High-performance supercapacitors based on porous activated carbons from cattail wool

Energy materials

Abstract

As electrode materials for supercapacitors, biomass-derived activated carbons attract much attention owing to their natural abundance and low cost. In this work, porous activated carbons are facilely synthesized from cattail wool using Ni(NO3)2·6H2O and KOH as co-etching agents. Compared with the carbons singly etched with KOH, these CWAC-x materials with hierarchical pores have much higher specific surface areas and exhibit much better capacitive performance. As for CWAC-10, the specific surface area and total pore volume are as high as 1581 m2 g−1 and 0.992 cm3 g−1, respectively. For supercapacitor applications, CWAC-10 exhibits a high specific capacitance (314 F g−1 at 1.0 A g−1 in a three-electrode system), excellent cycling stability and high energy density (37.29 Wh kg−1 at a power density of 159.98 W kg−1 in a coin-type symmetric device). The enhanced electrochemical performance can be attributed to the unique structure and the existence of O and N elements.

Notes

Acknowledgements

Financial supports from the National Natural Science Foundation of China (No. U1304203), the Natural Science Foundation of Henan Province (No. 162300410258), the Foundation of Henan Educational Committee (No. 16A150046), the College Science and Technology Innovation Team of Henan Province (No. 16IRTSTHN001), and 111 Project (B12015) are greatly acknowledged.

Supplementary material

10853_2018_2208_MOESM1_ESM.doc (360 kb)
Supplementary material 1 (DOC 360 kb)

