Ionic liquid-based amphiphilic conetwork with mechanical toughness: a promising candidate for dye removal

  • Wenqi Song
  • Liwei Qian
  • Bo Gao
  • Yanfang Zhu
  • Min Zhu
  • Yuzhen Zhao
  • Huaping Ren
  • Zongcheng Miao
Chemical routes to materials
  • 6 Downloads

Abstract

Hydrogels have been widely used in water treatment materials due to their intriguing three-dimensional cross-linked networks and a large number of functional groups. However, conventional chemically cross-linked hydrogels inevitably face severe problems such as insufficient adsorption performance and poor mechanical property. Here, a novel ionic liquid (IL)-based amphiphilic conetwork (APILCN) with homogeneous network and good adsorption capacity and mechanical strength was developed for the efficient treatment of anionic dye. The strategy was based on one-pot step polymerization of “A3 + B3” via N-alkylation reaction of a bromo-terminated A3-type amphiphilic macromonomer and an imidazole-terminated B3-type monomer. Under the optimum conditions, the maximum adsorption capacity of APILCN toward bromophenol blue (BPB) could reach ~ 397 mg g−1 with a good mechanical strength of 2.44 MPa at the compressive strain of 60%. The excellent adsorption and mechanical property are attributed to the exposed IL functional groups and the homogeneous network structure, respectively. Furthermore, Freundlich and Langmuir model for the isothermal study of APILCN demonstrated that BPB adsorption mechanism varied with the different chemical structures of A3 macromonomer, and the kinetic study revealed that the adsorption of BPB followed the pseudo-second-order kinetic model. In addition, APILCN was capable of selectively separating anionic dye and could remain 93.2% of the initial saturation adsorption capacity after five adsorption–desorption cycles. These results indicated that such APILCN was qualified for the work as efficient and stable adsorbents and, more importantly, the structure of APILCN might accelerate the application of the hydrogels in diverse fields.

Notes

Acknowledgements

This work was supported by National Natural Science Foundation of China (CN) (Nos. 21805177, 51673157), Natural Science Foundation of Shaanxi Province (CN) (Nos. 2017JQ2019, 2018JQ2035) and Science Research Foundation of Xijing University (XJ18T03).

Compliance with ethical standards

Conflict of interest

The authors declare that they have no competing interests.

Supplementary material

10853_2019_3328_MOESM1_ESM.pdf (1.3 mb)
Supplementary material 1 (PDF 1312 kb)

