Tensile properties and fracture behaviour of carbon fibre filament materials

  • Sweety Kumari
  • S. Nithya
  • N. Padmavathi
  • N. Eswara PrasadEmail author
  • J. Subrahmanyam
Article

Abstract

Monotonic tensile properties and fracture behaviour of carbon fibre filament materials, namely single/mono- and multi-filaments (two and four filaments) as well as virgin carbon tows have been evaluated and discussed. Micro composite or single fibre approach is used in this study, which facilitated the evaluation of tensile properties and nature of fracture of carbon filament materials in a relatively short time with a large number of inexpensive trials. Tensile tests have been conducted on these filament materials at ambient temperature and laboratory air atmosphere. Load–elongation and the corresponding stress–strain plots thus obtained have been analysed to understand the tensile behaviour. The peak tensile strength of single carbon filament is found to be 3.8 GPa, and the value of the resilience obtained is 19 MJ/m3. The peak tensile strength was found to increase moderately with further increase in number of filaments. However, the value of resilience was found to increase with increase in the number of fibres, which is attributed to the controlled failure of multi-filaments. On the other hand, the tensile strength of virgin carbon tow without matrix was found to be 1.13 GPa, and the value of the fracture energy was determined to be 9.9 MJ/m3, which is nearly one fourth or even less than the corresponding values of the mono- and multi-filaments. The data obtained in the case of the virgin carbon tows were further analysed to evaluate the Weibull statistical parameters.

Keywords

Carbon Fibre Fracture Energy Single Fibre Weibull Modulus Corrected Stress 

Notes

Acknowledgements

The authors are indebted to Dr. AM Srirama Murty and Dr. G Malakondaiah, former and present Directors, respectively, Defence Metallurgical Research Laboratory (DMRL) for their constant encouragement, and kind permission to publish this article. The authors express their grateful thanks to Dr. M Srinivas and Dr. Vikas Kumar of DMRL for many useful suggestions. The authors are also grateful to Smt. G Rohini Devi, Scientist, Advanced Systems Laboratory, Hyderabad for the provision of the facilities to conduct some of the experiments for this study. Funding from DRDO is gratefully acknowledged.

References

  1. 1.
    Huttener W (1990) In: Figneiredo JL (ed) Carbon fibers filament and composite. Kluwel Academic Publications, BostonGoogle Scholar
  2. 2.
    Fitzer E, Manocha LM (1998) Carbon reinforcements and carbon/carbon composites. Springer, BerlinCrossRefGoogle Scholar
  3. 3.
    Savage G (1993) Carbon–carbon composites. Chapman and Hall, LondonCrossRefGoogle Scholar
  4. 4.
    Naslain R (1992) In: Warren R (ed) Ceramic matrix composites. Chapman & Hall, LondonGoogle Scholar
  5. 5.
    Xu Y, Cheng L, Zhang L, Yin H, Yin X, You C (2001) J European Ceram Soc 21:809CrossRefGoogle Scholar
  6. 6.
    Wilson DM (2001) ASM handbook on composites. ASM International, Metal Park, OhioGoogle Scholar
  7. 7.
    Evans AG (1990) J Am Ceram Soc 73:187CrossRefGoogle Scholar
  8. 8.
    Besmann TM, Sheldon BW, Lowden RA (1991) Science 253:1104CrossRefGoogle Scholar
  9. 9.
    Jemet JF, Lamicq PJ (1993) In: Naslain R (ed) High temperature ceramic matrix composites. Woodhead, BordeauxGoogle Scholar
  10. 10.
    Donald IW, McMillan PW (1976) J Mater Sci 11:949. doi: https://doi.org/10.1007/BF00542312 CrossRefGoogle Scholar
  11. 11.
    Goto K, Hattam H, Oe M, Koizumi T (2003) J Am Ceram Soc 86:2129CrossRefGoogle Scholar
  12. 12.
    Eswara Prasad N, Sweety K, Kamat SV, Vijayakumar M, Malakondaiah G (2004) Eng Fract Mech 71:2589CrossRefGoogle Scholar
  13. 13.
    ASTM Standard C 1557-03 (2004) Standard test method for tensile strength and young’s modulus of fibers, annual book of ASTM Standards, vol 15.01. ASTM International, West Conshohocken, PA, pp 793–802Google Scholar
  14. 14.
    BSI standard DDENV 1007-4 (1994) Determination of tensile properties of filament at ambient temperatureGoogle Scholar
  15. 15.
    Kister G (2002) Composites A 33:435CrossRefGoogle Scholar
  16. 16.
    Bergman B (1984) J Mater Sci Lett 3:689CrossRefGoogle Scholar
  17. 17.
    Lamon J, Lissart N, Rechiniac C (1993) Ceram Eng Sci Proc 14:1115CrossRefGoogle Scholar
  18. 18.
    Padmavathi N, Subrahmanyam J, Ray KK (2008) J Mater Proc Tech 204:434CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2009

Authors and Affiliations

  • Sweety Kumari
    • 1
  • S. Nithya
    • 3
  • N. Padmavathi
    • 2
  • N. Eswara Prasad
    • 4
    Email author
  • J. Subrahmanyam
    • 1
  1. 1.Defence Metallurgical Research LaboratoryHyderabadIndia
  2. 2.Advanced Systems LaboratoryHyderabadIndia
  3. 3.Department of Mechanical and Industrial EngineeringConcordia UniversityMontrealCanada
  4. 4.Regional Centre for Military Airworthiness (Materials), CEMILAC, DRDOHyderabadIndia

Personalised recommendations