References

  1. 1.
    Jiang LL, Sheng LZ, Long CZ, Fan ZJ (2015) Densely packed graphene nanomesh-carbon nanotube hybrid film for ultra-high volumetric performance supercapacitors. Nano Energy 11:471–480CrossRefGoogle Scholar
  2. 2.
    Wang DW, Min YG, Yu YH, Peng B (2014) A general approach for fabrication of nitrogen-doped graphene sheets and its application in supercapacitors. J Colloid Interface Sci 417:270–277CrossRefGoogle Scholar
  3. 3.
    Zhao CJ, Ge ZX, Zhou YA, Huang YF, Wang GF, Qian XZ (2017) Solar-assisting pyrolytically reclaimed carbon fiber and their hybrids of MnO2/RCF for supercapacitor electrodes. Carbon 114:230–241CrossRefGoogle Scholar
  4. 4.
    Gao SY, Zang PY, Dang LQ, Xu H, Shi F, Liu ZH, Lei ZB (2016) Extraordinarily high-rate capability of polyaniline nanorod arrays on graphene nanomesh. J Power Sources 304:111–118CrossRefGoogle Scholar
  5. 5.
    Luo JW, Zhong WB, Zou YB, Xiong CL, Yang WT (2016) Preparation of morphology-controllable polyaniline and polyaniline/graphene hydrogels for high performance binder-free supercapacitor electrodes. J Power Sources 319:73–81CrossRefGoogle Scholar
  6. 6.
    Lu YH, Zhang F, Zhang TF, Leng K, Zhang L, Yang X, Ma YF, Huang Y, Zhang MJ, Chen YS (2013) Synthesis and supercapacitor performance studies of N-doped graphene materials using o-phenylenediamine as the double-N precursor. Carbon 63:508–516CrossRefGoogle Scholar
  7. 7.
    Wang K, Zhao N, Lei SW, Yan R, Tian XD, Wang JZ, Song Y, Xu DF, Guo QG, Liu L (2015) Promising biomass-based activated carbons derived from willow catkins for high performance supercapacitors. Electrochim Acta 166:1–11CrossRefGoogle Scholar
  8. 8.
    Li Y, Wang GL, Wei T, Fan ZJ, Yan P (2016) Nitrogen and sulfur co-doped porous carbon nanosheets derived from willow catkin for supercapacitors. Nano Energy 19:165–175CrossRefGoogle Scholar
  9. 9.
    Feng HB, Hu H, Dong HW, Xiao Y, Cai YJ, Lei BF, Liu YL, Zheng MT (2016) Hierarchical structured carbon derived from bagasse wastes: a simple and efficient synthesis route and its improved electrochemical properties for high-performance supercapacitors. J Power Sources 302:164–173CrossRefGoogle Scholar
  10. 10.
    Yang XQ, Li CF, Chen Y (2017) Hierarchical porous carbon with ultrahigh surface area from corn leaf for high-performance supercapacitors application. J Phys D-Appl Phys 50:055501CrossRefGoogle Scholar
  11. 11.
    Lei D, Song KH, Li XD, Kim HY, Kim BS (2017) Nanostructured polyaniline/kenaf-derived 3D porous carbon materials with high cycle stability for supercapacitor electrodes. J Mater Sci 52:2158–2168.  https://doi.org/10.1007/s10853-016-0504-5 CrossRefGoogle Scholar
  12. 12.
    An HJ, Kim NR, Song MY, Yun YS, Jin HJ (2017) Fallen-leaf-derived microporous pyropolymers for supercapacitors. J Ind Eng Chem 45:223–228CrossRefGoogle Scholar
  13. 13.
    Pan ZZ, Dong LB, Lv W, Zheng DQ, Li ZJ, Luo C, Zheng C, Yang QH, Kang FY (2017) A hollow spherical carbon derived from the spray drying of corncob lignin for high rate-performance supercapacitors. Chem-Asian J 12:503–506CrossRefGoogle Scholar
  14. 14.
    Su XL, Cheng MY, Fu L, Yang JH, Zheng XC, Guan XX (2017) Superior supercapacitive performance of hollow activated carbon nanomesh with hierarchical structure derived from poplar catkins. J Power Sources 362:27–38CrossRefGoogle Scholar
  15. 15.
    Wang K, Song Y, Yan R, Zhao N, Tian XD, Li X, Guo QG, Liu ZJ (2017) High capacitive performance of hollow activated carbon fibers derived from willow catkins. Appl Surf Sci 394:569–577CrossRefGoogle Scholar
  16. 16.
    Cheng P, Gao SY, Zang PY, Yang XF, Bai YL, Xu H, Liu ZH, Lei ZB (2015) Hierarchically porous carbon by activation of shiitake mushroom for capacitive energy storage. Carbon 93:315–324CrossRefGoogle Scholar
  17. 17.
    Ren L, Zhang J, Li Y, Zhang CL (2011) Preparation and evaluation of cattail fiber-based activated carbon for 2,4-dichlorophenol and 2,4,6-trichlorophenol removal. Chem Eng J 168:553–561CrossRefGoogle Scholar
  18. 18.
    Zhang J, Shi QQ, Zhang CL, Xu JT, Zhai B, Zhang B (2008) Adsorption of neutral red onto Mn-impregnated activated carbons prepared from Typha orientalis. Bioresour Technol 99:8974–8980CrossRefGoogle Scholar
  19. 19.
    Liu H, Ning W, Cheng PF, Zhang J, Wang Y, Zhang CL (2013) Evaluation of animal hairs-based activated carbon for sorption of norfloxacin and acetaminophen by comparing with cattail fiber-based activated carbon. J Anal Appl Pyrol 101:156–165CrossRefGoogle Scholar
  20. 20.