References

  1. 1.
    Sharma K, Dalai AK, Vyas RK (2017) Removal of synthetic dyes from multicomponent industrial wastewaters. Rev Chem Eng 34(1):107–134Google Scholar
  2. 2.
    Ren H, Tian S, Zhu M, Zhao Y, Li K, Ma Q, Ding S, Gao J et al (2018) Modification of montmorillonite by Gemini surfactants with different chain lengths and its adsorption behavior for methyl orange. Appl Clay Sci 151:29–36Google Scholar
  3. 3.
    Nidheesh PV, Zhou M, Oturan MA (2018) An overview on the removal of synthetic dyes from water by electrochemical. Chemosphere 197:210–227Google Scholar
  4. 4.
    Yang S, Niu C, Huang D, Zhang H, Liang C, Zeng G (2017) SrTiO3 nanocubes decorated with Ag/AgCl nanoparticles as photocatalysts with enhanced visible-light photocatalytic activity towards the degradation of dyes, phenol and bisphenol A. Environ Sci Nano 4:585–595Google Scholar
  5. 5.
    Li F, Xia Q, Gao Y, Cheng Q, Ding L, Yang B, Tian Q, Ma C et al (2018) Anaerobic biodegradation and decolorization of a refractory acid dye by a forward osmosis membrane bioreactor. Environ Sci Water Res Technol 4(2):272–280Google Scholar
  6. 6.
    Ji K, Xu H, Ma X, Yin J, Jiang X, Aastrup T (2017) Hyperbranched poly(ether amine)@poly(vinylidene fluoride) (hPEA@PVDF) porous membranes for selective adsorption and molecular filtration of hydrophilic dyes. J Mater Chem A 5:10470–10479Google Scholar
  7. 7.
    Liu J, Su D, Yao J, Huang Y, Shao Z, Chen X (2017) Soy protein-based polyethylenimine hydrogel and its high selectivity for copper ions removal in wastewater treatment. J Mater Chem A 5:4163–4171Google Scholar
  8. 8.
    Huang H, Hou L, Zhu F, Li J, Xu M (2018) Controllable thermal and pH responsive behavior of PEG based hydrogels and applications for dye adsorption and release. RSC Adv 8(17):9334–9343Google Scholar
  9. 9.
    Qian W, Texter J, Yan F (2017) Frontiers in poly(ionic liquid)s: syntheses and applications. Chem Soc Rev 46(4):1124–1159Google Scholar
  10. 10.
    Zhang S, Yang M, Qian L, Hou C, Tang R, Yang J, Wang X (2018) Design and preparation of a cellulose-based adsorbent modified by imidazolium ionic liquid functional groups and their studies on anionic dye adsorption. Cellulose 25(6):3557–3569Google Scholar
  11. 11.
    Chen L, Huang X (2017) Preparation and application of poly (ionic liquid)-based molecularly imprinted polymer for multiple monolithic fiber solid-phase microextraction of phenolic acids in fruit juice and beer samples. Analyst 142:4039–4047Google Scholar
  12. 12.
    Li K, Qian L, Song W, Zhu M, Zhao Y, Miao Z (2018) Preparation of an ionic liquid-based hydrogel with hyperbranched topology for efficient removal of Cr(VI). J Mater Sci 53(20):14821–14833.  https://doi.org/10.1007/s10853-018-2609-5 Google Scholar
  13. 13.
    Song W, Liu Y, Qian L, Niu L, Xiao L, Hou Y, Wang Y, Fan X (2016) Hyperbranched polymeric ionic liquid with imidazolium backbones for highly efficient removal of anionic dyes. Chem Eng J 287:482–491Google Scholar
  14. 14.
    Yu Y, De Andrade LCX, Fang L, Ma J, Zhang W, Tang Y (2015) Graphene oxide and hyperbranched polymer-toughened hydrogels with improved absorption properties and durability. J Mater Sci 50(9):3457–3466.  https://doi.org/10.1007/s10853-015-8905-4 Google Scholar
  15. 15.
    Yu X, Qin Z, Wu H, Lv H, Yang X (2018) pH-driven preparation of small, non-aggregated micelles for ultra-stretchable and tough hydrogels. Chem Eng J 342(15):357–363Google Scholar
  16. 16.
    Malkoch M, Vestberg R, Gupta N, Mespouille L, Dubois P, Mason AF, Hedrick JL, Liao Q et al (2006) Synthesis of well-defined hydrogel networks using Click chemistry. Chem Commun 26:2774–2776Google Scholar
  17. 17.
    Sakai T, Matsunaga T, Yamamoto Y, Ito C, Yoshida R, Suzuki S, Sasaki N, Shibayama M et al (2008) Design and fabrication of a high-strength hydrogel with ideally homogeneous network structure from tetrahedron-like macromonomers. Macromolecules 41(14):5379–5384Google Scholar
