, Volume 46, Issue 13, pp 4690–4694 | Cite as

Proton conduction in BaxCe0.8Y0.2O3−α + 0.04ZnO at intermediate temperatures and its application in ammonia synthesis at atmospheric pressure

  • Ming Zhang
  • Jia Xu
  • Guilin Ma
Article

Abstract

Dense ceramic samples BaxCe0.8Y0.2O3−α + 0.04ZnO (x = 1, 0.98, 0.96, 0.94) were successfully prepared by a solid-state reaction method, whose sintering temperature was about 573 K lower than a traditional solid state reaction method without sintering aid. XRD patterns indicated that all the samples exhibited a single-phase of orthorhombic perovskite structure. The conduction behavior was investigated by alternating current impedance in wet hydrogen atmosphere at 673–1073 K. It was found that the conductivities were affected by the nonstoichiometric amount of Ba, and increased in the order: σ (x = 0.94) < σ (x = 1) < σ (x = 0.96) < σ (x = 0.98). It was also found that the samples were almost pure ionic conductors and contributed mainly by proton and partially by oxide ion in wet hydrogen atmosphere at 773–1073 K. The ammonia synthesis at atmospheric pressure was successfully conducted using an electrolytic cell based on Ba0.98Ce0.8Y0.2O3−α + 0.04ZnO. The ammonia formation rate reached 2.36 × 10−9 mol s−1 cm−2 under the suitable conditions of 0.8 mA and 773 K.

Keywords

Ceramic Sample Electromotive Force Cathode Chamber Ammonia Synthesis High Proton Conductivity 

Notes

Acknowledgement

This study was supported by the National Natural Science Foundation of China (no. 20771079).

References

  1. 1.
    Iwahara H, Esaka T, Uchida H, Maeda N (1981) Solid State Ionics 3–4:359CrossRefGoogle Scholar
  2. 2.
    Iwahara H (1996) Solid State Ionics 86–88:9CrossRefGoogle Scholar
  3. 3.
    Peng RR, Wu Y, Yang LZ, Mao ZQ (2006) Solid State Ionics 177:389CrossRefGoogle Scholar
  4. 4.
    Kreuer KD (1996) Chem Mater 8:610CrossRefGoogle Scholar
  5. 5.
    Marnellos G, Stoukides M (1998) Science 282:98CrossRefGoogle Scholar
  6. 6.
    Liu JW, Li YD, Wang WB, Wang HTFZ, Ma GL (2010) J Mater Sci 45:5860. doi: https://doi.org/10.1007/s10853-010-4662-6 CrossRefGoogle Scholar
  7. 7.
    Chiodelli G, Malavasi L, Tealdi C, Barison S, Battagliarin M, Doubova L, Fabrizio M, Mortalo C, Gerbasi R (2009) J Alloy Compd 470:477CrossRefGoogle Scholar
  8. 8.
    Guo YX, Liu BX, Yang Q, Chen C, Wang WB, Ma GL (2008) Electrochem Commun 11:153CrossRefGoogle Scholar
  9. 9.
    Tomita A, Hibino T, Suzuki M, Sano M (2004) J Mater Sci 39:2493. doi: https://doi.org/10.1023/B:JMSC.0000020015.80430.d8 CrossRefGoogle Scholar
  10. 10.
    Ma G, Shimura T, Iwahara H (1998) Solid State Ionics 110:103CrossRefGoogle Scholar
  11. 11.
    Babilo P, Haile SM (2005) J Am Ceram Soc 88:2362CrossRefGoogle Scholar
  12. 12.
    Tao SW, Irvine JTS (2006) Adv Mater 18:1581CrossRefGoogle Scholar
  13. 13.
    Wang H, Peng RR, Wu XY, Hu JL, Xia CR (2009) J Am Ceram Soc 92:2623CrossRefGoogle Scholar
  14. 14.
    Guo YM, Ran R, Shao ZP (2010) Int J Hydrogen Energy 35:5611CrossRefGoogle Scholar
  15. 15.
    Xu J, Lu XY, Ding YZ, Chen YH (2009) J Alloy Comp 488:208CrossRefGoogle Scholar
  16. 16.
    Haile SM, Staneff G, Ryu KH (2001) J Mater Sci 36:1149. doi: https://doi.org/10.1023/A:1004877708871 CrossRefGoogle Scholar
  17. 17.
    Shimura T, Esaka K, Matsumoto H, Iwahara H (2002) Solid State Ionics 149:237CrossRefGoogle Scholar
  18. 18.
    Guan J, Dorris SE, Balachandran U, Liu M (1997) Solid State Ionics 100:42CrossRefGoogle Scholar
  19. 19.
    Tomita A, Nakajima J, Hibino T (2008) Angew Chem Int Edit 120:1484CrossRefGoogle Scholar
  20. 20.
    Zhang F, Yang Q, Pan B, Xu R, Hong HT, Ma GL (2007) Mater Lett 61:4144CrossRefGoogle Scholar
  21. 21.
    Zhang F, Sun LL, Zhu JL, Pan B, Xu R, Ma GL (2008) J Mater Sci 43:1587. doi: https://doi.org/10.1007/s10853-007-2328-9 CrossRefGoogle Scholar
  22. 22.
    Ouzounidou M, Skodra A, Kokkofitis C, Stoukides M (2007) Solid State Ionics 178:153CrossRefGoogle Scholar
  23. 23.
    Wang WB, Cao XB, Gao WJ, Zhang F, Wang HT, Ma GL (2010) J Membrane Sci 360:397CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2011

Authors and Affiliations

  1. 1.Key Laboratory of Organic Synthesis of Jiangsu Province, College of Chemistry, Chemical Engineering and Materials ScienceSoochow UniversitySuzhouChina

Personalised recommendations