    Feng J, Qiao K, Pei LY, Lv JP, Xie SL (2015) Using activated carbon prepared from Typha orientalis Presl to remove phenol from aqueous solutions. Ecol Eng 84:209–217CrossRefGoogle Scholar
  21. 21.
    Tao JY, Gao B, Zhang XM, Fu JJ (2016) Porous N-doped carbon microfibres derived from cattail as high-performance electrodes for supercapacitors. Int J Nanomanuf 12:225–236CrossRefGoogle Scholar
  22. 22.
    Yu M, Han YY, Li J, Wang LJ (2017) CO2-activated porous carbon derived from cattail biomass for removal of malachite green dye and application as supercapacitors. Chem Eng J 317:493–502CrossRefGoogle Scholar
  23. 23.
    Chen C, Yu DF, Zhao GY, Du BS, Tang W, Sun L, Sun Y, Besenbacher F, Yu M (2016) Three-dimensional scaffolding framework of porous carbon nanosheets derived from plant wastes for high-performance supercapacitors. Nano Energy 27:377–389CrossRefGoogle Scholar
  24. 24.
    Ramakrishnan P, Shanmugam S (2016) Nitrogen-doped carbon nanofoam derived from amino acid chelate complex for supercapacitor applications. J Power Sources 316:60–71CrossRefGoogle Scholar
  25. 25.
    Ramakrishnan P, Shanmugam S (2016) Nitrogen-doped porous multi-nano-channel nanocarbons for use in high-performance supercapacitor applications. ACS Sustain Chem Eng 4:2439–2448CrossRefGoogle Scholar
  26. 26.
    Li YJ, Yu N, Yan P, Li YG, Zhou XM, Chen SL, Wang GL, Wei T, Fan ZJ (2015) Fabrication of manganese dioxide nanoplates anchoring on biomass derived cross-linked carbon nanosheets for high-performance asymmetric supercapacitors. J Power Sources 300:309–317CrossRefGoogle Scholar
  27. 27.
    Zhao YQ, Lu M, Tao PY, Zhang YJ, Gong XT, Yang Z, Zhang GL, Li HL (2016) Hierarchically porous and heteroatom doped carbon derived from tobacco rods for supercapacitors. J Power Sources 307:391–400CrossRefGoogle Scholar
  28. 28.
    Luan YT, Huang YQ, Wang L, Li MX, Wang RH, Jiang BJ (2016) Porous carbon@MnO2 and nitrogen-doped porous carbon from carbonized loofah sponge for asymmetric supercapacitor with high energy and power density. J Electroanal Chem 763:90–96CrossRefGoogle Scholar
  29. 29.
    Lebedeva MV, Yeletsky PM, Ayupov AB, Kuznetsov AN, Yakovlev VA, Parmon VN (2015) Micro-mesoporous carbons from rice husk as active materials for supercapacitors. Mater Renew Sustain Energy 4:20CrossRefGoogle Scholar
  30. 30.
    Ma GF, Yang Q, Sun KJ, Peng H, Ran FT, Zhao XL, Lei ZQ (2015) Nitrogen-doped porous carbon derived from biomass waste for high-performance supercapacitor. Bioresour Technol 197:137–142CrossRefGoogle Scholar
  31. 31.
    Zhang WL, Zhao MZ, Liu RY, Wang XF, Lin HB (2015) Hierarchical porous carbon derived from lignin for high performance supercapacitor. Colloid Surfaces A 484:518–527CrossRefGoogle Scholar
  32. 32.
    Qu G, Jia SF, Wang H, Cao F, Li L, Qing C, Sun DM, Wang BX, Tang YW, Wang JB (2016) Asymmetric supercapacitor based on porous N-doped carbon derived from pomelo peel and NiO arrays. ACS Appl Mater Interfaces 8:20822–20830CrossRefGoogle Scholar
  33. 33.
    Lu BH, Hu LY, Yin HY, Mao XH, Xiao W, Wang DH (2016) Preparation and application of capacitive carbon from bamboo shells by one step molten carbonates carbonization. Int J Hydrogen Energy 41:18713–18720CrossRefGoogle Scholar
  34. 34.
    Gong CC, Wang XZ, Ma DH, Chen HF, Zhang SS, Liao ZX (2016) Microporous carbon from a biological waste-stiff silkworm for capacitive energy storage. Electrochim Acta 220:331–339CrossRefGoogle Scholar
  35. 35.
    Liu B, Zhou XH, Chen HB, Liu YJ, Li HM (2016) Promising porous carbons derived from lotus seedpods with outstanding supercapacitance performance. Electrochim Acta 208:55–63CrossRefGoogle Scholar
  36. 36.
    He XJ, Ling PH, Qiu JS, Yu MX, Zhang XY, Yu C, Zheng MD (2013) Efficient preparation of biomass-based mesoporous carbons for supercapacitors with both high energy density and high power density. J Power Sources 240:109–113CrossRefGoogle Scholar
  37. 37.
    Farma R, Deraman M, Awitdrus A, Talib IA, Taer E, Basri NH, Manjunatha JG, Ishak MM, Dollah BNM, Hashmi SA (2013) Preparation of highly porous binderless activated carbon electrodes from fibres of oil palm empty fruit bunches for application in supercapacitors. Bioresour Technol 132:254–261CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  1. 1.College of Chemistry and Molecular EngineeringZhengzhou UniversityZhengzhouChina
  2. 2.Department of Mechanical EngineeringThe Hong Kong Polytechnic UniversityHong KongChina
  3. 3.Key Laboratory of Advanced Energy Materials Chemistry (Ministry of Education)Nankai UniversityTianjinChina
  4. 4.School of Chemical Engineering and EnergyZhengzhou UniversityZhengzhouChina

Personalised recommendations