  18. 18.
    Zhang S, Chen H, Kong J (2016) Disulfide bonds-containing amphiphilic conetworks with tunable reductive-cleavage. RSC Adv 6(43):36568–36575Google Scholar
  19. 19.
    Ramazani A, Dabbaghi A, Gouranlou F (2018) Synthesis of amphiphilic co-network through click chemistry reactions: a review. Curr Org Chem 22(4):362–369Google Scholar
  20. 20.
    Jutrzenka Trzebiatowska P, Santamaria Echart A, Calvo Correas T, Eceiza A, Datta J (2018) The changes of crosslink density of polyurethanes synthesised with using recycled component. Chemical structure and mechanical properties investigations. Prog Org Coat 115:41–48Google Scholar
  21. 21.
    Deng S, Xu H, Jiang X, Yin J (2013) Poly(vinyl alcohol) (PVA)-enhanced hybrid hydrogels of hyperbranched poly(ether amine) (hPEA) for selective adsorption and separation of dyes. Macromolecules 46(6):2399–2406Google Scholar
  22. 22.
    Eatemadi A, Daraee H, Aiyelabegan HT, Negahdari B, Rajeian B, Zarghami N (2016) Synthesis and characterization of chrysin-loaded PCL-PEG-PCL nanoparticle and its effect on breast cancer cell line. Biomed Pharmacother 84:1915–1922Google Scholar
  23. 23.
    Moumene T, Belarbi EH, Haddad B, Villemin D, Abbas O, Khelifa B, Bresson S (2015) Study of imidazolium dicationic ionic liquids by Raman and FTIR spectroscopies: the effect of the nature of the anion. J Mol Struct 1083:179–186Google Scholar
  24. 24.
    Truong V, Blakey I, Whittaker AK (2012) Hydrophilic and amphiphilic polyethylene glycol-based hydrogels with tunable degradability prepared by “Click” chemistry. Biomacromol 13(12):4012–4021Google Scholar
  25. 25.
    Fodor C, Kali G, Thomann R, Thomann Y, Iván B, Mülhaupt R (2017) Nanophasic morphologies as a function of the composition and molecular weight of the macromolecular cross-linker in poly(N-vinylimidazole)-l-poly(tetrahydrofuran) amphiphilic conetworks: bicontinuous domain structure in broad composition ranges. RSC Adv 7(12):6827–6834Google Scholar
  26. 26.
    Yang Q, Lin CX, Liu FH, Li L, Zhang QG, Zhu AM, Liu QL (2018) Poly(2,6-dimethyl-1,4-phenylene oxide)/ionic liquid functionalized graphene oxide anion exchange membranes for fuel cells. J Membr Sci 552:367–376Google Scholar
  27. 27.
    Win P, Lin C, Long Y, Chen W, Chen G, Song Y (2018) Covalently cross-linked layered double hydroxide nanocomposite hydrogels with ultrahigh water content and excellent mechanical properties. Chem Eng J 335(1):409–415Google Scholar
  28. 28.
    Obukhov SP, Rubinstein M, Colby RH (1994) Network modulus and superelasticity. Macromolecules 27(12):3191–3198Google Scholar
  29. 29.
    Kamata H, Akagi Y, Kayasuga-Kariya Y, Chung U, Sakai T (2014) “Nonswellable” hydrogel without mechanical hysteresis. Science 343(6173):873–875Google Scholar
  30. 30.
    Dhanalakshmi J, Pathinettam Padiyan D (2017) Photocatalytic degradation of methyl orange and bromophenol blue dyes in water using sol–gel synthesized TiO2 nanoparticles. Mater Res Express 4(9):095020.  https://doi.org/10.1088/2053-1591/aa85fd Google Scholar
  31. 31.
    Bouanimba N, Zouaghi R, Laid N, Sehili T (2011) Factors influencing the photocatalytic decolorization of Bromophenol blue in aqueous solution with different types of TiO2 as photocatalysts. Desalination 275(1–3):224–230Google Scholar
  32. 32.
    Qian L, Yang M, Zhang S, Hou C, Song W, Yang J, Tang R (2018) Preparation of a sustainable bioadsorbent by modifying filter paper with sodium alginate, with enhanced mechanical properties and good adsorption of methylene blue from wastewaters. Cellulose 25:2021–2036Google Scholar
  33. 33.
    Malana MA, Ijaz S, Ashiq MN (2010) Removal of various dyes from aqueous media onto polymeric gels by adsorption process: their kinetics and thermodynamics. Desalination 263(1–3):249–257Google Scholar
  34. 34.
