Influence of curing temperature on the evolution of magnesium oxychloride cement
- 449 Downloads
Hardening behaviour and strength of oxychloride cement strongly depend on the formation of Phase 3 and Phase 5 from MgO and magnesium chloride water solution, and the initial composition can be chosen accordingly within the corresponding phase diagram. A certain number of reactions occur before the final formation of P5 or P3 crystals, and several parameters influence the transformations kinetic, such as MgO reactivity and temperature. Several articles deal with the first aspect, while no indications can be found with regard to the curing temperature’s effect on the formation of noble phases. In this article the evolution of magnesium oxychloride cement pastes is analysed at various curing temperatures between 5 and 40 °C. The study is carried out to simulate typical industrial processing conditions and indicate optimal conditions for the production of high chemical and mechanical resistance oxychloride cement. It is shown that at low temperature, Phase 3 is produced in place of Phase 5, and a certain amount of MgO remains non-reacted. The corresponding cement is characterised by lower mechanical strength and higher water solubility.
KeywordsMagnesium Chloride Silicone Mould Hexahydrate Magnesium Chloride Universal Mechanical Testing Machine Magnesium Oxychloride Cement
The authors thank Deroma Spa for their financial support. The authors thank also Dr. Andrea Camporese and Dr. Marco Passerini (Ricert srl, Monte di Malo , VI, Italy) for their helpful discussions.
- 1.Sorel S (1867) C R Acad Sci France 65:102Google Scholar
- 2.P de Henau, M Dupas (1976) In Proceedings of the second international symposium on the deterioration of building stone, Athens, p 319Google Scholar
- 3.Skoulikidis Th, Papakonstantinou E, Galanos A, Doganis Y (1994) Study for the restoration of the Parthenon, vol 3. Ministry of Culture, Committee for the Preservation of the Acropolis Monuments, AthensGoogle Scholar
- 11.Matkovic B, Young IF (1973) Phys Sci 246:79Google Scholar
- 20.Shetty DK, Rosenfield AR, McGuire P, Bansal GK, Duckworth WH (1980) Ceram Bull 59(12):1193Google Scholar
- 21.JCPDS – Joint Committee on Powder Diffraction Standards – PDF Powder Diffraction FileGoogle Scholar
- 22.ICSD Collection Code – available on Crystallography Open Database (COD). https://doi.org/www.crystallography.net