Dynamic transformation of Ti–6Al–4V during torsion in the two-phase region
- 215 Downloads
Isothermal torsion tests were performed on a Ti–6Al–4V alloy in the two-phase region. The results show that straining leads to an increase in the beta phase fraction, which increases slightly with strain rate. Transformation took place at 880, 940, 960, 980 and 1000 °C. The extent of this type of dynamic transformation (alpha to beta) was increased when the temperature approached the transus temperature. The reverse transformation (beta to alpha) occurred during isothermal holding after torsion and the volume fraction retransformed increased with time. The driving forces promoting dynamic and reverse transformation together with the energy barriers opposing these transformations were derived and compared. The critical stresses required to initiate dynamic transformation are calculated from the flow curves. This analysis confirms that the peak stresses are always higher than the critical stresses at the temperatures employed in the present tests, which makes it possible for the transformation to occur.
The authors are grateful to Dr. Clodualdo Aranas Jr. of CanmetMATERIALS and Prof. Mohammad Jahazi and Dr. Ameth Fall of Ecole de Technologie Superieure (ETS) for discussions. The authors acknowledge with gratitude funding received from the China Scholarship Council and the McGill Engineering Doctoral Award program.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflicts of interest.
- 1.Senuma T (1986) Massive type transformation induced by hot deformation in low carbon steels. In: Proceedings of international conference on martensitic transformations, Nara, pp 515–520Google Scholar
- 3.Ying C, Qi-an C (2003) Dilatometric investigation on isothermal transformation after hot deformation. J Iron Steel Res Int 10:46–48Google Scholar
- 6.Aranas C, Rodrigues SF, Shen YJ, Zhang Z, Jonas JJ (2017) Time-temperature-reverse transformation (TTRT) behaviors of a C‐Mn and a Nb microalloyed steel after dynamic transformation above the Ae3. Steel Res Int 88:1–7Google Scholar
- 23.Fields D, Backofen W (1957) Determination of strain hardening characteristics by torsion testing. Proc ASTM 57:1259–1272Google Scholar
- 27.Rack HJ, Qazi J, Allard L, Valiev R (2008) Thermal stability of severe plastically deformed VT-6 (Ti–6Al–4V). In: Materials Science Forum, Trans Tech Publ, pp 893–898Google Scholar
- 30.Semiatin SL, Zhang F, Larsen R, Chapman L, Furrer D (2016) Precipitation in powder-metallurgy, nickel-base superalloys: review of modeling approach and formulation of engineering methods to determine input data. IMMI 5:3–20Google Scholar