, Volume 45, Issue 2, pp 354–362 | Cite as

Thermal stability and strength of Mo/Pt multilayered films

  • A. Bellou
  • L. Scudiero
  • D. F. BahrEmail author
Article

Abstract

The strength of Mo/Pt multilayers of varying thicknesses has been investigated using nanoindentation. Metallic composites with individual layer thicknesses ranging from 100 to 20 nm were fabricated. Of specific interest in this study was the strength of the nanocomposites after annealing in air at relatively high temperatures (475 °C) since potential applications involve high temperature and oxidizing environments. Annealing causes significant losses in strength, with the highest losses corresponding to the structures with the thinner Pt layers. Annealing caused grain coarsening as well as loss of the continuous interface between the individual layers when the Pt thickness was less than 35 nm. Oxidation of the Mo layers occurred during annealing, causing an increase in the thickness of the Mo containing layers. The oxidation of Mo occurs in a uniform manner which results in an increase of the total film thickness while the layered structure is maintained. Deconvolution of the Mo 3d spectrum from X-ray Photoelectron Spectroscopy revealed several oxide species, and no Pt–Mo intermetallics were detected. The changes in microstructure are related to the changes in mechanical properties. Films with thinner layer thicknesses were stronger prior to annealing; however, they showed larger losses in strength after the thermal treatment. Structures with thicker Pt layers should be used when the multilayers are exposed to elevated temperatures.

Keywords

Residual Stress MoO3 Annealed Film Bulge Testing Contact Depth 

Notes

Acknowledgement

This work was supported in part by the US Department of Energy under Grant number DE-FG02-07ER4635.

References

  1. 1.
    Misra A, Hirth JP, Kung H (2002) Philos Mag A 82:2935CrossRefGoogle Scholar
  2. 2.
    Was GS, Foecke T (1996) Thin Solid Films 286:1CrossRefGoogle Scholar
  3. 3.
    Misra A, Kung H (2001) Adv Eng Mater 3:217CrossRefGoogle Scholar
  4. 4.
    Misra A, Hirth JP, Hoagland RG (2005) Acta Mater 53:4817CrossRefGoogle Scholar
  5. 5.
    Lee HJ, Kwon KW, Ryu C, Sinclair R (1999) Acta Mater 47:3965CrossRefGoogle Scholar
  6. 6.
    Misra A, Hoagland RG (2005) J Mater Res 20:2046CrossRefGoogle Scholar
  7. 7.
    Misra A, Verdier M, Lu YC, Kung H, Mitchell TE, Nastasi M, Embury JD (1998) Scripta Mater 39:555CrossRefGoogle Scholar
  8. 8.
    McKeown J, Misra A, Kung H, Hoagland RG, Nastasi M (2002) Scripta Mater 46:593CrossRefGoogle Scholar
  9. 9.
    Huang H, Spaepen F (2000) Acta Mater 48:3261CrossRefGoogle Scholar
  10. 10.
    Eakins LMR, Olson BW, Richards CD, Richards RF, Bahr DF (2003) Thin Solid Films 441:180CrossRefGoogle Scholar
  11. 11.
    Morris DJ, Bahr DF, Anderson MJ (2008) Sens Actuators A 141:262CrossRefGoogle Scholar
  12. 12.
    Bonnotte E, Delobelle P, Bornier L, Trolard B, Tribillon G (1997) J Mater Res 12:2234CrossRefGoogle Scholar
  13. 13.
    Vlassak JJ, Nix WD (1992) J Mater Res 7:3242CrossRefGoogle Scholar
  14. 14.
    Massalski TB (1986) Binary alloy phase diagrams. American Society for Metals, Metals Park, OHGoogle Scholar
  15. 15.
    Underwood JH, Gullikson EM, Nguyen K (1993) Appl Opt 32:6985CrossRefGoogle Scholar
  16. 16.
    Werfel F, Minni E (1983) J Phys C: Solid State Phys 16:6091CrossRefGoogle Scholar
  17. 17.
    Barr TL (1978) J Phys Chem 82:1801CrossRefGoogle Scholar
  18. 18.
    Brox B, Olefjord L (1988) Surf Interface Anal 13:3CrossRefGoogle Scholar
  19. 19.
    Jaksic JM, Vracar Lj, Neophytides SG, Zafeiratos S, Papakonstantinou G, Krstajic NV, Jaksic MM (2005) Surf Sci 598:156CrossRefGoogle Scholar
  20. 20.
    Natesan K, Deevi SC (2000) Intermetallics 8:1147CrossRefGoogle Scholar
  21. 21.
    Geng DY, Zhang ZD, Zhang M, Li D, Song XP, Hu KY (2004) Scripta Mater 50:983CrossRefGoogle Scholar
  22. 22.
    Gulbransen EA, Andrew KF, Brassart FA (1963) J Electrochem Soc 110:952CrossRefGoogle Scholar
  23. 23.
    Misra A, Verdier M, Kung H, Embury JD, Hirth JP (1999) Scripta Mater 41:973CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2009

Authors and Affiliations

  1. 1.School of Mechanical and Materials EngineeringWashington State UniversityPullmanUSA
  2. 2.Department of ChemistryWashington State UniversityPullmanUSA

Personalised recommendations