    El-Zahhar AA, Awwad NS, El-Katori EE (2014) Removal of bromophenol blue dye from industrial waste water by synthesizing polymer-clay composite. J Mol Liq 199:454–461Google Scholar
  35. 35.
    Dhananasekaran S, Palanivel R, Pappu S (2016) Adsorption of methylene blue, bromophenol blue, and coomassie brilliant blue by α-chitin nanoparticles. J Adv Res 7(1):113–124Google Scholar
  36. 36.
    You L, Wu Z, Kim T, Lee K (2006) Kinetics and thermodynamics of bromophenol blue adsorption by a mesoporous hybrid gel derived from tetraethoxysilane and bis(trimethoxysilyl)hexane. J Colloid Interf Sci 300(2):526–535Google Scholar
  37. 37.
    Sohni S, Gul K, Ahmad F, Ahmad I, Khan A, Khan N, Bahadar Khan S (2018) Highly efficient removal of acid red-17 and bromophenol blue dyes from industrial wastewater using graphene oxide functionalized magnetic chitosan composite. Polym Compos 39(9):3317–3328Google Scholar
  38. 38.
    Chen J, Pu Y, Wang C, Han J, Zhong Y, Liu K (2018) Synthesis of a novel nanosilica-supported poly β-cyclodextrin sorbent and its properties for the removal of dyes from aqueous solution. Colloids Surf A 538:808–817Google Scholar
  39. 39.
    Ghaedi M, Ghaedi AM, Negintaji E, Ansari A, Vafaei A, Rajabi M (2014) Random forest model for removal of bromophenol blue using activated carbon obtained from Astragalus bisulcatus tree. J Ind Eng Chem 20(4):1793–1803Google Scholar
  40. 40.
    Liu J, Yao S, Wang L, Zhu W, Xu J, Song H (2014) Adsorption of bromophenol blue from aqueous samples by novel supported ionic liquids. J Chem Technol Biot 89(2):230–238Google Scholar
  41. 41.
    Yan J, Huang Y, Miao Y, Tjiu WW, Liu T (2015) Polydopamine-coated electrospun poly(vinyl alcohol)/poly(acrylic acid) membranes as efficient dye adsorbent with good recyclability. J Hazard Mater 283:730–739Google Scholar
  42. 42.
    Swat AAA, Saleh TA, Ganiyu SA, Siddiqui MN, Alhooshani KR (2017) Preparation of activated carbon, zinc oxide and nickel oxide composites for potential application in the desulfurization of model diesel fuels. J Anal Appl Pyrol 128:246–256Google Scholar
  43. 43.
    Wang C, Zhang J, Wang P, Wang H, Yan H (2015) Adsorption of methylene blue and methyl violet by camellia seed powder: kinetic and thermodynamic studies. Desalin Water Treat 53:3681–3690Google Scholar
  44. 44.
    Foo KY, Hameed BH (2012) Coconut husk derived activated carbon via microwave induced activation: effects of activation agents, preparation parameters and adsorption performance. Chem Eng J 184:57–65Google Scholar
  45. 45.
    Dong Z, Zhao L (2018) Covalently bonded ionic liquid onto cellulose for fast adsorption and efficient separation of Cr(VI): batch, column and mechanism investigation. Carbohyd Polym 189:190–197Google Scholar
  46. 46.
    Kumar PS, Ramalingam S, Kirupha SD, Murugesan A, Vidhyadevi T, Sivanesan S (2011) Adsorption behavior of nickel(II) onto cashew nut shell: equilibrium, thermodynamics, kinetics, mechanism and process design. Chem Eng J 167(1):122–131Google Scholar
  47. 47.
    Yu Z, Dang Q, Liu C, Cha D, Zhang H, Zhu W, Zhang Q, Fan B (2017) Preparation and characterization of poly(maleic acid)-grafted cross-linked chitosan microspheres for Cd(II) adsorption. Carbohyd Polym 172:28–39Google Scholar
  48. 48.
    Gong C, Ou X, Liu S, Jin Y, Huang H, Tang Q, Hon-Wah Lam M, Chow C et al (2017) A molecular imprinting-based multifunctional chemosensor for phthalate esters. Dyes Pigments 137:499–506Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Key Laboratory of Organic Polymer Photoelectric Materials, Shaanxi Engineering Research Center for Pulse Neutron Source and its Application, School of ScienceXijing UniversityXi’anChina
  2. 2.National Demonstration Center for Experimental Light Chemistry Engineering Education, College of Bioresources Chemical and Materials EngineeringShaanxi University of Science and TechnologyXi’anChina

Personalised recommendations