Effect of interface defects on the magnetoresistance in Bi4Ti3O12/(La, Sr)Mn1−xO3 heterostructures
- 59 Downloads
Heterostructure between layered ferroelectric oxide Bi4Ti3O12 and perovskite (La, Sr)Mn1−xO3 is highly interesting due to the need to explore new types of functional heterostructures. However, fabricating such heterostructures with high quality is challenging because of the non-isostructural crystalline symmetry of the two constituents. In this work, we constructed two different heterostructures, in which the Bi4Ti3O12 layers with precisely controlled thicknesses were deposited on insulating La0.7Sr0.3Mn0.81O3 and conducting La0.7Sr0.3MnO3 bottom layers, respectively. Results of cross section transmission electron microscopy identified rough interfaces between insulating (La, Sr)Mn1−xO3 and Bi4Ti3O12, while sharp interfaces between metallic (La, Sr)Mn1−xO3 and Bi4Ti3O12. In the former, levels of intermixing and charge leaking are strongly dependent on the thickness of the Bi4Ti3O12 capping layer, which induces a capping-layer-thickness-dependent magnetoresistance. These results demonstrated that the interfacial defect is a critical factor for designing functional heterostructures composed of layered oxide and perovskite oxide.
The authors acknowledge the RBS help from Prof. Donglai Feng and Dr. Rui Peng in Fudan University. This work was supported by the National Science Foundation of China (Grant Nos. 11504358 and 11574287), the National Natural Science Foundation of China (51627901), the National Key R&D Program of China (2016YFA0401004), the National Key R&D Program of China (2017YFA0402900) and the Hefei Science Center CAS (2015HSC-SRG052). The authors thank beamline BL08U1A and BL14 B1 of SSRF for providing the beam time.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 15.Spurgeon SR, Sloppy JD, Kepaptsoglou D, Balachandran PV, Nejati S, Karthik J, Damodaran AR, Johnson CL, Ambaye H, Goyette R, Lauter V, Ramasse QM, Idrobo JC, Lau KKS, Lofland SE Jr, Rondinelli JM, Martin LW, Taheri ML (2014) Thickness-dependent crossover from charge-to strain-mediated magnetoelectric coupling in ferromagnetic/piezoelectric oxide heterostructures. ACS Nano 8:894–903CrossRefGoogle Scholar
- 26.Barriocanal JG, Cezar JC, Bruno FY, Thakur P, Brookes NB, Utfeld C, Calzada AR, Giblin SR, Taylor JW, Duffy JA, Dugdale SB, Nakamura T, Kodama K, Leon C, Okamoto S, Santamaria J (2010) Spin and orbital Ti magnetism at LaMnO3/SrTiO3 interfaces. Nat Commun 1:82Google Scholar
- 28.Hossain MA, Hu Z, Haverkort MW, Burnus T, Chang CF, Klein S, Denlinger JD, Lin H-J, Chen CT, Mathieu R, Kaneko Y, Tokura Y, Satow S, Yoshida Y, Takagi H, Tanaka A, Elfimov IS, Sawatzky GA, Tjeng LH, Damascelli A (2008) Crystal-field level inversion in lightly Mn-doped Sr3Ru2O7. Phys Rev Lett 101:016404CrossRefGoogle Scholar
- 29.Grisolia MN, Varignon J, Sanchez-Santolino G, Arora A, Valencia S, Varela M, Abrudan R, Weschke E, Schierle E, Rault JE, Rueff J-P, Barthélémy A, Santamaria J, Bibes M (2016) Hybridization-controlled charge transfer and induced magnetism at correlated oxide interfaces. Nat Phys 12:484–492CrossRefGoogle Scholar