A piecewise constitutive model, microstructure and fracture mechanism of a nickel-based superalloy 750H during high-temperature tensile deformation
- 29 Downloads
In order to understand the high-temperature deformation behavior of a nickel-based superalloy, a range of tensile tests were carried out at 720, 750, and 780 °C with strain rates ranging from 5 × 10−5 to 5 × 10−3 s−1. A piecewise constitutive model was applied to describe the work hardening-dynamic recovery and dynamic flow softening behaviors. The predicted flow stresses have a good agreement with the experimental results. Microstructures in the fracture frontier of the ruptured specimens were analyzed to further understand the fracture mechanism. Twinning and dislocation structures were surveyed at the tested conditions. Twin structure decreased as temperature increased. These two precipitates were characterized: M23C6 carbide located in the grain boundary and spherical γ′ phase in the matrix. Precipitates, twin and dislocation structures are the dominant strengthening mechanism of the superalloy during high-temperature deformation. Orientations < 111 >//RD and < 001 >//RD were detected as the main texture structure. Cavities formed near the precipitates and triple grain boundary. On the basis of fracture surface observations, the 750H superalloy shows both intergranular and transgranular fracture mode in the tested conditions. The dimples became small and shallow as the strain rate increased.
This work was financially supported by the National Natural Science Foundation of China (51475326) and Demonstration Project of National Marine Economic Innovation (BHSF2017–22).
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 8.Wang J, Zhang YF, Ma JY, Li JX, Zhang Z (2017) Microcrack nucleation and propagation investigation of Inconel 740H alloy under in situhigh temperature tensile test. Acta Metall Sin 53:1627–1635Google Scholar
- 16.Lin F, Xie X, Zhao S (2011) Selection of superalloys for superheater tubes of domestic 700 A-USC boilers. J Chin Soc Power Eng 31:960–968Google Scholar
- 18.Blum R, Vanstone RW (2003) Materials development for boilers and steam turbines operating at 700°C. In: Proceedings of the 6th international Charles Parsons turbine conference, Dublin, IrelandGoogle Scholar
- 19.Shingledecker J, Purgert R, Rawls P (2013) Current status of the U.S. DOE/OCDO A-USC materials technology research and development program. In: Proceedings from the 7th international conference on advances in materials technology for fossil power plants, Hawaii, USAGoogle Scholar
- 20.Fukuda M (2013) Advanced USC technology development in Japan. In: Proceedings from the 7th international conference on advances in materials technology for fossil power plants, Hawaii, USAGoogle Scholar
- 21.Liu ZD, Bao HS, Yang G, Xu SQ, Wang QJ (2013) Material advancement used for 700°C A-USC-PP in China. In: Proceedings from the 7th international conference on advances in materials technology for fossil power plants, Hawaii, USAGoogle Scholar
- 46.Rai K, Tripathy HP, Hajra RN, Raju S, Saibaba S, Jayakumar T (2016) Measurement of high temperature phase stability and thermophysical properties of alloy 740. Mater Sci Technol 32(5):488–497Google Scholar