Effect of 0.4 wt% yttrium addition and heat treatment on the high-temperature compression behavior of cast AZ80
- 57 Downloads
The effects of 0.4 wt% yttrium (Y) addition, annealing, and annealing + aging on the hot compression behavior of cast AZ80 were studied at strain rates between 10−4 and 10−2 s−1 and temperatures ranging between 573 and 673 K. The apparent activation energies of the as-cast AZ80 and AZ80 + 0.4Y were 122 and 182 kJ/mol, respectively. Shear bands formed in each alloys. Compared with the as-cast AZ80, more shear bands formed, and a larger volume of cracks initiated and propagated from the grain boundaries and shear bands in as-cast AZ80 + 0.4Y. In general, Y addition increased the peak stress at lower temperatures and higher strain rates. The annealed and annealed + aged alloys exhibited more shear bands and larger compressive peak stresses than their respective as-cast counterparts after compression at 573 K, 10−2 s−1. There were more shear bands in the annealed and annealed + aged AZ80 + 0.4Y compared with AZ80 after compression at 573 K, 10−2 s−1. Fine precipitates appeared in the shear bands of AZ80 + 0.4Y. The average width of the shear bands increased with increasing temperature and decreasing strain rate, and the angles of intersection between the different shear bands were approximately 90°.
This work was supported by the China Scholarship Council (201707000086) and Key Development Project of Sichuan Province (2017GZ0399). Acknowledgements are given to 2015 Cultivation Program for the Excellent Doctoral Dissertation of Southwest Jiaotong University (received by Lingbao Ren), the Program of the 2015 Doctoral Innovation Fund of Southwest Jiaotong University (received by Lingbao Ren), and the support from Litmat Technology Chengdu Co., Ltd.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 2.Ren LB, Quan GF, Jiang ZZ, Yin DD (2016) Atmospheric heat dispersion research of Mg–Al–Zn magnesium alloys. Rare Metal Mater Eng 46(5):1265–1270Google Scholar
- 4.Ren LB, Fan LL, Zhou MY, Guo YY, Zhang YWX, Boehlert CJ, Quan GF (2018) Magnesium application in railway rolling stocks: a new challenge and opportunity for lightweighting. Int J Lightweight Mater Manuf 1:81–88Google Scholar
- 5.Chen ZH, Xia WJ, Yan HG (2005) Wrought magnesium alloys. Chemical Industry Press, Beijing (in Chinese) Google Scholar
- 28.Imandoust A, Barrett CD, Al-Samman T, Tschopp MA, Essadiqi E, Hort N, Kadiri HE (2018) Unraveling recrystallization mechanisms governing texture development from rare-earth element additions to magnesium. Metall Mater Trans A 49(5):1809–1829Google Scholar
- 31.Ren LB, Boehlert CJ, Quan GF (2018) Mechanical asymmetry and anisotropy resulting from the yttrium addition to AZ80, unpublished 2018Google Scholar
- 45.Slużalec A (2010) An analysis of dead zones in the process of direct extrusion through single-hole flat die. Int J Numer Methods Biomed Eng 7(4):281–287Google Scholar