khaokong C, Tanrattanakul V (2012) Toughness enhancement of poly(lactic acid) by melt blending with natural rubber. J Appl Polym Sci 124:5027–5036. Google Scholar
  28. 28.
    Tham WL, Poh BT, Mohd Ishak ZA, Chow WS (2016) Epoxidized natural rubber toughened poly(lactic acid)/halloysite nanocomposites with high activation energy of water diffusion. J Appl Polym Sci. Google Scholar
  29. 29.
    Shameli K, Ahmad MB, Zargar M, Yunus WMZW, Ibrahim NA (2011) Fabrication of silver nanoparticles doped in the zeolite framework and antibacterial activity. Int J Nanomed 6:331–341. CrossRefGoogle Scholar
  30. 30.
    Phinyocheep P, Phetphaisit CW, Derouet D, Campistron I, Brosse JC (2005) Chemical degradation of epoxidized natural rubber using periodic acid: preparation of epoxidized liquid natural rubber. J Appl Polym Sci 95:6–15. CrossRefGoogle Scholar
  31. 31.
    Bradbury JH, Perera MCS (1985) Epoxidation of natural rubber studied by nmr spectroscopy. J Appl Polym Sci 30:3347–3364. CrossRefGoogle Scholar
  32. 32.
    Davey JE, Loadman MJR (1984) A chemical demonstration of the randomness of epoxidation of natural rubber. Brit Polym J 16:134–138. CrossRefGoogle Scholar
  33. 33.
    Burfield DR, Lim K-L, Law K-S, Ng S (1984) Analysis of epoxidized natural rubber. A comparative study of d.s.c., n.m.r., elemental analysis and direct titration methods. Polymer 25:995–998. CrossRefGoogle Scholar
  34. 34.
    Kourki H, Famili MHN, Mortezaei M, Malekipirbazari M (2018) Mixing challenges for SiO2/polystyrene nanocomposites. J Thermoplast Compos 31:709–726. CrossRefGoogle Scholar
  35. 35.
    Yuzay IE, Auras R, Selke S (2010) Poly(lactic acid) and zeolite composites prepared by melt processing: morphological and physical–mechanical properties. J Appl Polym Sci 115:2262–2270. CrossRefGoogle Scholar
  36. 36.
    Wang H, Sun X, Seib P (2001) Strengthening blends of poly(lactic acid) and starch with methylenediphenyl diisocyanate. J Appl Polym Sci 82:1761–1767. CrossRefGoogle Scholar
  37. 37.
    Shogren R (1997) Water vapor permeability of biodegradable polymers. J Environ Polym Degrad 5:91–95. CrossRefGoogle Scholar
  38. 38.
    Mat Uzir Wahit AH, Ibrahim AN, Zawawi NA, Kunasegeran K (2015) Mechanical, thremal, and chemical resistance of epoxidized natural rubber toughened polylactic acid blends. Sains Malays 44:1615–1623Google Scholar
  39. 39.
    Spriger G, Shen C (1976) Moisture absorption and desorption of composite materials. J Compos Mater 20:2–20Google Scholar
  40. 40.
    Kushwaha PK, Kumar R (2009) Studies on water absorption of bamboo-polyester composites: effect of silane treatment of mercerized bamboo. Polym Plast Technol Eng 49:45–52. CrossRefGoogle Scholar
  41. 41.
    Pötschke P, Krause B, Buschhorn ST et al (2013) Improvement of carbon nanotube dispersion in thermoplastic composites using a three roll mill at elevated temperatures. Compos Sci Technol 74:78–84. CrossRefGoogle Scholar
  42. 42.
    Jo Y, Garcia CV, Ko S et al (2018) Characterization and antibacterial properties of nanosilver-applied polyethylene and polypropylene composite films for food packaging applications. Food Biosci 23:83–90. CrossRefGoogle Scholar
  43. 43.
    Kim JS, Kuk E, Yu KN et al (2007) Antimicrobial effects of silver nanoparticles. Nanomedicine 3:95–101. CrossRefGoogle Scholar
  44. 44.
    Jokar M, Abdul Rahman R, Ibrahim NA, Abdullah LC, Tan CP (2012) Melt production and antimicrobial efficiency of low-density polyethylene (LDPE)-silver nanocomposite film. Food Bioprocess Tech 5:719–728. CrossRefGoogle Scholar
  45. 45.
    Cho K-H, Park J-E, Osaka T, Park S-G (2005) The study of antimicrobial activity and preservative effects of nanosilver ingredient. Electrochim Acta 51:956–960. CrossRefGoogle Scholar
  46. 46.
    Becaro AA, Puti FC, Correa DS, Paris EC, Marconcini JM, Ferreira MD (2015) Polyethylene films containing silver nanoparticles for applications in food packaging: characterization of physico-chemical and anti-microbial properties. J Nanosci Nanotechnol 15:2148–2156. CrossRefGoogle Scholar
  47. 47.
    Prapruddivongs C, Sombatsompop N (2012) Roles and evidence of wood flour as an antibacterial promoter for triclosan-filled poly(lactic acid). Compos B 43:2730–2737. CrossRefGoogle Scholar
  48. 48.
    Zhang C, Wang W, Huang Y et al (2013) Thermal, mechanical and rheological properties of polylactide toughened by expoxidized natural rubber. Mater Des 45:198–205. CrossRefGoogle Scholar
  49. 49.
    Nematollahi M, Jalali-Arani A, Modarress H (2019) High-performance bio-based poly(lactic acid)/natural rubber/epoxidized natural rubber blends: effect of epoxidized natural rubber on microstructure, toughness and static and dynamic mechanical properties. Polym Int 68:439–446. CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Department of Chemistry, Faculty of ScienceMahidol UniversityBangkokThailand
  2. 2.Department of Biotechnology and Mahidol University-Osaka, University Collaborative Research Center for Bioscience and Biotechnology (MU-OU: CRC), Faculty of ScienceMahidol UniversityBangkokThailand
  3. 3.Institut des Molécules et des Matériaux du Mans (IMMM) UMR CNRS 6283Le Mans UniversitéLe Mans Cedex 9France

Personalised recommendations