A comparative study of different solvothermal methods for the synthesis of Sn2+-doped BaTiO3 powders and their dielectric properties
- 240 Downloads
Ternary oxides containing Sn2+ are rare and difficult to prepare by the conventional solid state reactions due to the disproportionation of Sn2+ to Sn4+ and Sn at high temperatures. In this article, Sn2+-doped barium titanate, Ba1−xSnxTiO3 (x = 0.00, 0.02, 0.05, and 0.10) nanopowders were successfully synthesized at a moderate temperature by a microwave-assisted solvothermal reaction (MSR) and a solvothermal reaction with rolling (SRR). The powders obtained using the MSR and SRR consisted of nanoparticles of 20–50 nm and 100–120 nm in diameter, respectively. The dielectric constant of the sample increased by doping with a small amount of Sn2+ (x ≤ 0.05), but decreased by doping in excess amounts of it.
KeywordsBaTiO3 Curie Temperature Barium Titanate Conventional Solid State Reaction Ceramic Body
This research was partially supported by the Ministry of Education, Culture, Sports, Science and Technology, “Special Education and Research Expenses, Post-Silicon Materials and Devices Research Alliance”.
- 2.Mizoguchi H, Wattiaux A, Kykyneshi R, Tate J, Sleight AW, Subramanian MA (2008) Mater Res Bull 43:1943. doi: https://doi.org/10.1016/j.materresbull.2008.03.011 CrossRefGoogle Scholar
- 3.Konishi Y, Ohsawa M, Yonezawa Y, Tanimura Y, Chikyow T, Wakisaka T, Koinuma H, Miyamoto A, Kubo M, Sasata K (2003) Mater Res Soc Symp Proc 748:U3.13.1Google Scholar
- 5.Konisi Y, Osawa M, Yonezawa Y (2003) Fuji Jiho 76(4):241 in JapaneseGoogle Scholar
- 7.Ercit TS, Cerny P (1988) Can Mineral 26:899Google Scholar
- 8.Kumada N, Yonesaki Y, Takei T, Kinomura N, Wada S (2009) Mater Res Bull 44:1298. doi: https://doi.org/10.1016/j.materresbull.2008.12.017 CrossRefGoogle Scholar
- 12.Takenaka T, Nagata H (2005) J Eur Ceram Soc 25:2693. doi: https://doi.org/10.1016/j.jeurceramsoc.2005.03.125 CrossRefGoogle Scholar