A comparative study on 3D printed silicone-epoxy/acrylate hybrid polymers via pure photopolymerization and dual-curing mechanisms
- 198 Downloads
A type of silicone-epoxy resin has been synthesized and compounded with acrylates to obtain hybrid inks for stereolithography 3D printing. Two approaches of printing have been developed: one approach is pure photopolymerization through the addition of free radical and cationic photoinitiators to the hybrid resin; the other approach untilizes a photo-thermal dual-curing system with free radical photoinitiator for acrylates and thermal curing agent for epoxy resin. The results of hardness, gel content, FTIR and SEM measurements show that both systems get highly crosslinked and interpenetrating polymer network structures, but with different extent of phase separation due to different curing processes. Thermalmechanical and mechanical tests demonstrate that 3D objects from the dual-curing system have higher glass transition temperatures, higher printing efficiency and much enhanced mechanical properties compared with these from the pure photopolymerization system. In addition, both of the systems get 3D objects with high printing accuracy and good thermal stability. The dual-curing mechanism, therefore, has distinct advantages over the pure photopolymerization method.
This study is financially supported by the National Natural Science Foundation of China (Nos. 51603208 and 51573189) and the National Key Research and Development Program of China (No. 2017YFB0404800).
Compliance with ethical standards
Conflict of interest
The authors declare no competing financial interest.
- 4.Choudhari CM, Patil VD (2016) Product development and its comparative analysis by SLA, SLS and FDM rapid prototyping processes. IOP Conf Ser Mater Sci Eng 149(1):012009Google Scholar
- 8.Ming L, Yang H, Zhang W, Zeng X, Xiong D, Xu Z, Wang H, Chen W, Xu X, Wang M, Duan J, Cheng Y-B, Zhang J, Bao Q, Wei Z, Yang S (2014) Selective laser sintering of TiO2 nanoparticle film on plastic conductive substrate for highly efficient flexible dye-sensitized solar cell application. J Mater Chem A 2(13):4566–4573. https://doi.org/10.1039/C3TA14210H Google Scholar
- 12.Yang J, Jiao J, Wang L, Li B (2017) Spark plasma sintering of silicon carbide powders with carbon and boron as additives. In: Singh M, Ohji T, Dong S, Koch D, Shimamura K, Clauss B, Heidenreich B, Akedo J (eds) Advances in high temperature ceramic matrix compo sites and materials for sustainable development; ceramic transactions, vol CCLXIII. Wiley, New York, pp 137–143. https://doi.org/10.1002/9781119407270.ch14 Google Scholar
- 24.Renault T, Ogale AA, Charan R, Bagchi A (1996) Selective reinforcement of photoresins with continuous fibers using 3-D composite photolithography. J Adv Mater 27(4):8–12Google Scholar